硼改性T i O2 纳米管阵列负载 Mo - N i - P催化剂的制备及加氢脱硫性能

杨 雪王德慧宋官龙赵德智   

  1. ( 辽宁石油化工大学, 辽宁抚顺1 1 3 0 0 1)
  • 收稿日期:2014-03-28 修回日期:2014-06-10 出版日期:2014-10-25 发布日期:2014-12-19
  • 通讯作者: 王德慧( 1 9 8 1 - ) , 男, 博士, 讲师, 从事重油加工、 清洁燃料工艺研究; E - m a i l : d h u i w a n g@a l i y u n. c o m。
  • 作者简介:杨雪( 1 9 8 6 - ) , 女, 硕士研究生, 从事脱硫催化剂工艺研究; E - m a i l : 3 6 1 8 0 8 8 8 6@q q. c o m。
  • 基金资助:
    辽宁省科技厅博士科研启动基金计划( 2 0 1 3 1 0 6 3) ; 辽宁省教育厅科学研究一般项目( L 2 0 1 2 1 3 3) 。

Preparation and Hydrotreating Desulfurization Properties of  BoronModified TiO2 Nanotube Array MoNiP Catalyst

  1. (Liaoning Shihua University,Fushun Liaoning 113001,China)
  • Received:2014-03-28 Revised:2014-06-10 Published:2014-10-25 Online:2014-12-19

摘要: 采用阳极氧化法制备适宜孔容和大比表面积的 T i O2 纳米管阵列, 以其为载体将具有催化加氢活性的金属 Mo和 N i负载其表面。通过负载前硼改性、 磷修饰等手段制备了具有较大孔径( 7 2. 3n m) 和比表面积( 1 5 6 m2/ g) 的催化加氢精制催化剂, 并对其进行表征。催化加氢脱硫性能选用5mL固定床小试设备, 以孤岛焦化柴油作为原料进行加氢评价。结果表明, 压力7MP a, 温度3 6 0℃, 空速1. 5h-1, 氢油体积比为6 0 0∶1的条件下, 该柴油产品脱硫率为9 6. 6%, 基本达到工业化生产的要求。

关键词: T i O2 纳米管阵列,    ,  , 催化加氢,   ,  硼改性,   ,  , 脱硫

Abstract: The nanotube array with big specific surfacearea and aperture was prepared by the anodic oxidation. Bmodified MoNiP hydrotreating catalyst with pore diameter of 72.3 nm and specific surface area of 156 m2/g was prepared by the impregnation method,and characterized by mercury intrusion method and XRD. The activity of the novel catalyst was evaluated in a fixed bed reactor using diesel oil of Gudao island as the raw material. The results showed that the desulfurization rates of the products reached 96.6% under the optimum hydrogenation condition as follows: temperature 360 ℃,pressure 7 MPa,volume ratio of hydrogen to oil 600∶1 and space velocity 1.5 h-1.

Key words: TiO2 nanotube array,    ,  Hydrotreating catalyst,   ,  Boron modification,    ,  Desulfurization

引用本文

杨 雪, 王德慧, 宋官龙, 赵德智. 硼改性T i O2 纳米管阵列负载 Mo - N i - P催化剂的制备及加氢脱硫性能[J]. 石油化工高等学校学报, 2014, 27(5): 39-42.

Yang Xue, Wang Dehui, Song Guanlong, Zhao Dezhi. Preparation and Hydrotreating Desulfurization Properties of  BoronModified TiO2 Nanotube Array MoNiP Catalyst[J]. Journal of Petrochemical Universities, 2014, 27(5): 39-42.

使用本文