1 5 2型碱式硫酸镁晶须疏水改性研究

王 婷,  武玉民   

  1. ( 青岛科技大学化工学院, 山东青岛2 6 6 0 4 2)
  • 收稿日期:2014-03-06 修回日期:2014-04-28 出版日期:2014-06-25 发布日期:2014-06-16
  • 通讯作者: 武玉民( 1 9 6 4 - ) , 男, 博士, 教授, 从事高分子纤维及无机晶须材料合成和应用研究; E - m a i l : w u y u m i n 0 0 5@1 6 3.c o m。
  • 作者简介:王婷( 1 9 8 8 - ) , 女, 硕士研究生, 从事无机晶须材料研究; E - m a i l : W_ t i n g 1 2 3 4 5 6@1 6 3. c o m。
  • 基金资助:
    国家自然科学基金( 2 1 1 0 6 0 7 5) ; 山东省优秀中青年科学家研究奖励资金( B S 2 0 1 2 C L 0 1 6) 。

Hydrophobic Modification of 152 Magnesium Hydroxide Sulfate Hydrate Whiskers

  1. (College of Chemical Engineering, Qingdao University of Science and Technology, Qingdao Shandong 266042, China)
  • Received:2014-03-06 Revised:2014-04-28 Published:2014-06-25 Online:2014-06-16

PDF

摘要： 以乙醇为溶剂, 十七氟葵基三乙氧基硅烷 ( AC - F A S)为 改 性 剂, 对 1 5 2 型 碱 式 硫 酸 镁 晶 须 ( 1 5 2MHSH) 的疏水改性进行了研究。采用扫描电子显微镜( S EM) 、 X - R a y衍射仪( XR D) ,傅立叶变换红外光谱仪 ( F T - I R) 和水接触角测试仪( CAM) 等测试手段对改性前后样品的形貌、 结晶状况及产品组成等进行了表征。结果表 明, 通过疏水性处理, 改性剂被成功包覆在1 5 2碱式硫酸镁晶须表面, 实现了对其疏水改性的目的。当改性处理时间 为1h时获得了理想的疏水表面, 其水接触角达到1 2 6 ° 。F T - I R、 XR D、 S EM 及E D S分析均表明 AC - F A S仅成功包 覆在 MHSH晶须的表面, 并未对晶须的晶型造成影响。

关键词: 碱式硫酸镁,    ,  , 疏水改性,    ,  表征

Abstract: Hydrophobic modification of 152 magnesium hydroxide sulfate hydrate (MHSH) whisker was studied using ethyl alcohol as the solvent and heptadecafluoroalkylsilane（ACFAS） as modifier. The morphology, crystalline state and composition of products before and after hydrophobic modification were characterized by scanning electron microscopy (SEM), Xray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and contact angle measurements (CAM), respectively. The characterization results indicated that 152 MHSH was successfully coated by the modifierand the hydrophobic 152 MHSH whiskers were obtained. The ideal hydrophobic surface with water contact angle of 126° was achieved when the whisker was treated for 1 h. FTIR, XRD, SEM and EDS analysis showed that there were no change in the crystal form of whiskers, and ACFAS molecules were successfully coated on the surface of MHSH whiskers.

Key words: Magnesium hydroxide sulfate hydrate,    ,  Hydrophobic modification,    ,  Characterization

引用本文

王 婷, 武玉民. 1 5 2型碱式硫酸镁晶须疏水改性研究[J]. 石油化工高等学校学报, 2014, 27(3): 1-5.

Wang Ting, Wu Yumin. Hydrophobic Modification of 152 Magnesium Hydroxide Sulfate Hydrate Whiskers[J]. Journal of Petrochemical Universities, 2014, 27(3): 1-5.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal.lnpu.edu.cn/syhg/CN/10.3969/j.issn.1006-396X.2014.03.001

               http://journal.lnpu.edu.cn/syhg/CN/Y2014/V27/I3/1



网站版权 © 2021《石油化工高等学校学报》编辑部

本系统由北京玛格泰克科技发展有限公司设计开发