Ce-CoFe-P@CC纳米复合催化体系的OER性能

doi:10.12422/j.issn.1006-396X.2024.03.007

摘要/Abstract

摘要：

对粉末电催化剂进行电催化性能测试时通常需要加入黏合剂，该测试容易导致催化剂电阻增加，催化剂负载量减少，并且在长时间测试下催化剂容易被剥离。采用一步水热法使Ce掺杂CoFe层状双金属氢氧化物在碳布上均匀生长，并进一步磷化处理直接获得了无需黏合剂的Ce-CoFe-P@CC自支撑电极材料；通过XRD、SEM、TEM、N₂吸附-脱附等温曲线和XPS对电极材料进行表征，并对其进行了电催化OER性能测试。结果表明，合成得到的电极材料具有规则的纳米片形貌，纳米片长度和厚度分别为2.50 μm和0.05 μm；Ce和P的掺杂优化了CoFe-LDH电子结构，促进了电荷转移，增加了催化活性位点，提高了电极的耐久性；Ce-CoFe-P@CC在10 mA/cm²的电流密度下只需187 mV的过电势，表现出优异的OER催化性能。

关键词: 析氧反应, 电催化, CoFe层状双金属氢氧化物, 稀土金属, 磷化物

Abstract:

Powder electrocatalysts usually need adhesives for electrocatalytic performance testing,resulting in an increase in resistance,a decrease in catalyst load,and easy stripping of the catalyst under long-time testing.Ce-doped CoFe layered bimetallic hydroxides were uniformly grown on carbon cloth by one-step hydrothermal method,and the adhesive-free Ce-CoFe-P@CC self-supporting electrocatalyst was obtained by further phosphating treatment.It was characterized by XRD,SEM,TEM,N₂ adsorption-desorption isotherm and XPS,and its electrocatalytic OER performance was tested.The results show that the synthesized electrode material has regular thin nanosheet morphology,and the length and thickness of the nanoflake are 2.50 μm and 0.05 μm, respectively.The doping of Ce and P optimizes the electronic structure of CoFe-LDH,promotes the charge transfer,increases the catalytically active site,and improves the durability of the electrode.The Ce-CoFe-P@CC only needs an overpotential of 187 mV at a current density of 10 mA/cm²,showing excellent OER catalytic performance.

Key words: Oxygen evolution reaction, Electrocatalysis, CoFe layered bimetallic hydroxide, Rare earth metal, Phosphide

中图分类号:

TQ151

毕艳琴, 陈亮亮, 段春阳, 赵增华. Ce-CoFe-P@CC纳米复合催化体系的OER性能[J]. 石油化工高等学校学报, 2024, 37(3): 49-57.

Yanqin BI, Liangliang CHEN, Chunyang DUAN, Zenghua ZHAO. OER Performance of Ce-CoFe-P@CC Nanocomposite Catalytic System[J]. Journal of Petrochemical Universities, 2024, 37(3): 49-57.

图/表 10

图1 Ce-CoFe-P@CC纳米片的合成示意图

Fig.1 Schematic diagram of synthesis of Ce-CoFe-P@CC nanosheets

图2 Ce-CoFe和Ce-CoFe-P的XRD谱图

Fig.2 XRD diagram of Ce-CoFe and Ce-CoFe-P

图3 Ce-CoFe@CC和Ce-CoFe-P@CC的SEM图像

Fig.3 SEM images of Ce-CoFe @CC and Ce-CoFe-P@CC

图4 Ce-CoFe-P的TEM、HRTEM及元素分布图

Fig.4 Distribution diagram of TEM, HRTEM and elements of Ce-CoFe-P

图5 Ce-CoFe-P的N2吸附-脱附等温曲线及孔径分布图

Fig.5 N2 adsorption-desorption isotherm curve and pore size distribution of Ce-CoFe-P

