碳材料为基础的电化学法去除水中重金属研究进展

doi:10.3969/j.issn.1006-396X.2022.04.008

摘要/Abstract

摘要：

电化学处理技术已广泛用于水体重金属的去除研究。其中，具有导电性强、比表面积大、结构可控等性能的碳基电极在电化学处理和回收重金属方面表现出巨大的应用前景。主要介绍了碳纳米管、石墨烯、活性炭等碳基电极通过电吸附、电氧化还原以及电沉积等电化学方法去除与回收水中重金属的研究进展，并展望了碳材料为基础的电化学处理重金属的发展趋势。

关键词: 水处理, 碳材料, 电化学处理, 重金属, 环境保护

Abstract:

Electrochemical treatment technologies have been widely used to remove heavy metals in water.Specifically,carbon?based electrodes show positive application prospects in electrochemical treatment and recovery of heavy metals due to their strong electrical conductivity,large specific surface area,and controllable structure.This paper reviewed the research progress in the removal and recovery of heavy metals in electrochemical fields,such as electro?adsorption,electro?reduction,electro?oxidation,and electro?deposition by carbon?based electrodes including carbon nanotubes,graphene,and activated carbon.In addition,the development trends of removing heavy metals by electrochemical treatment technologies based on carbon materials were predicted.

Key words: Water treatment, Carbon materials, Electrochemical treatment, Heavy metal, Environmental protection

中图分类号:

TQ110.9

曹瑜寒, 王荣忠, 张月华, 彭国文, 曾庆意. 碳材料为基础的电化学法去除水中重金属研究进展[J]. 石油化工高等学校学报, 2022, 35(4): 52-59.

Yuhan Cao, Rongzhong Wang, Yuehua Zhang, Guowen Peng, Qingyi Zeng. Removal of Heavy Metals in Water by Electrochemical Treatment Technologies Based on Carbon Materials[J]. Journal of Petrochemical Universities, 2022, 35(4): 52-59.

图/表 6

图1 电化学还原法机理示意图

Fig.1 Mechanism diagram of electro?reduction

图2 电化学氧化法机理示意图

Fig.2 Mechanism diagram of electro?oxidation

图3 电吸附法机理示意图

Fig.3 Mechanism diagram of electro?adsorption

图4 电解法机理示意图

Fig.4 Mechanism diagram of electrolysis

图5 电沉积法机理示意图

Fig.5 Mechanism diagram of electro?deposition

表1 电化学处理方法的比较

Table 1 Comparison of electrochemical treatment methods

处理方法	优点	缺点	碳基电极	适用范围
电化学还原法	同时去除重金属离子和回收高纯度重金属	电流密度低，电解速率差，耗能大	碳纳米管电极、石墨烯基电极、活性炭基电极	可用于还原六价铬
电化学氧化法	能耗小，成本低，占地面积小，对重金属具有选择性	效率低，影响因素多，原位生成的活性物质(H₂O₂、 $⋅$ OH、 $⋅$ O $2 -$ 等)相对较少且不稳定	石墨烯基电极、三维网状玻璃态碳电极	可用于氧化三价砷
电吸附法	操作灵活，成本低，无二次污染，吸附量大，自动化程度高；电极材料可以再生，使用寿命较长	在电极处发生不需要的反应，这将导致导电性不足；样品经电吸附法处理后，仍会存在重金属离子残留	活性炭基电极、碳纳米管电极、石墨烯基电极、碳气凝胶基电极、其他碳基电极	可去除砷、铬、镉、铜、铅、锌、镍、铁、铅等重金属离子
电解法	一次去除多种污染物，不消耗化学药剂，无二次污染，能直接回收有价值的金属	耗能高，处理水量小；电极材料消耗较大，容易发生副反应，电极易钝化；电解时析氧、析氢或析氯时产生不安全因素，出水水质差	碳气凝胶电极、三维网状玻璃态碳电极、活性炭基电极	可用于处理含铬、铜、钴、镍等重金属废水
电沉积法	不需要化学试剂，不产生污泥，选择性高，运行成本低，可回收重金属	难以处理低浓度重金属废水；产生沉积物，释放气体，这可能会引起安全问题；在酸性条件下电极腐蚀严重，发生析氧等副反应	三维网状玻璃态碳电极、石墨烯基电极	可用于去除铅、铜、锌等重金属离子

