水滑石类光催化剂在污水处理中的应用

doi:10.3969/j.issn.1006-396X.2022.03.006

摘要/Abstract

摘要：

双金属复合氢氧化物（LDHs，又叫水滑石）因具有层状结构、稳定的物化性质和电子特性等优点，可以大范围地应用在污水处理中。目前，水滑石作为光催化剂及其复合材料在污水处理上的应用受到越来越多的关注。综述了水滑石光催化剂的制备及其改性，着重介绍了不同类型水滑石对水中不同污染物的去除效果，并简要阐述了水滑石光催化剂的作用机理和研究现状。最后，展望了水滑石光催化剂的发展趋势，以期为后续水滑石在污水处理上的应用提供借鉴。

关键词: 水滑石, 光催化, 水污染治理, 降解污染物, 水滑石改性

Abstract:

Layered double hydroxides (LDHs),also known as hydrotalcite,can be widely employed in water pollution treatment because of their special layered structures,high physicochemical stability,and electronic properties.The application of LDH composites as catalysts for photocatalysis has received increasing attention.Therefore,the preparation and modification of LDH photocatalysts were reviewed,and the removal effect of pollutants from wastewater exerted by different LDHs was emphatically introduced.In addition, the mechanism and research status of LDH photocatalysts were briefly described.Finally,the development trend of LDH photocatalysts was prospected to provide a reference for the subsequent application of LDHs in water pollution treatment.

Key words: LDHs, Photocatalysis, Water pollution treatment, Degradation of pollutants, Modification of LDHs

中图分类号:

TQ110.9

赵东启, 顾贵洲, 李政. 水滑石类光催化剂在污水处理中的应用[J]. 石油化工高等学校学报, 2022, 35(3): 36-42.

Dongqi Zhao, Guizhou Gu, Zheng Li. Application of LDHs with Photocatalytic Properties in Water Pollution Treatment[J]. Journal of Petrochemical Universities, 2022, 35(3): 36-42.

