Synthesis and Properties of Poly -Alpha -Olefin Wi th 1 -Decene

  

  1. 1 .Liaoning University of Petroleum & Chemical Technology , Fushun Liaoning 113001 , P .R .China ;
    2 .No .1 Plant of Funshun Petrochemical Company of CCPC , Fushun Liaoning 113003, P .R .China
  • Received:2005-04-12 Published:2005-03-25 Online:2005-03-25

癸烯-1 聚α-烯烃合成油的合成及性质

张志峰1 , 2 , 丁洪生1 , 权成光2 , 钱建华1   

  1. 1 .辽宁石油化工大学, 辽宁抚顺113001 ;
    2 .中油抚顺石油化工公司石化一厂, 辽宁抚顺113003
  • 作者简介:张志峰(1966 -), 男, 辽宁朝阳市, 在读工程硕士。

Abstract:

   Poly -alpha -olefin is one kind of important lubricants.The polymerization of 1-decene catalyzed by boron trifluoride catalyst was studied.The properties of the synthesized poly -alpha - olefin lubricant were investigated under various kinds of technological conditions, for example , reaction temperature , reaction pressure , reaction time , various kinds of initiator , mole ratio of the catalyst and promoter .The optimum condition for the synthesis of poly-alpha-olefin are as follows :the reaction temperature is 30 ℃, the reaction pressure is 0 .4 MPa , the reaction time is 3 hours, the initiator is butanol, and the mole ratio of the catalyst to the initiator is 2 .0.The components of poly -alpha -olefin lubricants were analyzed using gas chromatog raph.Under the optimum technological conditions, the conversion of 1-decene is 99.8%, the mass fraction of dimer is 2 .5 %, the mass fraction of trimer is 64 .5%, the mass fraction of tetramer is 27.5 %, and the mass fraction of pentamer is 5 .6 %.The proper ties of the poly -alpha -olefin oils w ere studied by kinematical viscometer and petrolic products distilling test instrument .The viscosity is 4.80 mm2/s and 23 .09 mm2/s at 100 ℃ and 40 ℃, respectively .The viscosity index is 132 , the freezing point is -60 ℃.

Key words:  1 -Decene ,  PAO,  Snthesis technology ,  Poperty

摘要:      聚α-烯烃合成油(PAO)是重要的合成润滑油之一。使用三氟化硼为催化剂对癸烯-1 聚合物合成油进行了研究。考察了不同温度、压力、反应时间、引发剂、催化剂与引发剂的摩尔比等工艺条件对癸烯-1 聚合及合成油性能的影响。确定了合成聚α-烯烃合成油的最佳工艺条件:温度为30 ℃, 压力为0 .4 MPa , 反应时间为3 h ,以正丁醇作引发剂, 催化剂与引发剂的摩尔比为2.0。采用气相色谱法对聚合物合成油的组分进行了分析。在最佳工艺条件下, 癸烯-1 的转化率为99.8%, 二聚物的质量分数为2.5%, 三聚物的质量分数为64.5%, 四聚物的质量分数为27 .5 %, 五聚物的质量分数为5.6%。采用运动粘度仪和石油产品馏程测定器等仪器研究了聚合物合成油的物化性能, 100 ℃的粘度为4.80 mm2/s , 40 ℃的粘度为23.09 mm2/s , 其粘度指数为132 , 凝点为-60 ℃。

关键词: 癸烯-1 ,  聚α-烯烃合成油,  合成工艺,  性能

Cite this article

ZHANG Zhi -feng,DING Hong -sheng,et al. Synthesis and Properties of Poly -Alpha -Olefin Wi th 1 -Decene[J]. Journal of Liaoning Petrochemical University, 2005, 25(3): 24-27.

张志峰, 丁洪生,权成光,钱建华. 癸烯-1 聚α-烯烃合成油的合成及性质[J]. 辽宁石油化工大学学报, 2005, 25(3): 24-27.

share this article

0
    /   /   Recommend

Add to citation manager EndNote|Ris|BibTeX

URL: https://journal.lnpu.edu.cn/EN/

         https://journal.lnpu.edu.cn/EN/Y2005/V25/I3/24