图6 Ce-CoFe和CoFe的XPS谱图

Fig.6 XPS analysis of Ce-CoFe and CoFe

图7 Ce-CoFe-P和Ce-CoFe的XPS谱图

Fig.7 XPS contrast spectra of Ce-CoFe-P and Ce-CoFe

图8 不同催化剂的LSV极化曲线、相应的过电势及Tafel斜率（a） LSV极化曲线（b）过电势（c） Tafel斜率

Fig.8 LSV polarization curves of different catalysts and corresponding overpotential and Tafel slope

图9 不同催化剂的CV曲线、Cdl和EIS图

Fig.9 CV curves, Cdl and EIS diagrams of different catalysts

图10 Ce-CoFe-P@CC的稳定性测试结果

Fig.10 Stability test of Ce-CoFe-P@CC

参考文献 33

1	AHMED A，AL-AMIN A Q，AMBROSE A F，et al.Hydrogen fuel and transport system：A sustainable and environmental future［J］.International Journal of Hydrogen Energy，2016，41（3）：1369-1380.
2	CHAUBEY R，SAHU S，JAMES O O，et al.A review on development of industrial processes and emerging techniques for production of hydrogen from renewable and sustainable sources［J］.Renewable and Sustainable Energy Reviews，2013，23：443-462.
3	杜坤，郭佳欣，马紫昂，等.中性环境下电催化析氧反应研究进展［J］.石油化工高等学校学报，2023，36（5）：1-14.
	DU K，GUO J X，MA Z A，et al.Progress in electrocatalytic oxygen precipitation reaction under neutral environment［J］.Journal of Petrochemical Universities，2023，36（5）：1-14.
4	STASZAK-JIRKOVSKÝ J，MALLIAKAS C D，LOPES P P，et al.Design of active and stable Co–Mo–Sx chalcogels as pH-universal catalysts for the hydrogen evolution reaction［J］.Nature Materials，2016，15：197-203.
5	关扬，闫飞，黄亮亮，等.Pt负载Li₂Co₂O₄的合成及其析氧性能研究［J］.辽宁石油化工大学学报，2018，38（5）：30-34.
	GUAN Y，YAN F，HUANG L L，et al.Synthesis of Pt loaded Li₂Co₂O₄ and its oxygen evolution performance［J］.Journal of Liaoning Shihua University，2018，38（5）：30-34.
6	XIE X H，DU L，YAN L T，et al.Oxygen evolution reaction in alkaline environment：Material challenges and solutions［J］.Advanced Functional Materials，2022，32（21）：2110036.
7	王硕，张浩楠，杨英.电解水催化剂界面结构调控研究进展［J］.石油炼制与化工，2024，55（2）：1-9.
	WANG S，ZHANG H N，YANG Y.Research progress on interface structure regulation of electrolytic water catalysts［J］.Petroleum Processing and Petrochemicals，2024，55（2）：1-9.
8	LONG X，WANG Z L，XIAO S，et al.Transition metal based layered double hydroxides tailored for energy conversion and storage［J］.Materials Today，2016，19（4）：213-226.
9	FU X M，CHEN Y Y，WANG T，et al.Core-shell nanoarray structured La doped Cu（OH）₂@NiCo layered double hydroxide for oxygen evolution reaction［J］.International Journal of Hydrogen Energy，2022，47（65）：27996-28006.
10	HUI J，YAN C P，SHI Y，et al.Rare-earth metal multicomponent perovskite as a electrocatalyst for water splitting［J］.Materials Letters，2023，332：133532.
11	LI F J，JIANG M H，LAI C G，et al.Yttrium- and cerium-codoped ultrathin metal–organic framework nanosheet arrays for high-efficiency electrocatalytic overall water splitting［J］.Nano Letters，2022，22（17）：7238-7245.
12	XU M D，WEI J，CUI X R，et al.High-efficiency electro-fenton process based on in-situ grown CoFeCe-LDH@CFs free-standing cathodes：Correlation of cerium and oxygen vacancies with H₂O₂［J］.Chemical Engineering Journal，2023，455（Part 2）：140922.
13	FAN C，WU X D，LI M，et al.Surface chemical reconstruction of hierarchical hollow inverse-spinel manganese cobalt oxide boosting oxygen evolution reaction［J］.Chemical Engineering Journal，2022，431（Part 1）：133829.
14	YIN L L，ZHANG S，SUN M Z，et al.Heteroatom‐driven coordination fields altering single cerium atom sites for efficient oxygen reduction reaction［J］.Advanced Materials，2023，35（28）：2302485.
15	LIU Z Y，WAN J X，LI M，et al.Synthesis of Co/CeO₂ hetero-particles with abundant oxygen-vacancies supported by carbon aerogels for ORR and OER［J］.Nanoscale，2022，14（5）：1997-2003.
16	RONG M K，ZHONG H，WANG S，et al.La/Ce doped CoFe layered double hydroxides （LDH） highly enhanced oxygen evolution performance of water splitting［J］.Colloids and Surfaces A：Physicochemical and Engineering Aspects，2021，625：126896.
