Research of Waste Unsaturated Polyester Resin Split ting Technique

  

  1. School of In formation Engineering , Liaoning University of Petroleum & Chemical Technology ,
    Fushun Liaoning 113001 , P .R .China
  • Received:2004-07-17 Published:2005-03-20 Online:2017-04-14

废旧不饱和聚酯树脂裂解工艺

杜昭辉   

  1. 辽宁石油化工大学信息工程学院, 辽宁抚顺113001
  • 作者简介:杜昭辉(1949 -), 男, 辽宁抚顺县, 高级工程师

Abstract:

        The technique to produce fuel oil from unsaturated polyester resin(UPR)wastes was studied by pyrolysis.The process conditions for thermal cracking and catalytic cracking w ere investigated systematically .The experimental results indicate that the temperature for catalytic cracking is 400 ~ 450 ℃ which is about 100 ℃ lower than that for thermal cracking , the yield of liquid phase pro duct increases about 20 %, the reaction time is 70 ~ 80 minutes, and the catalyst -oil mass ratio is 1∶5.Four kinds of catalysts were evaluated as per catalytic property with the results that the yield of liquid phase product is 58 .22%~ 59.14 %with the YB-2 catalyst independently and the best yield of liquid phase pro duct is 68 .76% with both the YB-1 and YB -2.I t is indicated that the best way to reduce the environmental pollution of waste unsaturated polyester resin is by its catalytic cracking .

Key words: Unsaturated polyester resins,    , Catalytic cracking ,    , Flue oil

摘要:         对不饱和聚酯树脂(UPR)废料裂解制燃料油技术进行了研究, 系统地考察了热裂解和催化裂解反应工艺条件。试验结果表明, 催化裂解所需反应温度比热裂解反应温度降低了100 ℃, 液相产品收率提高了20 %。试验确定催化裂解反应温度为400 ~ 450 ℃, 反应时间为70 ~ 80 min;剂油质量比为1∶5。试验对4 种催化剂的催化性能进行了评价, 研究表明, 单独使用YB-2 催化剂, 液相产品收率为58 .22%~ 59.14 %;YB-1 和YB-2 混合使用, 最高液相产品收率为68.76%。通过试验证明, 应用催化裂解技术是解决废旧不饱和聚酯树脂对环境污染问题的最佳方案。

关键词: 不饱和聚酯树脂,    , 催化裂解,    , 燃料油

Cite this article

DU Zhao -hui. Research of Waste Unsaturated Polyester Resin Split ting Technique[J]. Journal of Liaoning Petrochemical University, 2005, 25(1): 16-19.

杜昭辉. 废旧不饱和聚酯树脂裂解工艺[J]. 辽宁石油化工大学学报, 2005, 25(1): 16-19.

share this article

0
    /   /   Recommend

Add to citation manager EndNote|Ris|BibTeX

URL: https://journal.lnpu.edu.cn/EN/

         https://journal.lnpu.edu.cn/EN/Y2005/V25/I1/16