图/表 2

参考文献 45

1	Tuček J，Kemp K C，Kim K S，et al.Iron⁃oxide⁃supported nanocarbon in lithium⁃ion batteries，medical，catalytic，and environmental applications［J］.ACS Nano，2014，8（8）：7571⁃7612.
2	Dong C C，Ji J H，Shen B，et al.Enhancement of H₂O₂decomposition by the co⁃catalytic effect of WS₂ on the fenton reaction for the synchronous reduction of Cr（VI） and remediation of phenol［J］.Environment Science & Technology，2018，52（19）：11297⁃11308.
3	Duan X G，Sun H Q，Shao Z P，et al.Nonradical reactions in environmental remediation processes：Uncertainty and challenges［J］.Applied Catalysis B：Environmental，2018，224：973⁃982.
4	于喜洋，顾贵洲，李政.水滑石材料处理工业废水的研究进展［J］.石油化工高等学校学报，2021，34（6）：16⁃21.
	Yu X Y，Gu G Z，Li Z.Research progress of industrial wastewater treatment by hydrotalcite［J］.Journal of Petrochemical Universities，2021，34（6）：16⁃21.
5	Lin D，Zhou S.Synthesis and characterization of a novel Mg⁃Al hydrotalcite⁃loaded kaolin clay and its adsorption properties for phosphate in aqueous solution［J］.Journal of Alloys and Compounds，2015，637：188⁃196.
6	周俊义.镍铁水滑石的制备及析氧性能研究［D］.青岛：青岛科技大学，2019.
7	der Ven L D，Gemert M，van Batenburg L F，et al.On the action of hydrotalcite⁃likeclay materials as stabilizers in polyvinylchloride ［J］.Applied Clay Science，2000，17（1⁃2）：25⁃34.
8	张宁，李先铭，张红霞，等.不同层板离子及插层类水滑石对PVC热稳定性的影响［J］.中国塑料，2020，34（2）：74⁃78.
	Zhang N，Li X M，Zhong H X，et al.Effect of intercalated hydrotalcite⁃like compounds with different interlayer ions on thermal stability of PVC［J］.China Plastics，2020，34（2）：74⁃78.
9	Lu H，Zhu Z，Zhang H，et al.Fenton like catalysis and oxidation/ adsorption performances of acetaminophen and arsenic pollutants in water on a multi⁃metal Cu⁃Zn⁃Fe⁃LDH［J］.Acs Applied Materials & Interfaces，2016，8（38）：25343⁃25352.
10	肖康，王新星，吴小飞，等.水滑石层间阴离子为还原剂原位负载贵金属纳米颗粒［J］.化学通报，2018，81（4）：47⁃53.
	Xiao K，Wang X X，Wu X F，et al.Reductive loading of noble metal nanoparticles on layered doube hydroxide with interlayer anion as reductant［J］.Chemistry，2018，81（4）：332⁃338.
11	张鋆益，邹勇昌，陈俊，等.层间阴离子对镁⁃铝水滑石吸附HCl与PVC热稳定性的影响［J］.塑料工业，2019，42（12）：116⁃121.
	Zhang J Y，Zhou Y C，Chen J，et al.Effect of interlayer anions on the absorption by Mg⁃Al hydrotalcite and the thermal stability of PVC［J］.China Plastics Industry，2019，42（12）：116⁃121.
12	Zhang Y，Du D，Li X，et al.Electrostatic self⁃assembly of sandwich⁃like CoAl⁃LDH/ polypyrrole/ graphene nanocomposites with enhanced capacitive performance［J］.Acs Applied Materail Interfaces，2017，9（37）：31699⁃13709.
13	赵策，曾虹燕，王亚举，等.Mg⁃Al水滑石“记忆效应”及其对Cr（VI）阴离子吸附性能研究［J］.无机材料学报，2011，26（8）：874⁃880.
	Zhao C，Zhen H Y，Wang Y J，et al.“Memory effect” of Mg⁃Al hydrotalcites and its chromium（VI） absorption property［J］.Journal of Inorganic Metarials［J］.2011，26（8）：874⁃880.
14	高昆，汪朝晖，汪效祖.水热法制Zn⁃Mg⁃Al花状水滑石［J］.精细化工，2013，30（2）：126⁃143.
	Gao K，Wang C H，Wang X Z.Hydrothermal synthsis and characterization of Zn⁃Mg⁃Al hydrotalcite［J］.Fine Chemicals，2013，30（2）：126⁃143.
15	刘媛，蒋晓帆，姚培.镁铝水滑石结构记忆性及其应用研究［J］.广东化工，2011，38（1）：80⁃82.
	Liu Y，Jiang X F，Yao P.Memory effect and its application of Mg⁃Al hydrotalcite［J］.Guangdong Chemical Industry，2011，38（1）：80⁃82.
16	胡盛，付英英，汪桐，等.反应时间对镁铝水滑石结构的影响［J］.非金属矿，2019，42（1）：46⁃49.
	Hu S，Fu Y Y，Wang T，et al.Effect of reaction time on the structure of Mg⁃Al Hydrotalcite［J］.Non⁃metallic Mines，2019，42（1）：46⁃49.
17	滑亚婷，杜春贵，姚潇翎，等.水滑石阻燃剂的离子改性研究概况与发展前景［J］.化学通报，2018，82（4）：316⁃322.
	Hua Y T，Du C G，Yao X L，et al.Progress in ion⁃ modified hydrotalcite flame retardants［J］.Chemistry，2018，82（4）：316⁃322.
18	Chen Y，Li J，Zhai B Y，et al.Enhanced photocatalytic degradation of RhB by two⁃dimensional composite photocatalyst［J］.Colloids & Surfaces A Physicochemical & Engineering Aspects，2019，568：429⁃435.
19	Marianna I，Antonio D M，Antonio V，et al.Synthesis，characterization，and sorption capacity of layered double hydroxides and their complexes with polymerin［J］.Journal of Agricultural and Food Chemistry，2010，58（9）：5523⁃5530.
20	Rehab M，Samah A M，Fatma M，et，al.Comparative study of single and multiple pollutants system using Ti–Fe chitosan LDH adsorbent with high performance in wastewater treatment［J］.Journal of Chemical and Engineering Data，2017，62（11）：3703⁃3722.
21	张骄佼，田森林，周键.镁铝水滑石的合成与应用研究进展［J］.材料导报，2013，27（4）：144⁃148.
	Zhan J J，Tian S L，Zhou J.Study on synthesis and application of Mg⁃Al Hydrotalcite［J］.Materials Reports A：Review，2013，27（4）：144⁃148.
22	Zhou F，Zhao X M，Andrew V B，et al.Coprecipitation synthesis of NixMn_1- x（OH）₂ mixed hydroxides［J］.Chemistry of Materials，2010，22（3）：1015⁃1021.
