C 5 和C 9 石油树脂改性制备吸音矿棉板防水剂的研究

杨雅君1，李凤艳2，代党会1，袁亚东1   

  1. ( 1. 北京化工大学化学工程学院, 北京1 0 0 0 2 9; 2. 北京石油化工学院化学工程学院, 北京1 0 2 6 1 7)
  • 收稿日期:2013-12-09 修回日期:2014-03-02 出版日期:2014-04-25 发布日期:2014-06-16
  • 通讯作者: 李凤艳( 1 9 6 0 - ) , 女, 博士, 教授, 从事应用化学领域的研究; E - m a i l : l i f e n g y a n t d@1 2 6. c o m。
  • 作者简介:杨雅君( 1 9 8 9 - ) , 女, 硕士研究生, 从事矿棉板防水剂、 乳化石蜡、 乳化硅油产品研究; E - m a i l : y a n g y a j u n@b i p t . e d u. c n。

Preparation of the Waterproofing Agent for the Mineral Wool Board  from Modified C5 and C9 Petroleum Resin

  1. (1. Department of Chemical Engineering, Beijing University of Chemical Technology, Beijing 100029, China;  2. Department of Chemical Engineering, Beijing Institute of Petrochemical Technology, Beijing 102617, China)
  • Received:2013-12-09 Revised:2014-03-02 Published:2014-04-25 Online:2014-06-16

PDF

摘要： 研究了改性制备C 5、 C 9 混合石油树脂乳液的方法, 主要讨论了C 5、 C 9 混合的最佳质量配比, 改性剂马来酸酐及分散剂马来松香的用量, 改性时间和碱液用量对乳液性能的影响。实验结果表明, 最佳制备工艺条件为: C 5 石油树脂与C 9 石油树脂混合质量比为1∶3; 改性时间为3h; 改性温度为2 0 0℃; 马来酸酐质量分数为1. 5%; 马来松香质量分数为9%; 碱液为N a OH溶液, 质量分数为2%。混合石油树脂乳液与石蜡乳液混合质量比为1∶2, 制备出了吸音矿棉板防水剂。

关键词: C 5 石油树脂,    ,  C 9 石油树脂,    ,  改性剂,    ,  防水剂,    ,  , 马来酸酐,    ,  , 马来松香

Abstract: The mixed petroleum resin emulsion prepared from theC5 and C9 petroleum resin were modified with maleic anhydride. The effects of the mixing ratio between theC5 and C9 petroleum resin，amount of maleic rosin and maleic anhydride, modification time and the alkali liquor on properties of the emulsion were discussed. The results showed that the optimum process conditions were: C5 petroleum resin/C9 petroleum resin mixing ratio of 1∶3, maleic anhydride mass fraction of 1.5%, maleic rosin mass fraction of 9%, NaOH mass fraction of 2%, petroleum resin modification temperature of 200 ℃, petroleum resin modification time of 3 h, and modified petroleum resin emulsion/wax emulsion mixing ratio of 1∶2.

Key words: C5 petroleum resin,    ,  C9 petroleum resin,    ,  Modifier,    ,  Waterproofing agent,    ,  Maleic rosin,    ,  Maleic anhydride

引用本文

杨雅君, 李凤艳, 代党会, 袁亚东. C 5 和C 9 石油树脂改性制备吸音矿棉板防水剂的研究[J]. 石油化工高等学校学报, 2014, 27(2): 37-41.

Yang Yajun,Li Fengyan,Dai Danghui,Yuan Yadong. Preparation of the Waterproofing Agent for the Mineral Wool Board  from Modified C5 and C9 Petroleum Resin[J]. Journal of Petrochemical Universities, 2014, 27(2): 37-41.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal.lnpu.edu.cn/syhg/CN/10.3969/j.issn.1006-396X.2014.02.008

               http://journal.lnpu.edu.cn/syhg/CN/Y2014/V27/I2/37



网站版权 © 2021《石油化工高等学校学报》编辑部

本系统由北京玛格泰克科技发展有限公司设计开发