新型氮化碳材料的合成及其吸附性能的研究

邓政义,  赵 岷,  黄 醒   

  1. ( 渤海大学化学化工与食品安全学院,辽宁锦州1 2 1 0 0 0)
  • 收稿日期:2014-03-27 修回日期:2014-07-08 出版日期:2014-10-25 发布日期:2014-12-19
  • 通讯作者: 赵岷( 1 9 6 0 - ) , 女, 博士, 教授, 从事量子化学理论研究; E - m a i l : l n z h a o m i n@1 6 3. c o m。
  • 作者简介:邓政义( 1 9 8 3 - ) , 男, 硕士研究生, 从事吸附材料研究; E - m a i l : 1 4 9 8 1 1 9 0 9@q q. c o m。
  • 基金资助:
    辽宁省自然科学基金资助项目( 2 0 1 1 0 2 0 0 3) 。

Synthesis of New Carbon Nitride Materials and Their Absorption Properties

  1. (College of Chemistry, Chemical Engineering and Food Safety, Bohai University, Jinzhou Liaoning 121000, China)
  • Received:2014-03-27 Revised:2014-07-08 Published:2014-10-25 Online:2014-12-19

PDF

摘要： 以天然凹凸棒土为模板剂, 采用乙二胺 - 四氯化碳、 双氰胺、 尿素及三聚氰胺四类含氮有机化合物作为 前驱体, 合成了4种具有石墨型结构的氮化碳材料( CN - E DA - C T C、CN - D C D、CN - UR EA、CN - MEM) 。通过 X - 射 线粉末衍射、 热重、 N2 吸附及CO2 吸附等手段表征并测试了4种材料的结构及其吸附性能。结果表明, 前驱体的结 构和性质对合成的氮化碳材料的吸附性能有较大的影响, 其中, 对CO2 吸附能力最强的是CN - UR EA, 吸附量分别 为8 5. 4 3 8c m3/ g( 0℃) 和5 8. 9 3 1c m3/ g( 2 5℃) 。同时发现, 选择天然凹凸棒土作为模板剂, 并利用质量分数5% HF 在磁力搅拌下处理样品, 可以有效地提高孔容, 增强对CO2 的吸附能力。

关键词: 氮化碳材料,    ,  , 凹凸棒土,     ,  , N2 吸附,   ,  , CO2 吸附,    ,  模拟剂

Abstract: Four graphiticlike carbon nitride materials (CNEDACTC,CNDCD, CNUREA, CNMEM) have been synthesized with ethylenediaminecarbon tetrachloride, dicyandiamide, urea and melamine as precursors, using attapulgite (ATP) as hard template. The new materials were characterized by XRD and TG, besides which, the N2 and CO2 absorption properties were tested repectively. The results indicated that the structure and properties of the precursors played an important role in the adsorption capacity of carbon nitride materials. In the four materials, the CNUREA exhibited the highest capacity of CO2  with a capacity of 85.438 cm3/g at 0 ℃ and 58.931 cm3/g at 25 ℃. In addition, the results showed the attapulgite used as template in the new materials was removed thoroughly under magnetic stirring condition in 5% HF. The pore volumes and the CO2 absorption capacity of the samples were improved obviously.

Key words: Carbon nitride materials,    , Attapulgite,    ,  N2 absorption,    ,  CO2 absorption,   ,  Template

引用本文

邓政义, 赵 岷, 黄 醒. 新型氮化碳材料的合成及其吸附性能的研究[J]. 石油化工高等学校学报, 2014, 27(5): 33-38.

Deng Zhengyi, Zhao Min, Huang Xing. Synthesis of New Carbon Nitride Materials and Their Absorption Properties[J]. Journal of Petrochemical Universities, 2014, 27(5): 33-38.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal.lnpu.edu.cn/syhg/CN/10.3969/j.issn.1006-396X.2014.05.008

               http://journal.lnpu.edu.cn/syhg/CN/Y2014/V27/I5/33



网站版权 © 2021《石油化工高等学校学报》编辑部

本系统由北京玛格泰克科技发展有限公司设计开发