C u O - Z n O - C e O2 / A l 2O3 催化剂的催化及表征

牟川川1,  刘道胜1,  贾秀峰2,  桂建舟1, 3,  刘 丹1, 3   

  1.         
    ( 1. 辽宁石油化工大学化学化工与环境学部, 辽宁抚顺1 1 3 0 0 1; 2. 鄂尔多斯市东胜区煤矿安全监督管理站,
    内蒙古鄂尔多斯0 1 7 0 0 0; 3. 天津工业大学环境与化学工程学院, 天津3 8 0 3 8 7)
  • 收稿日期:2014-12-31 修回日期:2015-04-09 出版日期:2015-10-25 发布日期:2015-10-21
  • 通讯作者: 桂建舟( 1 9 7 3 - ) , 男, 博士, 教授, 从事石油化工催化剂及工艺的研究; E - m a i l : j z g u i @h o t m a i l . c o m。
  • 作者简介:牟川川( 1 9 9 0 - ) , 女, 硕士研究生, 从事催化化学研究; E - m a i l : m u c h u a n_g o o d@1 2 6. c o m。
  • 基金资助:
    国家自然科学基金项目 ( 2 1 5 7 6 2 1 1) ; 辽宁省教育厅一般项目( L 2 0 1 2 1 2 8) ; 天津市应用基础与前沿技术研究
    ( 1 3 J CY B J C 4 1 6 0 0) 。

Catalytic and Characterization ofC u O - Z n O - C e O2 / A l 2O3 Catalyst

  1. （1.College of Chemistry, Chemical Engineering and Environment, Liaoning Shihua University, Fushun Liaoning 113001, China; [JP] 2. Dongsheng District Coal Mine Safety Supervision and Management Station, Eerduosi Inner Mongolia 017000, China； 3. School of Environmental and Chemical Engineering, Tianjin Polytechnic University, Tianjin 300387, China)
  • Received:2014-12-31 Revised:2015-04-09 Published:2015-10-25 Online:2015-10-21

PDF

摘要： 采用共沉淀法制备了用于催化湿式氧化工艺的 C u O - Z n O - C e O2 / A l 2O3 催化剂, 采用 X射线衍射 ( XR D)对催化剂进行了表征, 并以实验室配置的苯酚溶液为目标污染物, 考察了C u O - Z n O - C e O2 / A l 2O3催化剂的活性和稳定性。结果表明, C e的加入有提高催化剂体系分散度的作用; 催化剂中的活性组分 C u、 Z n、 C e分别以 C u O、 Z n O、 C e O2的形式存在, 并成功负载于载体 A l 2O3; 对于初始质量浓度为9 0 0m g / L的实验室配置苯酚溶液, 在反应温度为1 8 0℃, 压力为4MP a, 搅拌速度为3 0 0r /m i n, 催化剂加入量为0. 1g /( 1 0 0mL) , 反应时间3 0m i n时, 化学需氧量( COD) 去除率达到9 5%。

关键词: 湿式氧化,  , 催化剂, 化学需氧量,  , C u O - Z n O - C e O2 / A l 2O3

Abstract: The C u O - Z n O - C e O2 / A l 2O3 catalyst using in catalytic wet oxidation process was prepared by coprecipitation, and X ray diffraction (XRD) was used to characterize the catalyst. The effect of C u O - Z n O - C e O2 / A l 2O3 on catalyst activity and stability was studied using phenol as the target pollutants. The results shows that addition of Ce increased the degree of dispersion of catalyst system, the active element of Cu, Zn, Ce in catalyst existed in the form of CuO, ZnO and CeO2, and all the active element successfully loaded on carrier A l 2O3. For the phenol wastewater with initial concentration of 900 mg/L, the removal rate of COD reached 95% with reaction temperature 180 ℃, pressure 4 MPa, stirring speed 300 r/min, the catalyst amount 0.1 g/(100 mL), reaction time 30 min.

Key words: Wet air oxidation,    ,  Catalysts,    ,  Chemical oxygen demand,   C u O - Z n O - C e O2 / A l 2O3

引用本文

牟川川, 刘道胜, 贾秀峰, 桂建舟, 刘 丹. C u O - Z n O - C e O2 / A l 2O3 催化剂的催化及表征[J]. 石油化工高等学校学报, 2015, 28(5): 17-19.

Mu Chuanchuan,Liu Daosheng,Jia Xiufeng,et al. Catalytic and Characterization ofC u O - Z n O - C e O2 / A l 2O3 Catalyst[J]. Journal of Petrochemical Universities, 2015, 28(5): 17-19.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal.lnpu.edu.cn/syhg/CN/10.3969/j.issn.1006-396X.2015.05.004

               http://journal.lnpu.edu.cn/syhg/CN/Y2015/V28/I5/17



网站版权 © 2021《石油化工高等学校学报》编辑部

本系统由北京玛格泰克科技发展有限公司设计开发