石油化工高等学校学报

石油化工高等学校学报 ›› 2014, Vol. 27 ›› Issue (2): 21-25.DOI: 10.3969/j.issn.1006-396X.2014.02.005

• 石油化工 • 上一篇    下一篇

A l 3+/阳离子交换树脂催化剂制备及在裂解C 9 馏分聚合中的应用

  

  1. ( 1. 哈尔滨工业大学, 黑龙江哈尔滨1 5 0 0 0 1; 2. 长春工业大学化学工程学院, 吉林长春1 3 0 0 1 2;
    3. 辽宁石油化工大学, 辽宁抚顺1 1 3 0 0 1; 4. 中国石化石油化工管理干部学院, 北京1 0 0 0 1 2)
  • 收稿日期:2014-02-26 修回日期:2014-03-23 出版日期:2014-04-25 发布日期:2014-06-16
  • 通讯作者: 亓玉台( 1 9 5 6 - ) , 男, 博士, 教授, 从事原油组成分析及重油加工工艺研究;E - m a i l : q i y u t a i @2 6 3. n e t 。
  • 作者简介:杨靖华( 1 9 7 5 - ) , 女, 博士研究生, 讲师, 从事轻质油改质和重质油加工工艺研究;E - m a i l : j i n g h u a 8 7 y a n g@1 6 3. c o m
  • 基金资助:
    吉林省自然科学基金项目( 2 0 1 2 1 2 1 7 2) 。

Preparation and Application of Al3+/CationExchange Resin  Catalyst for Polyreaction of Cracking C9 Fraction

  1. (1. Harbin Institute of Technology, Harbin Heilongjiang 150001,China; 2. School of Chemical Engineering, Changchun University of Technology, Changchun Jinlin 130012,China; 3.Liaoning Shihua University, Fushun Liaoning 113001,China; 4.Sinopec Management Institute, Beijing 100012,China)
  • Received:2014-02-26 Revised:2014-03-23 Published:2014-04-25 Online:2014-06-16

PDF

摘要： 以苯乙烯系7 3 2型阳离子交换树脂为载体, 通过离子交换络合无水 A l C l 3, 制备 A l3+/阳离子交换树脂催化剂, 并考察了制备 A l3+/阳离子交换树脂催化的工艺条件。实验结果表明, 7 3 2型阳离子交换树脂减压干燥1 2h, 以四氯化碳为溶剂, 交换温度7 2℃, 无水 A l C l 3 与7 3 2型阳离子交换树脂质量比为1. 1∶1, 交换时间为1 0h,后处理采用蒸馏水 - 乙醇( 质量分数9 5%) - 蒸馏水洗, Al3+的负载量达到2. 2 9%。将 Al3+/阳离子交换树脂催化剂用于乙烯裂解副产C 9  馏分催化聚合反应。在反应温度为5 0℃, 反应时间6h, 催化剂中 Al3+质量分数为2%, 得到的聚合物通过红外分析结构, 结果表明 A l 3+/阳离子交换树脂固体催化剂在多烯烃系统里具有良好的催化效果。使用树脂固体催化剂催化聚合多烯烃, 省去脱除催化剂过程, 不产生反应系统的洗脱废液。

关键词: 三氯化铝,    ,  , 阳离子交换树脂,    ,  聚合反应,    ,  , 固体酸催化剂

Abstract: Al3+/cation exchange resin catalyst was prepared by ion exchange complex, with commercial 732 cation exchange resin as carrier and aluminium trichloride as ion exchangers. The process conditions of the preparation of Al3+/cation exchange resin catalyst were investigated. The experimental results showed that the quality of supported on Al3+ can be up to 2.29% when the decompression drying time of 732 cation exchange resin was 12 h, the solvent was carbon tetrachloride, exchange temperature was 72 ℃, the mass ratio of aluminium trichloride and 732 cation exchange resin was 1∶1, exchange time was 10 h and postprocessing was in turn with the distilled water and ethanol (95%). Al3+/cation exchange resin catalyst was used to catalyze the polymerization of ethylene cracking fraction（C 9 ）.Al3+/cation exchange resin had good catalytic effect in the mixed olefin system when the reaction occurred at 50 ℃ for 6 h with catalyst dosage 2%( according to the quality of Al3+ content meter). Structure of polymer was verified by infrared spectroscopy.

Key words: Aluminum chloride,    ,  Cation exchange resin,    ,  Polymerization,    ,  Solid acid catalyst

引用本文

杨靖华, 曹祖宾, 亓玉台. A l 3+/阳离子交换树脂催化剂制备及在裂解C 9 馏分聚合中的应用[J]. 石油化工高等学校学报, 2014, 27(2): 21-25.

Yang Jinghua,Cao Zubin,Qi Yutai. Preparation and Application of Al3+/CationExchange Resin  Catalyst for Polyreaction of Cracking C9 Fraction[J]. Journal of Petrochemical Universities, 2014, 27(2): 21-25.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://journal.lnpu.edu.cn/syhg/CN/10.3969/j.issn.1006-396X.2014.02.005

               https://journal.lnpu.edu.cn/syhg/CN/Y2014/V27/I2/21