表1 电化学处理方法的比较

Table 1 Comparison of electrochemical treatment methods

处理方法	优点	缺点	碳基电极	适用范围
电化学还原法	同时去除重金属离子和回收高纯度重金属	电流密度低，电解速率差，耗能大	碳纳米管电极、石墨烯基电极、活性炭基电极	可用于还原六价铬
电化学氧化法	能耗小，成本低，占地面积小，对重金属具有选择性	效率低，影响因素多，原位生成的活性物质(H₂O₂、 $⋅$ OH、 $⋅$ O $2 -$ 等)相对较少且不稳定	石墨烯基电极、三维网状玻璃态碳电极	可用于氧化三价砷
电吸附法	操作灵活，成本低，无二次污染，吸附量大，自动化程度高；电极材料可以再生，使用寿命较长	在电极处发生不需要的反应，这将导致导电性不足；样品经电吸附法处理后，仍会存在重金属离子残留	活性炭基电极、碳纳米管电极、石墨烯基电极、碳气凝胶基电极、其他碳基电极	可去除砷、铬、镉、铜、铅、锌、镍、铁、铅等重金属离子
电解法	一次去除多种污染物，不消耗化学药剂，无二次污染，能直接回收有价值的金属	耗能高，处理水量小；电极材料消耗较大，容易发生副反应，电极易钝化；电解时析氧、析氢或析氯时产生不安全因素，出水水质差	碳气凝胶电极、三维网状玻璃态碳电极、活性炭基电极	可用于处理含铬、铜、钴、镍等重金属废水
电沉积法	不需要化学试剂，不产生污泥，选择性高，运行成本低，可回收重金属	难以处理低浓度重金属废水；产生沉积物，释放气体，这可能会引起安全问题；在酸性条件下电极腐蚀严重，发生析氧等副反应	三维网状玻璃态碳电极、石墨烯基电极	可用于去除铅、铜、锌等重金属离子

