溶剂水p H对C r 3+聚合物凝胶分子内交联成胶效果影响

doi:10.3969/j.issn.1006-396X.2015.04.015

石油化工高等学校学报 ›› 2015, Vol. 28 ›› Issue (4): 69-74.DOI: 10.3969/j.issn.1006-396X.2015.04.015

溶剂水p H对C r³⁺聚合物凝胶分子内交联成胶效果影响

谢坤, 卢祥国, 曹豹, 曹伟佳, 郭琦, 张宝岩

( 东北石油大学提高油气采收率教育部重点实验室, 黑龙江大庆1 6 3 3 1 8)

收稿日期:2015-03-13 修回日期:2015-04-09 出版日期:2015-08-25 发布日期:2015-08-25
通讯作者: 卢祥国( 1 9 6 0 - ) , 男, 博士, 教授, 博士生导师, 从事提高采收率理论和技术方面的研究; E - m a i l : l u x i a n g g 2 0 0 3@a l i y u n. c o m。
作者简介:谢坤( 1 9 9 1 - ) , 男, 硕士研究生, 从事提高采收率理论和技术方面的研究; E - m a i l : x i e k u n 7 2 5@1 6 3. c o m。
基金资助:
黑龙江省自然科学基金重点项目“ 抗盐型聚合物缔合程度及其油藏适应性研究 ” ( Z D 2 0 1 3 1 2) ; 东北石油大学研究
生创新科研项目“ 疏水缔合聚合物缔合程度渤海油藏适应性研究” ( Y J S C X 2 0 1 4 - 0 1 7 NE PU) 。

Effect of Solvent Water pH on Intramolecular Rosslinked  Gelation Performance of Cr^3+ Polymer Gel

(Key Laboratory of Enhanced Oil and Gas Recovery of Education Ministry, Northeast  Petroleum University, Daqing Heilongjiang 163318, China)

Received:2015-03-13 Revised:2015-04-09 Published:2015-08-25 Online:2015-08-25

摘要/Abstract

摘要： 为进一步探究不同p H条件下C r ³⁺聚合物凝胶“ 分子内” 交联成胶机理, 针对大庆喇嘛甸油田储层地质特征和流体性质, 以聚合物质量浓度、矿化度调节剂浓度和聚铬比为影响因素, 在通过正交试验优选出成胶效果良好的聚合物凝胶配方组成基础上, 研究了p H对C r ³⁺聚合物凝胶成胶效果影响。结果表明, 酸性条件能够促进醋酸铬的电离, 增大多核羟桥配离子与聚合物分子链上羧基之间发生配位反应的概率, 有利于C r ³⁺聚合物凝胶形成 “ 分子内” 交联结构体系; 随溶剂水p H增加, 溶液中 OH^- 数量增加, 参与交联反应的C r ³⁺ 数量减少, 聚合物凝胶分子内” 交联成胶效果变差; 适当降低溶剂水p H可进一步改善聚合物凝胶“ 分子内” 交联成胶效果。

关键词: p H, &ldquo, 分子内&rdquo, 交联, C r ³⁺聚合物凝胶, , 正交试验, 成胶效果, 机理分析

Abstract: In order to further explore intramolecular rosslinked gelation mechanism of Cr^3+ polymer gel under different pH conditions, effect of pH on Cr^3+  polymer gel gelation performance was researched. Polymer gelformulation composition with good gelation performance was obtained by orthogonal experiment taking polymer mass concentration, water solution salinity and "polymer/Cr^3+ " as the influence factors, aimed at Daqing Lamadian oilfield geological characteristics and fluid properties. The results showed that acidic conditions could promote ionization of chromium acetate and increase the number of Cr^3+  in solution, thus increase the probability of coordination reaction between carboxyl in polymer chains and polynuclear olation complex ion, which is in favor of the formation of intramolecular crosslinked Cr^3+  polymer gel system. The number of OH^- was increased with solvent water pH, which could result in the reduction of Cr^3+  involved in crosslinking reaction and gelation performance getting worse accordingly. when the system was similar to intramolecular crosslinked Cr^3+  polymer gel, gelation performance of polymer gel system can be further improved by appropriately reducing pH value of solvent water.

