低氧分压法在服役炉管内表面制备防结焦膜

doi:10.3969/j.issn.1006-396X.2012.04.013

石油化工高等学校学报 ›› 2012, Vol. 25 ›› Issue (4): 57-61.DOI: 10.3969/j.issn.1006-396X.2012.04.013

低氧分压法在服役炉管内表面制备防结焦膜

王华良,高万夫* ,邵明增,王一雄,崔立山

中国石油大学材料科学与工程系,北京102249

收稿日期:2012-06-11 出版日期:2012-08-25 发布日期:2012-08-25
作者简介:王华良（１９８７－），男，山东聊城市，在读硕士
基金资助:
重质油国家重点实验室开发基金项目（２００８０９）

The Synthesis of Anti-Coking Oxide Film for Inner Surface of Cracking Tube in Service by Low Oxygen Partial Pressure

Department of Material Science and Engineering, China University of Petroleum, Beijing 102249, P.R.China

Received:2012-06-11 Published:2012-08-25 Online:2012-08-25

摘要/Abstract

摘要： 利用低氧分压法在已服役炉管的内表面制备防结焦氧化膜。用扫描电子显微镜（SEM）、能谱仪（EDAX）、X射线衍射仪（XRD）及划痕仪等实验手段，研究已服役炉管及氧化膜的形貌、组织结构、氧化膜与基体结合状况及氧化膜的抗结焦性能。结果表明，经过低氧分压处理后，已服役炉管试样表面的Fe，Ni元素含量降低，表面形成了以MnCr₂O₄和Cr₂O₃为主的氧化膜，氧化膜的临界载荷为9.25 N，结焦抑制率达到69.92%，具有明显的防催化结焦效果。

关键词: 已服役炉管 , 低氧分压 , 氧化膜 , 防结焦

Abstract: An anti-coking oxide film was prepared by a low oxygen partial pressure method for inner surface of cracking tube in service. The morphologies, composition and structure of the inner surface, the adhesion between the oxide film and the substrate and the anti-coking performance of the specimen were characterized by SEM, EDAX, X-ray diffraction, scratch tester. The results show that Fe and Ni content decreases after the process of low oxygen partial pressure. The oxide film is mainly composed of MnCr₂O₄ and Cr₂O₃ and the critical load between oxide films and substrates is 9.25 N. The anti-coking ratio reaches 69.92%, it proves that the oxide films can prevent catalytic filament cokes from deposition effectively.

Key words: Cracking tube in service, Low oxygen partial pressure, Oxide film, Anti-coking

王华良,高万夫,邵明增,王一雄,崔立山. 低氧分压法在服役炉管内表面制备防结焦膜[J]. 石油化工高等学校学报, 2012, 25(4): 57-61.

WANG Hua-liang, GAO Wan-fu,SHAO Ming-zeng,et al. The Synthesis of Anti-Coking Oxide Film for Inner Surface of Cracking Tube in Service by Low Oxygen Partial Pressure[J]. Journal of Petrochemical Universities, 2012, 25(4): 57-61.

低氧分压法在服役炉管内表面制备防结焦膜

The Synthesis of Anti-Coking Oxide Film for Inner Surface of Cracking Tube in Service by Low Oxygen Partial Pressure

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 0

编辑推荐

Metrics