参考文献 40

1	Ngah W S W，Hanafiah M A K M.Removal of heavy metal ions from wastewater by chemically modified plant wastes as adsorbents： A review［J］.Bioresource Technology，2008，99（10）：3935⁃3948.
2	Chu Z J，Fan X H，Wang W N，et al.Quantitative evaluation of heavy metals' pollution hazards and estimation of heavy metals' environmental costs in leachate during food waste composting［J］.Waste Management，2019，84：119⁃128.
3	Oturan M A，Aaron J J.Advanced oxidation processes in water/wastewater treatment：Principles and applications.A review［J］.Critical Reviews in Environmental Science and Technology，2014，44（23）：2577⁃2641.
4	Chen G H.Electrochemical technologies in wastewater treatment［J］.Separation and Purification Technology，2004，38（1）：11⁃41.
5	汤佳玉，孔鹏飞，鞠佳，等.不同结构碳纳米管吸附胆红素的研究［J］.辽宁石油化工大学学报，2021，41（5）：38⁃43.
	Tang J Y，Kong P F，Ju J，et al.Adsorption of bilirubin by carbon nanotubes with different structures［J］.Journal of Liaoning Petrochemical University，2021，41（5）：38⁃43.
6	Zhu Y S，Zhang G J，Xu C，et al.Interconnected graphene hollow shells for high⁃performance capacitive deionization［J］.ACS Applied Materials & Interfaces，2020，12（26）：29706⁃29716.
7	Liu D，Shen J，Li Y J，et al.Pore structures of carbon aerogels and their effects on electrochemical supercapacitor performance［J］.Acta Phys.Chim.Sin.，2012，28：843⁃849.
8	Choi J H.Fabrication of a carbon electrode using activated carbon powder and application to the capacitive deionization process［J］.Sep.Purif.Technol.，2010，70（3）：362⁃366.
9	Liu Y X，Yuan D X，Yan J M，et al.Electrochemical removal of chromium from aqueous solutions using electrodes of stainless steel nets coated with single wall carbon nanotubes［J］.Journal of Hazardous Materials，2011，186（1）：473⁃480.
10	Velasco G，Gutiérrez⁃Granados S，Ponce de León C，et al.The electrochemical reduction of Cr（VI） ions in acid solution at titanium and graphite electrodes［J］.Journal of Environmental Chemical Engineering，2016，4（3）：3610⁃3617.
11	Zhang Y M，Zhang D D，Zhou L C，et al.Polypyrrole/reduced graphene oxide aerogel particle electrodes for high⁃efficiency electro⁃catalytic synergistic removal of Cr（VI） and bisphenol A［J］.Chemical Engineering Journal，2018，336：690⁃700.
12	Mohanraj P，AllwinEbinesar J S S，Amala J，et al.Biocomposite based electrode for effective removal of Cr （VI） heavy metal via capacitive deionization［J］.Chemical Engineering Communication，2019，207（6）：775⁃789.
13	Li X H，Liu F，Zhang W F，et al.Electrocatalytical oxidation of arsenite by reduced graphene oxide via in⁃situ electrocatalytic generation of H₂O₂［J］.Environmental Pollution，2019，254：112958.
14	Rivera J F，Pignot⁃Paintrand I，Pereira E，et al.Electrosynthesized iridium oxide⁃polymer nanocomposite thin films for electrocatalytic oxidation of arsenic（III）［J］.Electrochimica Acta，2013，110：465⁃473.
15	Chen R，Sheehan T，Ng J L，et al.Capacitive deionization and electrosorption for heavy metal removal［J］.Environmental Science⁃Water Research & Technology，2020，6（2）：258⁃282.
16	Dai M，Xia L，Song S X，et al.Electrosorption of As（III） in aqueous solutions with activated carbon as the electrode［J］.Applied Surface Science，2018，434：816⁃821.
17	Huang S Y，Fan C S，Hou C H.Electro⁃enhanced removal of copper ions from aqueous solutions by capacitive deionization［J］.Journal of Hazardous Materials，2014，278：8⁃15.
18	Fan C S，Tseng S C，Li K C，et al.Electro⁃removal of arsenic（III） and arsenic（V） from aqueous solutions by capacitive deionization［J］.Journal of Hazardous Materials，2016，312：208⁃215.
19	Dai M，Zhang M，Song S X，et al.Combined electrosorption and chemisorption of As（V） in water by using Fe⁃rGO@AC electrode［J］.ACS Sustainable Chemistry & Engineering，2017，5（8）：6532⁃6538.
20	李秀玲，黄金萍，石新彪，等.用载钛改性活性炭纤维电极电吸附水中Cr（VI）［J］.湿法冶金，2021，40（3）：239⁃244.
	Li X L，Huang J P，Shi X B，et al.Electroadsorption of Cr（V）in water using titanium carrving modified activated carbon fiber［J］.Hydrometallurgy of China，2021，40（3）：239⁃244.
21	Chen Y P，Peng L，Zeng Q R，et al.Removal of trace Cd（II） from water with the manganese oxides/ACF composite electrode［J］.Clean Technologies and Environmental Policy，2014，17（1）：49⁃57.
22	Hu C Z，Liu F Y，Lan H C，et al.Preparation of a manganese dioxide/carbon fiber electrode for electrosorptive removal of copper ions from water［J］.Journal of Colloid and Interface Science，2015，446：359⁃365.
23	Huang C C，Su Y J.Removal of copper ions from wastewater by adsorption/electrosorption on modified activated carbon cloths［J］.Journal of Hazardous Materials，2010，175（1⁃3）：477⁃483.
24	Sun J Q，Liu L F，Yang F L.A WO₃/PPy/ACF modified electrode in electrochemical system for simultaneous removal of heavy metal ion Cu²⁺ and organic acid［J］.Journal of Hazardous Materials，2020，394：122534.
25	Liu L H，Qiu G H，Suib S L，et al.Enhancement of Zn²⁺ and Ni²⁺ removal performance using a deionization pseudocapacitor with nanostructured birnessite and its carbon nanotube composite electrodes［J］.Chemical Engineering Journal，2017，328：464⁃473.
26	Zhan Y K，Pan L K，Nie C Y，et al.Carbon nanotube–chitosan composite electrodes for electrochemical removal of Cu（II） ions［J］.Journal of Alloys and Compounds，2011，509（18）：5667⁃5671.
27	Li H B，Zou L D，Pan L K，et al.Using graphene nano⁃flakes as electrodes to remove ferric ions by capacitive deionization［J］.Separation and Purification Technology，2010，75（1）：8⁃14.
28	王一明，黄玮，丛玉凤.新型GO/MoS₂复合电极的制备及对铅离子的吸附［J］.石油化工高等学校学报，2021，34（1）：28⁃33.
	Wang Y M，Huang W，Cong Y F.A novel GO/MoS₂ composite electrode：Preparation and application in Pb（II） adsorption［J］.Journal of Petrochemical Universities，2021，34（1）：28⁃33.
29	Bautista⁃Patacsil L，Lazarte J P L，Dipasupil R C，et al.Deionization utilizing reduced graphene oxide⁃titanium dioxide nanotubes composite for the removal of Pb²⁺and Cu²⁺［J］.Journal of Environmental Chemical Engineering，2019，8（3）：103063.
30	Zhai Z Z，Wang S S，Xu Y L，et al.Carbon aerogels with modified pore structures as electrode materials for supercapacitors［J］.Journal of Solid State Electrochemistry，2017，21（12）：3545⁃3555.
31	Rana⁃Madaria P，Nagarajan M，Rajagopal C，et al.Removal of chromium from aqueous solutions by treatment with carbon aerogel electrodes using response surface methodology［J］.Industrial & Engineering Chemistry Research，2005，44（17）：6549–6559.
32	Cao Z L，Zhang C，Yang Z X，et al.Preparation of carbon aerogel electrode for electrosorption of copper ions in aqueous solution［J］.Materials，2019，12（11）：1864.
33	Huang C C，He J C.Electrosorptive removal of copper ions from wastewater by using ordered mesoporous carbon electrodes［J］.Chemical Engineering Journal，2013，221：469⁃475.
34	Rana P，Mohan N，Rajagopal C.Electrochemical removal of chromium from wastewater by using carbon aerogel electrodes［J］.Water Research，2004，38（12）：2811⁃2820.
35	Dell'Era A，Pasquali M，Lupi C，et al.Purification of nickel or cobalt ion containing effluents by electrolysis on reticulated vitreous carbon cathode［J］.Hydrometallurgy，2014，150：1⁃8.
36	Chen F Y，Hu C Z，Sun M，et al.Enhancing destruction of copper （I） cyanide and subsequent recovery of Cu（I） by a novel electrochemical system combining activated carbon fiber and stainless steel cathodes［J］.Chemical Engineering Journal，2017，330：1187⁃1194.
37	Ramalan N H M，Karoonian F S，Etesami M，et al.Impulsive removal of Pb（II） at a 3⁃D reticulated vitreous carbon cathode［J］.Chemical Engineering Journal，2012，203：123⁃129.
38	Li X H，Li H Y，Xu X J，et al.Preparation of a reduced graphene oxide @ stainless steel net electrode and its application of electrochemical removal Pb（II）［J］.Journal of The Electrochemical Society，2017，164（4）：E71⁃E77.
39	Hannula P M，Khalid M K，Janas D，et al.Energy efficient copper electrowinning and direct deposition on carbon nanotube film from industrial wastewaters［J］.Journal of Cleaner Production，2018，207：1033⁃1039.
40	Zhang L G，Xu Z M，He Z.Selective recovery of lead and zinc through controlling cathodic potential in a bioelectrochemically⁃assisted electrodeposition system［J］.Journal of Hazardous Materials，2020，386：121941.