23	Xu Z P，Qing G.Hydrothermal synthesis of layered double hydroxides （LDHs） from mixed MgO and Al₂O₃：LDH formation mechanism［J］.Chemistry of Materials，2005，17（5）：1055⁃1062.
24	Liang D J，Yue W B，Sun G B，et al.Direct synthesis of unilamellar MgAl⁃LDH nanosheets and stacking in aqueous solution［J］.Langmuir，2015，31（45）：12464⁃12471.
25	张永辉，陈雪冰，张静.可见光催化剂氧化铋的改性研究进展［J］.辽宁石油化工大学学报，2021，41（6）：1⁃8.
	Zhang Y H，Chen X B，Zhang J.Research progress on modification of bismuth oxide as visible light photocatalyst［J］.Journal of Liaoning Petrochemical University，2021，41（6）：1⁃8.
26	Zhang Y H，Tang Z R，Fu X Z，et al.TiO₂⁃graphene nanocomposites for gas⁃phase photocatalytic pegradation of volatile aromatic pollutant：Is TiO₂⁃graphene truly different from other TiO₂⁃carbon composite materials？［J］.ACS Nano，2010，4（12）：7303⁃7314.
27	Tian J Y，David B C，Claudio Q，et al.Lead perovskite and competitive Formation of 6H and 3C perovskite structure with mixed A cations［J］.ACS Applied Energy Materials，2019，2（8）：5427–5437.
28	倪哲明，薛继龙.含Cu水滑石的结构与光催化性能［J］.高等学校化学学报，2013，34（3）：503⁃508.
	Ni Z M，Xue J L.Synthesis of CuMgAl layered double hydroxides for efficient photocatalysis of rhodamine B［J］.Chemical Journal of Chinese Universities，2013，34（3）：503⁃508.
29	Xiong X Y，Zhao Y F，Shi R，et al.Selective photocatalytic CO₂ reduction over Zn⁃based layered double hydroxides containing tri or tetravalent metals［J］.Science Bulletin，2020，65（12）：987⁃994.
30	符艺.稀土金属离子掺杂水滑石的制备及其光催化性能研究［D］.北京：北京化工大学，2016.
31	Wei M，Shi Z Y，David G E，et al.Study on the intercalation and interlayer oxidation transformation of L⁃cysteine in a confined region of layered double hydroxides［J］.Journal of Materials Chemistry，2006，16（21）：2102⁃2109．
32	González M A，Pavlovic I，Delgalo R，et al.Removal of Cu^{2 +}Pb^{2 +} and Cd^{2 +}by layered double hydroxidehumate hybrid.Sorbate and sorbent comparative studies［J］.Chemical Engineering Journal，2014，254：605⁃611．
33	Zhao Y F，Chen P Y，Zhang B S，et al.Highly dispersed TiO₆ units in a layered double hydroxide for water splitting［J］.Chemistry⁃A European Journal，2012，18（38）：11949⁃11958.
34	Yao L H，Wei D，Ni Y M，et al.Surface localization of CdZnS quantum dots onto 2D g⁃C₃N₄ultrathin microribbons：Highly efficient visible light⁃induced H₂⁃generation［J］.Nano Energy，2016，26：248⁃256.
35	Xu Y，Liu T J，Zhang Y，et al.Advances in technologies for pharmaceuticals and personal care products removal［J］.Journal of Materials Chemistry A，2017，5（24）：12001⁃12014.
36	杜仙格.多元类水滑石材料的制备及催化PMS去除水中难降解有机污染物的研究［D］.太原：太原理工大学，2020.
37	Wang Z，Jia W，Jiang M L，et al.Microwave⁃assisted synthesis of layer⁃by⁃layer ultra⁃large and thin NiAl⁃LDH/RGO nanocomposites and their excellent performance as electrodes［J］.Science China Materials，2015，58（12）：944⁃952.
38	邢嘉钰，李丽，张国权，等.锰钴水滑石/石墨烯电极的制备及催化性能［J］.中国环境科学，2020，40（11）：167⁃175.
	Xing J Y，Li L，Zhang G Q，et al.The preparation and catalytic performance of MnCo layered double hydroxides/reduced graphene oxide electrode［J］.China Environmental Science，2020，40（11）：4804⁃4812.
39	方若超，吴代赦，杨昱，等.H₂O₂协同强化CuCoAl⁃LDHs/GO复合材料光催化效能［J］.环境工程学报，2021，15（9）：2913⁃2921.
	Fang R C，Wu D M，Yang L，et al.Photocatalytic performance of CuCoAl⁃LDHs/GO composites synergistically enhanced by H₂O₂［J］.Chinese Journal of Environmental Engineering，2021，15（9）：2913⁃2921.
40	Sun J C，Zhang Y B，Cheng J，et al.Synthesis of Ag/AgCl/Zn⁃Cr LDHs composite with enhanced visible⁃light photocatalytic performance［J］.Journal of Molecular Catalysis A Chemical，2014，382（4）：146⁃153.
41	石双欣，卫静.光催化技术处理染料废水研究进展［J］.绿色科技，2021，23（2）：63⁃65.
	Shi S X，Wei J.Research progress in photocatalytic treatment of dye wastewater［J］.Green Technology，2021，23（2）：63⁃65.
42	Yuan X，Li W，Yuan X，et al.Enhancement photocatalytic degradation of rhodamine B on nanoPt intercalated Zn⁃Ti layered double hydroxides［J］.Applied Surface Science，2014，293：345⁃351.
43	Da G P，Liu S Q，Liang Y，et al.Fabrication of a nano⁃sized Ag₂CO₃/reduced graphene oxide photocatalyst with enhanced visible⁃light photocatalytic activity and stability［J］.RSC Advances，2014，4（65）：34226⁃34231.
44	Ao Y H，Wang P F，Wang C，et al.Enhanced photocatalytic properties of the 3D flower⁃like Mg⁃Al layered double hydroxides decorated with Ag₂CO₃under visible light illumination［J］.Materials Research Bulletin，2016，80：23⁃29.
45	Wang Y Y，Jing Y Q，Li W X，et al.Silicate silver/flower⁃like magnalium hydroxide composites for enhanced visible light photodegradation activities［J］.RSC Advances，2018，8（41）：23442⁃23450.