17	RAJAGOPAL K，KATHIRESAN M，RAJARAM A，et al.Development of robust noble-metal free lanthanum，ndymium doped L i 1.05 N i 0.5 M n 1.5 O 4 as a bifunctional electrocatalyst for electrochemical water splitting［J］.RSC Advances，2023，13（34）：23829-23840.
18	WANG X X，SUN C，HE F，et al.Enhanced hydrogen evolution reaction performance of NiCo₂P by filling oxygen vacancies by phosphorus in thin-coating CeO₂［J］.ACS Applied Materials & Interfaces，2019，11（35）：32460-32468.
19	WU L B，YU L，ZHANG F H，et al.Heterogeneous bimetallic phosphide Ni₂P-Fe₂P as an efficient bifunctional catalyst for water/seawater splitting［J］.Advanced Functional Materials，2021，31（1）：2006484.
20	WANG Z C，LIU H L，GE R X，et al.Phosphorus-doped Co₃O₄ nanowire array：A highly efficient bifunctional electrocatalyst for overall water splitting［J］.ACS Catalysis，2018，8（3）：2236-2241.
21	LI M G，WANG J F，GUO X，et al.Structural engineering of Fe-doped Ni₂P nanosheets arrays for enhancing bifunctional electrocatalysis towards overall water splitting［J］.Applied Surface Science，2021，536：147909.
22	YU L P，ZHANG J，DANG Y L，et al.In situ growth of Ni₂P–Cu₃P bimetallic phosphide with bicontinuous structure on self-supported NiCuC substrate as an efficient hydrogen evolution reaction electrocatalyst［J］.ACS Catalysis，2019，9（8）：6919-6928.
23	TESCH M F，NEUGEBAUER S，NARANGODA P V，et al.The rotating disc electrode：Measurement protocols and reproducibility in the evaluation of catalysts for the oxygen evolution reaction［J］.Energy Advances，2023，2（11）：1823-1830.
24	DENG B，LIANG J，YUE L C，et al.CoFe-LDH nanowire arrays on graphite felt：A high-performance oxygen evolution electrocatalyst in alkaline media［J］.Chinese Chemical Letters，2022，33（2）：890-892.
25	SUN S F，ZHENG M，CHENG P F，et al.Porous bimetallic cobalt-iron phosphide nanofoam for efficient and stable oxygen evolution catalysis［J］.Journal of Colloid and Interface Science，2022，626：515-523.
26	LIU C C，HAN Y，YAO L B，et al.Engineering bimetallic NiFe-based hydroxides/selenides heterostructure nanosheet arrays for highly-efficient oxygen evolution reaction［J］.Small，2021，17（7）：e2007334.
27	DENG Y，XIAO Z Y，WANG Z C，et al.The rational adjusting of proton-feeding by Pt-doped FeP/C hollow nanorod for promoting nitrogen reduction kinetics［J］.Applied Catalysis B：Environmental，2021，291：120047.
28	DU L，GAO X Y，WANG G Y，et al.CeO₂ nanoparticles decorated on porous Ni–Fe bimetallic phosphide nanosheets for high-efficient overall water splitting［J］.Materials Research Letters，2023，11（2）：159-167.
29	WANG L，LIU Y，LIU X H，et al.3D nanostructured Ce-doped CoFe-LDH/NF self-supported catalyst for high-performance OER［J］.Dalton Transactions，2023，52（34）：12038-12048.
30	WANG X D，WANG C，LAI F Y，et al.Self-supported CoFe-P nanosheets as a bifunctional catalyst for overall water splitting［J］.ACS Applied Nano Materials，2021，4（11）：12083-12090.
31	HUANG Y R，LI M G，YANG W W，et al.Ce-doped ordered mesoporous cobalt ferrite phosphides as robust catalysts for water oxidation［J］.Chemistry A European Journal，2020，26（58）：13305-13310.
32	NIE F，LI Z，DAI X P，et al.Interfacial electronic modulation on heterostructured NiSe@CoFe LDH nanoarrays for enhancing oxygen evolution reaction and water splitting by facilitating the deprotonation of OH to O［J］.Chemical Engineering Journal，2022，431（Part 2）：134080.
33	YANG L T，CHEN L，YANG D W，et al.NiMn layered double hydroxide nanosheets/NiCo₂O₄ nanowires with surface rich high valence state metal oxide as an efficient electrocatalyst for oxygen evolution reaction［J］.Journal of Power Sources，2018，392：23-32.