[1]	刘瑞娟, 杨兰, 苗时雨, 李艳红, 安晓强, 兰华春. 废膜炭吸附去除废水中典型污染物的性能研究[J]. 石油化工高等学校学报, 2024, 37(2): 1-8.
[2]	张利星, 张熊, 李晨, 吴志勇, 曾涛明, 马向东. 煤基碳负极材料在锂离子电池中的应用研究进展[J]. 石油化工高等学校学报, 2022, 35(6): 10-18.
[3]	孟秀红, 张乐, 梁雪珍, 段晓静, 林文杰, 段林海. 可控条件对钾铈镧氧化物催化氧化碳烟颗粒的影响[J]. 石油化工高等学校学报, 2021, 34(4): 21-26.
[4]	沙畅畅, 毛杨杨, 曹永安, 王文举. 用于锂硫电池正极的生物质碳材料制备与应用[J]. 石油化工高等学校学报, 2020, 33(3): 1-7.
[5]	沙畅畅，陈宇超，王心妤，王文举. 太阳能驱动水蒸发装置中的碳基光吸收材料的研究进展[J]. 石油化工高等学校学报, 2019, 32(5): 1-7.
[6]	史学伟,吴艳阳,徐首红,赵双良. CH-90交换树脂对废水中Co²⁺ 丶Mn²⁺的去除[J]. 石油化工高等学校学报, 2017, 30(5): 1-5.
[7]	苏鑫,卢祥国,曹伟佳,杨怀军,张杰. Ca2+ 和Mg2+ 对聚/表二元体系性能影响研究#br# ———以大港孔南高盐高温高凝油藏为例[J]. 石油化工高等学校学报, 2016, 29(2): 71-75.
[8]	黄启玉, 毕权. 油田污水处理新技术在低渗透油田的应用[J]. 石油化工高等学校学报, 2015, 28(5): 69-73.
[9]	史博, 陈涛, 常旭轩, 郭勇, 周圣昊. 斜板溶气气浮处理油田污水实验研究[J]. 石油化工高等学校学报, 2015, 28(5): 74-77.
[10]	邓政义, 赵岷, 黄醒. 新型氮化碳材料的合成及其吸附性能的研究[J]. 石油化工高等学校学报, 2014, 27(5): 33-38.
[11]	韩春玉,韩春芳,刘春生. 聚合镁铝絮凝剂的合成及对废水COD的脱除研究[J]. 石油化工高等学校学报, 2010, 23(2): 58-60.