Key words: pH, , Intramolecular rosslinking, , Cr³⁺ polymer gel, , Orthogonal experiment, , Gelation performance, , Mechanism analysis

谢坤, 卢祥国, 曹豹. 溶剂水p H对C r³⁺聚合物凝胶分子内交联成胶效果影响[J]. 石油化工高等学校学报, 2015, 28(4): 69-74.

Xie Kun, Lu Xiangguo, Cao Bao, et al. Effect of Solvent Water pH on Intramolecular Rosslinked  Gelation Performance of Cr^3+ Polymer Gel[J]. Journal of Petrochemical Universities, 2015, 28(4): 69-74.

[1]	延晨政哲, 陈利贞, 高传慧, 武玉民. 基于动态亚胺键的自修复有机硅弹性体的制备及性能研究[J]. 石油化工高等学校学报, 2021, 34(5): 9-15.
[2]	何欣，卢祥国，曹伟佳，陈超，徐浩，张立东. 高盐油藏无机凝胶与泡沫复合调驱研究[J]. 石油化工高等学校学报, 2021, 34(3): 52-57.
[3]	李凤艳, 牟鹏林, 赵天波. 悬浮聚合制备交联聚苯乙烯石蜡微胶囊及性能研究[J]. 石油化工高等学校学报, 2020, 33(3): 8-13.
[4]	李凤艳，胡月，赵劲，赵天波. 交联改性提高水性含氟丙烯酸树脂力学性能[J]. 石油化工高等学校学报, 2020, 33(2): 42-46.
[5]	马永宇, 林梅钦, 王志永, 刘俊辰. 新型耐温聚合物微球的封堵特性研究[J]. 石油化工高等学校学报, 2020, 33(1): 48-53.
[6]	孟祥海，张云宝，夏欢，刘义刚，王威，吕金龙，殷庆国. 渤海油田大尺寸优势通道封堵与调驱技术研究[J]. 石油化工高等学校学报, 2019, 32(4): 44-51.
[7]	田中原，卢祥国，曹伟佳，陈清，闫冬. 自悬浮与普通支撑剂裂缝导流能力实验研究[J]. 石油化工高等学校学报, 2019, 32(3): 33-38.
[8]	孙哲,卢祥国,孙学法,周彦霞. 弱碱三元复合驱增油效果影响因素及其作用机理研究[J]. 石油化工高等学校学报, 2018, 31(01): 35-42.
[9]	程婷婷,侯吉瑞,安昊盈. 自组装颗粒调驱体系注入方式优选实验研究[J]. 石油化工高等学校学报, 2018, 31(01): 49-56.
[10]	史学伟,吴艳阳,徐首红,赵双良. CH-90交换树脂对废水中Co²⁺ 丶Mn²⁺的去除[J]. 石油化工高等学校学报, 2017, 30(5): 1-5.
[11]	胡文学,周如金,沈健. 工艺参数对加氢尾油裂解过程中结焦的影响[J]. 石油化工高等学校学报, 2017, 30(5): 6-11.
[12]	赖君玲,赖晓晨,柳叶,程云,罗根祥. 干水和碱性干碱的制备及催化水解COS的研究[J]. 石油化工高等学校学报, 2017, 30(5): 12-16.
[13]	宋官龙,赵德智,吴青. 反应条件对渣油悬浮床加氢裂化反应的影响[J]. 石油化工高等学校学报, 2017, 30(5): 17-21.
[14]	齐邦峰,宋君辉. 环烷基减压馏分油加氢脱除8种多环芳烃的研究[J]. 石油化工高等学校学报, 2017, 30(5): 22-25.
[15]	杨子浩,赵冀,唐永亮. 微米级交联聚合物微球对核孔膜的封堵作用[J]. 石油化工高等学校学报, 2017, 30(5): 26-31.

溶剂水p H对C r³⁺聚合物凝胶分子内交联成胶效果影响

Effect of Solvent Water pH on Intramolecular Rosslinked  Gelation Performance of Cr^3+ Polymer Gel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics