Abstract: The property and composition of ethylene cracking tar were investigated by four component analyses and the method of ndM. The results were shown that amount of the aromatic hydrocarbon, colloid and asphaltene was higher in the ethylene cracking tar. On the other hand, the delayed coke simulation test was carried on the selfmade apparatus based on the ethylene cracking tar as materials or doping different ratio of the ethylene cracking tar into the coking materials as material under the conditions was that the 500 ℃ and normal atmosphere. The results showed that the fraction of gasoline and wax oil was decreased, but the fraction of diesel oil and coke was increased under the doping ratio of ethylene cracking tar in coke material was increased. Compared with the industrial production device, under the doping ratio of ethylene cracking tar was 20%, the density of gasoline was nearly not changed, the fraction of sulfur and actual colloid were increased slightly, the initial boiling point and dry point of the middle distillate (200～350 ℃) was nearly not changed, however the density of the middle distillate (200～350 ℃) was increased, but the actual colloid was decreased. As for the coke, the fraction of volatile and ash was increased, but the fraction of water and sulfur was decreased apparent. The result mentioned above showed that the doping ratio of ethylene cracking tar was 20% will not affect apparently the production of the delayed coking. 

Key words: Ethylene cracking tar,    ,  Composition,    ,  Delayed coke simulation test,   ,  Doping ratio

摘要： 对乙烯裂解燃料油进行了基本性质和四组分分析, 并采用n - d - M 法进行了结构组成分析, 结果表明, 乙烯裂解燃料油中芳烃、 胶质和沥青质含量较高。同时, 在焦化中试装置上, 考察了常压、 5 0 0℃条件下乙烯裂解燃 料油的焦化产物分布, 以及在混合进料中掺炼比对产物分布和性质的影响。结果表明, 随着乙烯裂解燃料油掺炼比 的增加, 液体产物中汽油和蜡油馏分收率减少, 而柴油馏分和焦炭收率增加。与工业生产装置相比, 在乙烯裂解燃 料油掺炼比为2 0%时, 所得汽油馏分密度变化不大, 硫含量和实际胶质含量略有增加; 中间馏分( 2 0 0~3 5 0℃) 的初 馏点与干点变化不大, 但密度有所增大, 实际胶质含量下降; 石油焦中的挥发分和灰分含量增加, 水分和硫含量明显 下降。说明掺炼2 0%乙烯裂解燃料油, 对焦化所得产物的性质影响不大。

关键词: 乙烯裂解燃料油, 组成,  , 焦化中试,  , 掺炼比