Developing Rubber Softener From Furfural Extraction Oil 

CHEN Zhi-gang, ZHAO De-zhi*, CAO Zu-bin， SONG Guan-long

School of Petrochemical Engineering，Liaoning University of Petroleum & Chemical Technology，Fushun Liaoning 113001

Received:2008-10-18 Published:2009-03-25 Online:2017-07-05

摘要/Abstract

摘要： 采用溶剂抽提糠醛抽出油中的重质芳烃,用以生产橡胶软化剂,提高了抽出油的利用价值。结果表
明,选用具有良好选择性的糠醛作为抽提剂,原料油在反应温度为60℃,m (溶剂)∶m (原料油)为2.0,抽提时间为3
min,精制时间30min的条件下,抽出油可制取高分子芳烃类橡胶软化剂,其抽余油可作为催化裂化装置的原料,该
工艺具有良好的应用前景。

关键词: 糠醛抽出油 , 橡胶软化剂 , 抽提

Abstract: A method of solvent extraction to separate heavy aromatics was adopted from furfural extraction oil, which is used to produce rubber softener. This provides a good technique for taking good advantage of the extraction oil. The results show that with the furfural as the extract reagent, under the condition of the extract temperature is 60 ℃， the mass ratio of solvent to oil is 2.0， extract time 3 min，the sedimentation time is 30 min. After furfural extraction, the rubber softener satisfies the standard of rubber softener. A good macromolecule aromatics rubber softener would be obtained, and the remained oil can be used as the raw material of FCC. So this technology has good application potentials.

Key words: Furfural extraction oil , Rubber Softener , Extraction 

陈志刚,赵德智,曹祖宾,宋官龙. 糠醛抽出油制备橡胶软化剂的研究[J]. 辽宁石油化工大学学报, 2009, 29(1): 28-30.

CHEN Zhi-gang, ZHAO De-zhi, CAO Zu-bin， SONG Guan-long. Developing Rubber Softener From Furfural Extraction Oil [J]. Journal of Liaoning Petrochemical University, 2009, 29(1): 28-30.

[1]	许耀辉，马国东，李　云，曹祖宾，李丹东. 哈萨克斯坦油砂溶剂抽提的实验研究[J]. 辽宁石油化工大学学报, 2012, 32(3): 6-8.
[2]	宋小梅,赵德智,马锐,丁薇,陈菲菲. 超声波辅助作用下糠醛强化萃取的研究[J]. 辽宁石油化工大学学报, 2009, 29(4): 15-18.
[3]	王秀芬, 赵德智. 超声功率及声强对直馏蜡油氧化脱硫的影响[J]. 辽宁石油化工大学学报, 2007, 27(1): 14-16.