[1]	王嘉曼, 熊靖, 师金鸽, 韦岳长, 霍开玲. TiO₂催化剂催化CO₂还原的研究进展[J]. 石油化工高等学校学报, 2024, 37(4): 1-11.
[2]	杨文科, 卢连雪, 李鹏, 张健, 胡绍争. 光催化材料石墨相氮化碳的合成、改性及应用[J]. 石油化工高等学校学报, 2024, 37(1): 43-51.
[3]	宁尧, 刘满, 刘素燕. 多孔碳BVO/Zn@ZPC的制备及其光降解性能[J]. 石油化工高等学校学报, 2023, 36(6): 36-47.
[4]	陈基鹏, 杨阳佳子, 李鹏, 张健, 胡绍争. 石墨相氮化碳的制备、改性及应用[J]. 石油化工高等学校学报, 2023, 36(5): 45-51.
[5]	李敏, 李政, 顾贵洲, 于喜洋, 王辉. Zn⁃Mg⁃Al LDO的制备及其除氟性能研究[J]. 石油化工高等学校学报, 2023, 36(5): 73-80.
[6]	张若男, 何仕婕, 王晓蓉, 王芳芳, 陈常东. BaTiO₃⁃TiO₂复合体的软化学制备及其性能研究[J]. 石油化工高等学校学报, 2022, 35(4): 46-51.
[7]	陈佳慧, 黎泓麟, 杨紫坤, 罗鸿仙, 张金生, 李丽华. GO改性的铈基纳米复合光催化剂性能对比研究[J]. 石油化工高等学校学报, 2022, 35(1): 63-67.
[8]	于喜洋, 顾贵洲, 李政. 水滑石材料处理工业废水的研究进展[J]. 石油化工高等学校学报, 2021, 34(6): 16-21.
[9]	刘纪法, 陈雪冰, 王芳芳, 张静, 陈常东. 六方相/单斜相WO₃“异相结”的可控合成及光催化性能[J]. 石油化工高等学校学报, 2021, 34(6): 22-26.
[10]	齐永娟, 宫晓杰, 张丹, 吴限, 李丽华. 单模聚焦微波法制备MIL⁃53(Fe)及其光催化性能研究[J]. 石油化工高等学校学报, 2021, 34(5): 24-29.
[11]	周月娥, 陈雪冰, 张静. 内建电场调控光生电荷分离效率的研究进展[J]. 石油化工高等学校学报, 2021, 34(3): 1-6.
[12]	崔美玉，李飞. 可见光催化的烯烃胺化反应的研究进展[J]. 石油化工高等学校学报, 2021, 34(3): 31-37.
[13]	李鹏, 吕振波, 于芳. 可见光催化环丁醇的C-C断裂胺化反应的研究[J]. 石油化工高等学校学报, 2020, 33(4): 1-5.
[14]	商宇桐，杨丽娜，管景国，李剑. 光催化氧化脱硫催化剂研究进展[J]. 石油化工高等学校学报, 2020, 33(2): 12-17.
[15]	高文龙，陈雪冰，张静. 二维纳米片金红石TiO₂的可控合成及光催化性能[J]. 石油化工高等学校学报, 2019, 32(6): 22-26.