低碳钢在抚顺各典型地区土壤中的腐蚀行为

doi:10.3969/j.issn.1006-396X.2012.05.015

石油化工高等学校学报 ›› 2012, Vol. 25 ›› Issue (5): 59-63.DOI: 10.3969/j.issn.1006-396X.2012.05.015

低碳钢在抚顺各典型地区土壤中的腐蚀行为

史艳华,梁平,张国福

(辽宁石油化工大学机械工程学院,辽宁抚顺113001)

收稿日期:2012-05-17 出版日期:2012-10-25 发布日期:2012-10-25
作者简介:史艳华（１９７１－），女，辽宁锦州市，副教授，博士

Corrosion Behave of Low Carbon Steel in the Typical Soil of Fushun

School of Mechanical Engineering， Liaoning Shihua University, Liaoning Fushun 113001, P.R.China

Received:2012-05-17 Published:2012-10-25 Online:2012-10-25

摘要/Abstract

摘要： 采用埋片和电化学实验研究了常用结构钢20号钢在抚顺5种典型地区（东洲、望花、李石、露天矿、高尔山区）土壤中的腐蚀行为。研究表明,20号钢在5种土壤中的腐蚀速率不同，由高到低顺序为：李石农田区、露天矿区、东洲化工区、望花重工业区、高尔山区，其中腐蚀最严重的地区是李石农田区，年腐蚀速率为0.105 9 mm/a，约为高尔山区的10倍；电化学实验研究表明,20号钢在李石和露天矿区土壤中随浸泡时间延长形成锈层缓慢，锈层疏松不致密，且不连续、不稳定，对20号钢基材起不到保护作用，腐蚀较严重；而东洲化工区、望花重工业区及高尔山区土壤中20号钢表面能快速形成连续、致密且稳定的锈层，对基材起到保护作用，腐蚀较轻。

关键词: 土壤腐蚀 , 抚顺 , 埋片试验 , 电化学测试 , 腐蚀行为

Abstract: The corrosion behave of 20 steel in the five typical soil (Dongzhou, Wanghua, Lishi, Lutian kuang and Gaoer mountain) of Fushun by indoor buried corrosion test and electrochemical test were studied. The research shows that annual corrosion rate of 20 steel different in five typical soil, from high to low is: Lishi， Lutian kuang， Wanghua， Dongzhou， Gaoer mountain, the most serious corrosion of the 20 steel in Lishi area soil, the annual corrosion rate is 0.105 9 mm/a, about 10 times as Gaoer mountain area. The electrochemical research shows the serious corrosion of 20 steel in Lishi and Lutian kuang soil,because the immerse hours of native rust film on the surface of 20 steel is slow, the rust film is loose, not compact, discontinuous and instability, and does not have protective function. On the contrary, a continuous, compact and stable rust film can be formed on the surface of 20 steel in Dongzhou, Wanghua and Gaoer mountain soil which is slightly corroded and has protective function. 

Key words: Soil Corrosion, , Fushun, , Indoor buried corrosion test, , Electrochemical impedance spectroscopy (EIS), , Polarization curve 

史艳华,梁平,张国福. 低碳钢在抚顺各典型地区土壤中的腐蚀行为[J]. 石油化工高等学校学报, 2012, 25(5): 59-63.

SHI Yan-hua, LIANG Ping, ZHANG Guo-fu. Corrosion Behave of Low Carbon Steel in the Typical Soil of Fushun[J]. Journal of Petrochemical Universities, 2012, 25(5): 59-63.

[1]	贺俊凯，王丹，赵猛，宫克，李佳航. A3F和X70钢在H2S环境下腐蚀行为研究[J]. 石油化工高等学校学报, 2021, 34(2): 66-70.
[2]	杨永飞, 姚军, 赵修太, 赵晓珂. 酸化缓蚀剂对N80钢在盐酸溶液中的缓蚀性能[J]. 石油化工高等学校学报, 2009, 22(2): 26-29.
[3]	陈旭, 杜翠薇, 李晓刚, 梁平. 含水率对X70钢在鹰潭酸性土壤中腐蚀行为的影响[J]. 石油化工高等学校学报, 2007, 20(4): 55-58.

低碳钢在抚顺各典型地区土壤中的腐蚀行为

Corrosion Behave of Low Carbon Steel in the Typical Soil of Fushun

PDF

可视化

摘要/Abstract