硫酸盐还原菌对CaCO3垢层下20号钢腐蚀的影响

李东博1(), 董美1, 杜胜男1, 闫茂成2, 王卫强1()   

  1. 1.辽宁石油化工大学 石油天然气工程学院,辽宁 抚顺 113001
    2.中国科学院金属研究所 国家金属腐蚀控制工程技术研究中心,辽宁 沈阳 110016
  • 收稿日期:2021-03-29 修回日期:2021-04-21 出版日期:2022-08-25 发布日期:2022-09-26
  • 通讯作者: 王卫强
  • 作者简介:李东博(1996⁃),男,硕士研究生,从事油气管道腐蚀与防护方向研究;E⁃mail:790437137@qq.com
  • 基金资助:
    辽宁省教育厅项目(L20190008)

Effect of Sulfate⁃Reducing Bacteria on Corrosion of 20# Steel under CaCO3 Scale

Dongbo Li1(), Mei Dong1, Shengnan Du1, Maocheng Yan2, Weiqiang Wang1()   

  1. 1.College of Petroleum Engineering,Liaoning Petrochemical University,Fushun Liaoning 113001,China
    2.State Key Laboratory for Corrosion and Protection,Metal Research Chinese Academy of Sciences,Shenyang Liaoning 110016,China
  • Received:2021-03-29 Revised:2021-04-21 Published:2022-08-25 Online:2022-09-26
  • Contact: Weiqiang Wang

摘要:

采用室内模拟实验的方法,研究了硫酸盐还原菌(SRB)和CaCO3垢层共存对20号钢腐蚀行为的影响。通过腐蚀失重法研究平均腐蚀速率,通过电化学阻抗谱(EIS)和开路电位(OCP)研究注入水溶液中20号钢腐蚀电化学行为,利用扫描电镜(SEM)、EDS和Raman光谱分析20号钢表面腐蚀产物的形貌和成分,采用激光共聚焦显微镜(CLSM)分析20号钢的点蚀坑深度。结果表明,SRB与CaCO3垢层存在协同作用,CaCO3垢层的孔隙率和垢层下的厌氧环境为SRB的黏附和生长提供了便利的条件,接种SRB对CaCO3垢层下20号钢的均匀腐蚀和局部腐蚀均有促进作用。

关键词: 腐蚀, 硫酸盐还原菌(SRB), CaCO3垢层, 20号钢, 注水系统

Abstract:

The influence of sulfate reducing bacteria (SRB) and CaCO3 scale layer on the corrosion behavior of 20# steel was studied by laboratory simulation experiment. The uniform corrosion rate was studied by corrosion weight loss method.The corrosion electrochemical behavior of 20# steel in the injected aqueous solution was studied by electrochemical impedance spectroscopy (EIS) and open circuit potential (OCP). The morphology and composition of corrosion products on the surface of 20# steel were analyzed by scanning electron microscopy (SEM), EDS and Raman spectroscopy. The pitting pit depth of 20# steel was analyzed by laser confocal microscopy (CLSM). The results show that there is a synergistic effect between SRB and CaCO3 scale layer. The porosity of CaCO3 scale layer and the anaerobic environment under the scale layer provide convenient conditions for the adhesion and growth of SRB. The inoculation of SRB can promote the uniform corrosion and local corrosion of 20# steel under the CaCO3 scale layer.

Key words: Corrosion, Sulfate?reducing bacteria (SRB), CaCO3 scale layer, 20# steel, Water injection system

中图分类号: 

引用本文

李东博, 董美, 杜胜男, 闫茂成, 王卫强. 硫酸盐还原菌对CaCO3垢层下20号钢腐蚀的影响[J]. 辽宁石油化工大学学报, 2022, 42(4): 17-24.

Dongbo Li, Mei Dong, Shengnan Du, Maocheng Yan, Weiqiang Wang. Effect of Sulfate⁃Reducing Bacteria on Corrosion of 20# Steel under CaCO3 Scale[J]. Journal of Liaoning Petrochemical University, 2022, 42(4): 17-24.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://journal.lnpu.edu.cn/CN/10.3969/j.issn.1672-6952.2022.04.004

               https://journal.lnpu.edu.cn/CN/Y2022/V42/I4/17