双电层纳米材料的制备及在防腐涂料中的应用

doi:10.3969/j.issn.1006-396X.2018.02.003

石油化工高等学校学报 ›› 2018, Vol. 31 ›› Issue (02): 14-19.DOI: 10.3969/j.issn.1006-396X.2018.02.003

双电层纳米材料的制备及在防腐涂料中的应用

王萌^1，李保山¹，吴建华²，方大庆²，王红峰²，郑天水²

(1. 北京化工大学化工资源有效利用国家重点实验室，北京 100029; 2. 厦门双瑞船舶涂料有限公司，福建厦门 361101)

收稿日期:2017-05-05 修回日期:2017-08-18 出版日期:2018-04-26 发布日期:2018-04-25
通讯作者: 李保山（1962-），男，博士，教授，从事应用化学、功能材料等方面的研究；E-mail：bsli@mail.buct.edu.cn
作者简介:王萌（1990-），女，硕士，从事防腐涂料方面的研究； E-mail：wmqiuzhi@163.com
基金资助:
(国家十二五科技支撑项目(2014BAE12B0101);国家自然科学基金项目（21271017）;中央高校基本科研业务费专项资金项目（YS1406）

Preparation of Electric Double Layer Nanomaterials Based on LDHs and Research of the Application in Anticorrosion Coatings

Wang Meng¹，Li Baoshan¹,Wu Jianhua²,Fang Daqing²,Wang Hongfeng²,Zheng Tianshui²

(1. State Key Laboratory of Chemical Resource Engineering, School of Science, Beijing University of Chemical  Technology, Beijing 100029, China; 2. Xiamen Shuangrui Ship Coating Co., Ltd.,Xiamen Fujian 361101,China)

Received:2017-05-05 Revised:2017-08-18 Published:2018-04-26 Online:2018-04-25

摘要/Abstract

摘要： 先对硝酸根水滑石进行剥离以得到带正电荷的电水滑石层板，然后使其吸附一层Cl^-从而形成超分子双电层纳米材料，分别用XRD、HRTEM、FT-IR等对样品进行表征，并将其应用于防腐涂料中，用SEM、极化曲线及交流阻抗技术对图层的防腐性能进行研究。结果表明，这种超分子双电层纳米材料可以大大提高图层的耐腐蚀性能，腐蚀电位可由空白样品的-0.9 V提高到-0.5 V，具有很好的应用前景。

关键词: 水滑石, 超分子, 双电层纳米材料, 防腐涂料

Abstract: In this paper, the hydrotalcite with positive charge was obtained by stripping the nitrate hydrotalcite, then a layer of Cl^- was adsorbed to form electric double layer nanomaterials. The samples were characterized by XRD, HRTEM and FT-IR and used in anticorrosion coatings. The corrosion resistance of the coating was studied by SEM, polarization curve and nyquist curves technology. The results show that this kind of electric double layer nanomaterials can greatly improve the corrosion resistance of the layer, and the corrosion potential can be increased from -0.9 V to -0.5V, which has a good application prospect.

Key words: Hydrotalcite, Supermolecule, Electric double layer nanomaterials, Anticorrosion coating

王萌，李保山，吴建华，方大庆，王红峰，郑天水. 双电层纳米材料的制备及在防腐涂料中的应用[J]. 石油化工高等学校学报, 2018, 31(02): 14-19.

Wang Meng，Li Baoshan,Wu Jianhua,Fang Daqing,Wang Hongfeng,Zheng Tianshui. Preparation of Electric Double Layer Nanomaterials Based on LDHs and Research of the Application in Anticorrosion Coatings[J]. Journal of Petrochemical Universities, 2018, 31(02): 14-19.

[1]	李敏, 李政, 顾贵洲, 于喜洋, 王辉. Zn⁃Mg⁃Al LDO的制备及其除氟性能研究[J]. 石油化工高等学校学报, 2023, 36(5): 73-80.
[2]	赵东启, 顾贵洲, 李政. 水滑石类光催化剂在污水处理中的应用[J]. 石油化工高等学校学报, 2022, 35(3): 36-42.
[3]	于喜洋, 顾贵洲, 李政. 水滑石材料处理工业废水的研究进展[J]. 石油化工高等学校学报, 2021, 34(6): 16-21.
[4]	靳福全, 李晓红, 李东红. C a O / Z n - A l - O固体碱的制备、表征及其催化活性[J]. 石油化工高等学校学报, 2014, 27(5): 43-49.

双电层纳米材料的制备及在防腐涂料中的应用

Preparation of Electric Double Layer Nanomaterials Based on LDHs and Research of the Application in Anticorrosion Coatings