[1]	王嘉曼, 熊靖, 师金鸽, 韦岳长, 霍开玲. TiO₂催化剂催化CO₂还原的研究进展[J]. 石油化工高等学校学报, 2024, 37(4): 1-11.
[2]	李乐乐, 申丽莎, 涂志明, 卢卓信, 谭弘毅, 杨轶, 闫常峰. Cu掺杂WN松枝状自支撑纳米阵列的制备及其碱性析氢性能的研究[J]. 石油化工高等学校学报, 2024, 37(4): 57-65.
[3]	杜坤, 郭佳欣, 马紫昂, 毛晶, 凌涛, 赵巍. 中性环境下电催化析氧反应研究进展[J]. 石油化工高等学校学报, 2023, 36(5): 1-14.
[4]	武玉泰, 王佳琦, 李丹, 胡旭, 王永胜, 郝广平. 双金属⁃氮掺杂炭催化剂的制备及其电催化CO₂性能[J]. 石油化工高等学校学报, 2023, 36(3): 1-10.
[5]	刘梦珊, 孟超, 胡涵, 吴明铂. NiMoN催化电极材料的制备及其电解海水制氢性能[J]. 石油化工高等学校学报, 2023, 36(2): 1-9.
[6]	张瑀净, 张宝山, 孙洁. 电解水制氢技术及其催化剂研究进展[J]. 石油化工高等学校学报, 2022, 35(6): 19-27.
[7]	范琳, 杨磊, 车晓甄, 李夺, 潘立卫, 钟和香. CO₂电化学还原制CO金属催化剂的研究进展[J]. 石油化工高等学校学报, 2022, 35(6): 48-58.
[8]	许雪容, 彭祥. 层状双金属氢氧化物电催化剂的合成与应用研究进展[J]. 石油化工高等学校学报, 2022, 35(5): 1-11.
[9]	杨扬, 孟超, 胡涵, 吴明铂. NiCo₂O₄/Ru复合催化剂的制备及锌空电池的应用[J]. 石油化工高等学校学报, 2022, 35(5): 64-70.
[10]	宋楗, 韩乔, 杨占旭. NiMoP/C复合材料的制备及其电催化析氢性能[J]. 石油化工高等学校学报, 2022, 35(1): 1-9.
[11]	荣冰莹，刘贺，惠宇，宋丽娟，钟伟. 多吡啶铁配合物制备及电催化质子还原性能[J]. 石油化工高等学校学报, 2020, 33(2): 1-6.