纳米自组装大孔催化剂对催化裂化柴油的加氢催化性能

李思洋1，赵德智1，王鼎聪2，田野1，宋官龙1，朱珠1，赵春晓1   

  1.  ( 1. 辽宁石油化工大学化学化工与环境学部, 辽宁抚顺1 1 3 0 0 1; 2. 中国石化抚顺石油化工研究院, 辽宁抚顺1 1 3 0 0 1)
  • 收稿日期:2013-08-08 修回日期:2013-09-13 出版日期:2014-02-25 发布日期:2014-06-10
  • 通讯作者: 赵德智( 1 9 5 9 - ) , 男, 硕士, 教授, 从事重油加工、 轻油改质、 非常规能源( 页岩油、 油砂、 生物能源) 等研究; E - m a i l :f s z h a o d e z h i @1 6 3. c o m。
  • 作者简介:李思洋( 1 9 8 8 - ) , 男, 硕士研究生, 从事纳米自组装催化剂对劣质催化裂化柴油加氢性能评价研究; E - m a i l : l i s i y a n g 1 9 8 8@1 6 3. c o m。
  • 基金资助:
    中国石油化工集团公司资助项目( 0 3 0 8 0 1) 。

Preparation of Nano SelfAssembly Macroporous Catalyst and Its  Hydrogenation Performance for FCC Diesel Oil

  1. （1.College of Chemistry，Chemistry Engineering and Environmental Engineering，Liaoning Shihua University, Fushun Liaoning 113001，China； 2.Sinopec Fushun Research Institute of Petroleum and Petrochemicals, Fushun Liaoning 113001, China）
  • Received:2013-08-08 Revised:2013-09-13 Published:2014-02-25 Online:2014-06-10

PDF

摘要： 采用二次纳米自组装方法制备出具有大孔道的催化剂0 1 0 6、 1 2 2 7, 两种纳米自组装催化剂在3 0~1 0 0n m孔径分布分别占1 1%、 2 8%。纳米自组装催化剂具有低堆积密度和高金属含量等特点。在1 0mL固定床微型反应器中, 以镇海炼化的催化裂化柴油为原料, 在温度3 6 0曟、 压力7MP a、 氢油体积比为6 0 0暶1、 体积空速为1. 5h-1条件下, 考察了两种纳米自组装催化剂的初活性评价, 并与现有工业催化剂作对比。结果表明, 两种纳米自组装催化剂0 1 0 6、 1 2 2 7可使催化裂化柴油的含硫质量分数从1 24 0 0毺 g / g分别最低降到4 8 3、 2 8 3毺 g / g, 最高脱硫率分别为9 6. 1 0%、 9 7. 7 1%; 将含氮质量分数从15 0 7毺 g / g分别最低降到3 5. 7、 1 4. 0毺 g / g, 最高脱氮率分别为9 7. 6 3%和9 9 灡 0 0%; 其最高芳烃饱和率分别为6 7. 9 9%和6 8. 8 8%; 而 参比催化剂仅可使催化裂化柴油的含硫质量分数从1 24 0 0毺 g / g最低降到5 3 7毺 g / g, 最高脱硫率为9 4. 5 7%; 将含氮质量分数从15 0 7毺 g / g最低降到6 4. 6毺 g / g, 最高脱氮率为9 5. 5 4%; 其最高芳烃饱和率为6 5. 6 5%。

关键词: 纳米自组装催化剂,    ,  加氢脱硫,    , 加氢脱氮,    , 芳烃饱和,    , 催化裂化柴油

Abstract: Adopting secondary nano selfassembly method to prepare macroporous catalyst（0106，1227）with small stacking density and high metal loading， the distribution of pore volume centralized from 30 nm to 100 nm，which accounts for 11%,28%. The first activity of two kinds of nano selfassembly catalyst（0106，1227） was investigated with Zhenhai FCC diesel oil as feed at reaction temperatures of 360 ℃，reaction pressure of 7 MPa，hydrogenoil volume ratio of 600，volume space velocity oh 1.5 h-1 in a fixed bed micro reactor of 10 mL，and with reference agent as a contrast. The experimental results show that the two kinds of nano selfassembly catalyst （0106，1227）has higher activity of hydrodesulfurization，hydrodenitrificationand aromatics saturation than the reference catalyst.The sulfur mass fraction of FCC diesel [ＫＧ*４]oil[ＫＧ*４] feedstock [ＫＧ*４]could [ＫＧ*４]be [ＫＧ*４]reduced from 12 400 μg/g to 483，283 μg/g which the highest desulfurization rate of 96.10% and 9771%;the nitrogen mass fraction of FCC diesel oil feedstock could be reduced from 1 507 μg/g to 35.7，14 μg/g which the highest denitrification rate of 9763% and 9900%; the highest aromatics saturation rate of 67.99% and 68.88%,while only to 537，64.6 μg/g and 9457%，95.54%，6565% over the reference catalyst.

Key words: Nano selfassembly catalyst,    , 　Hydrodesulfurization,    , 　Hydrodenitrification,    , 　Aromatics saturation,    , 　FCC diesel oil

引用本文

李思洋, 赵德智, 王鼎聪. 纳米自组装大孔催化剂对催化裂化柴油的加氢催化性能[J]. 石油化工高等学校学报, 2014, 27(1): 11-16.

Li Siyang,Zhao Dezhi,Wang Dingcong,et al. Preparation of Nano SelfAssembly Macroporous Catalyst and Its  Hydrogenation Performance for FCC Diesel Oil [J]. Journal of Petrochemical Universities, 2014, 27(1): 11-16.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://journal.lnpu.edu.cn/syhg/CN/10.3969/j.issn.1006-396X.2014.01.003

               https://journal.lnpu.edu.cn/syhg/CN/Y2014/V27/I1/11



网站版权 © 2021《石油化工高等学校学报》编辑部

地址：辽宁省抚顺市望花区丹东路西段1号 电话：024-56860967 E-mail:lnxuebao@126.com 邮编：113001

本系统由北京玛格泰克科技发展有限公司设计开发