Experimental on Corrosion Characteristic of 20# Pipeline Steel in Soil Along Yangtze River in Nanjing

WANG Wen－he¹, SHEN Shi－ming^{1, 2}, YU Xiao－chun^{1, 2}

(1．College of Mechanical and Power Engineering, Nanjing University of Technology, Nanjing Jiangsu 210009，P.R. China; 2．Research Center of Engineering Risk Analysis Technology, SINOPEC, Nanjing Jiangsu 210009, P.R. China)

Received:2007-11-28 Published:2008-12-20 Online:2017-07-05

摘要/Abstract

摘要： 通过实验室内埋片试验研究了20 #钢在南京沿江近中性土壤中的腐蚀规律和机理。在3 种不同土壤
中埋片, 对腐蚀后的试样腐蚀形貌和产物进行EDS 和XRD 分析, 并测定了试样的腐蚀速率、自腐蚀电位以及极化曲
线随时间的变化关系。试验结果表明, 随着时间的延长, 腐蚀速率是不断变化的;3 种不同土壤中的钢试样经过相同
的腐蚀时间后, 1 #和2 #腐蚀最为严重, 3#腐蚀程度稍轻;经过2 个月腐蚀后, 能谱和射线分析其腐蚀产物主要是非
晶质、Fe(OH)3 和Fe2O3 ;不同时间和土壤的电位变化规律是不同的, 与腐蚀速率变化规律是一致的。并探讨了近
中性土壤腐蚀机理。

关键词: 埋地管道 , 近中性土壤 , 腐蚀机理

Abstract: Corrosion law and mechanism of 20# low-carbon steel in near-neutral in soil were studied by experiments of buried specimens in laboratory. In three kinds of soils, the corrosion features and products were analyzed by EDS and XRD, and the relation of corrosion rates, open-circuit potential and polarization curve with times were tested. The results indicate that corrosion rates changed incessantly along. On the condition of the same times, specimens and different soil samples, the corrosive degree of 1# and 2# specimens are serious, but 3# specimen is serious lightly. The corrosion products are main non-crystalloid, Fe（OH）3 and Fe2O3.The change rules of different times and soils are different, and are accordant with that of corrosion rates. The corrosion mechanism is discussed in near-neutral soils lastly.

Key words: Buried pipeline , Near-neutral soil , Corrosion mechanism

王文和,沈士明1, 於孝春. 南京沿江土壤中20#钢管道腐蚀特性试验研究[J]. 石油化工高等学校学报, 2008, 21(4): 59-63.

WANG Wen－he, SHEN Shi－ming, YU Xiao－chun. Experimental on Corrosion Characteristic of 20# Pipeline Steel in Soil Along Yangtze River in Nanjing[J]. Journal of Petrochemical Universities, 2008, 21(4): 59-63.

[1]	李泽, 马贵阳. 埋地输油管道泄漏三维数值模拟[J]. 石油化工高等学校学报, 2015, 28(5): 85-90.
[2]	齐浩,马贵阳,孟向楠,杨娜,高艳波. 不同埋深热油管道数值计算[J]. 石油化工高等学校学报, 2012, 25(6): 63-66.
[3]	刘珂,吴明,邵大伟,范开峰,王卫强. 埋地天然气管道泄漏数值模拟[J]. 石油化工高等学校学报, 2012, 25(6): 59-62.
[4]	陈世一, 吴先策, 江国业. 管道强制电流阴极保护电流和电位计算的数值方法[J]. 石油化工高等学校学报, 2008, 21(3): 75-78.