Preparation and Characterization of A Functional Polysulfone Anion Exchange Membrane of Polyethylene Glycol Modified Crown Ether

doi:10.12422/j.issn.1006-396X.2024.01.008

Abstract

Abstract:

In order to achieve high ionic conductivity and good alkaline resistance of Polysulfone?based AEMs, chloromethylated polysulfone was prepared by green method, and crown ether?functionalized polysulfone membranes with different triethylamine and amino crown ether contents were then prepared using amino crown ether as cross?linking agent and metal ions and triethylamine as cationic groups followed by crown ether functional polysulfone membrane with triethylamine and triethylamine as cationic groups(PSF?CE _X ?QA_1?_X ).The effect of the addition of polyethylene glycol on the membrane properties was explored by introducing the low molecular weight polyethylene glycol (PEG) into the above polysulfone cross?linking membrane.The results shown that the presence of hydrophilic polyethylene glycol helps to facilitate the formation of ordered ion channels in the membrane.The conductivity and alkali?resistant stability of PSF?CE _X ?QA_1?_X ?PEG were improved compared to PSF?CE _X ?QA_1?_X membrane.Among them, the electrical conductivity of PSF?CE_0.1?QA_0.9?PEG at 80 ℃ is 56.78 mS/cm,which can retain 85% of the original conductivity after alkaline resistance test.In addition,PSF?CE _X ?QA_1?_X ?PEG has good dimensional and thermal stability.

Key words: Anion exchange membrane, Polysulfone, Crown ether, Polyethylene glycol

摘要：

为了实现聚砜基阴离子交换膜（AEMs）高离子导电性和良好的耐碱性，采用绿色环保的方法制备了氯甲基化聚砜，并以氨基冠醚为交联剂，以氨基冠醚络合的金属离子和三乙胺为阳离子基团，制备了三乙胺和氨基冠醚质量分数不同的冠醚功能化聚砜膜（PSF?CE _X ?QA_1-_X ）。通过将低分子质量的聚乙二醇（PEG）引入PSF?CE _X ?QA_1-_X ）中，探究了PEG对膜性能的影响。结果表明，亲水PEG的存在有助于膜中离子通道的形成；与PSF?CE _X ?QA_1-_X 相比，PSF?CE _X ?QA_1-_X ?PEG的电导率和耐碱稳定性均得到了提高；在温度为80 ℃时，PSF?CE_0.1?QA_0.9?PEG的电导率为56.78 mS/cm，耐碱性测试后其电导率可维持初始电导率的85%。此外，PSF?CE _X ?QA_1-_X ?PEG还具有良好的尺寸稳定性和热稳定性。

关键词: 阴离子交换膜, 聚砜, 冠醚, 聚乙二醇

CLC Number:

TQ425.236

Yaning XU, Jianing YAN, Lulu WANG, Jilin WANG. Preparation and Characterization of A Functional Polysulfone Anion Exchange Membrane of Polyethylene Glycol Modified Crown Ether[J]. Journal of Petrochemical Universities, 2024, 37(1): 59-65.

徐亚宁, 闫佳宁, 王璐璐, 王吉林. 聚乙二醇改性冠醚功能化聚砜阴离子交换膜的制备及表征[J]. 石油化工高等学校学报, 2024, 37(1): 59-65.

Figures/Tables 8

Fig.1 Preparation and structure of the PSF?CE X%?QA1-X%

Fig.2 Structure of the PSF?CE X ?QA1-X ?PEG

Fig.3 FT-IR spectra of CMPSF,PSF?CE X ?QA1-X and PSF?CE X ?QA1-X ?PEG

Fig.4 SEM images of the surface and cross sections of PSF?CE X ?QA1-X and PSF?CE X ?QA1-X ?PEG

Table 1 The physico?chemical properties of PSF?CE X ?QA1-X and PSF?CE X ?QA1-X ?PEG

膜	离子交换量/（mmol∙g^-1）	含水率/%		溶胀率/%		T_s/MPa	E_b/%
膜	离子交换量/（mmol∙g^-1）	30 ^oC	60 ^oC	30 ^oC	60 ^oC	T_s/MPa	E_b/%
PSF⁃CE_0.05⁃QA_0.95	1.43	15.8	32.1	7.8	14.2	14.9	2.2
PSF⁃CE_0.1⁃QA_0.9	1.34	14.6	25.2	7.3	13.2	15.3	2.0
PSF⁃CE_0.15⁃QA_0.85	1.29	12.5	23.6	6.9	10.8	17.7	1.8
PSF⁃CE_0.2⁃QA_0.8	1.23	10.4	21.5	5.5	9.5	19.7	1.5
PSF⁃CE_0.05⁃QA_0.95⁃PEG	1.42	16.4	34.1	8.1	16.9	16.3	4.1
PSF⁃CE_0.1⁃QA_0.9⁃PEG	1.35	15.1	28.1	7.8	14.2	17.3	3.9
PSF⁃CE_0.15⁃QA_0.85⁃PEG	1.29	13.8	26.2	7.2	12.5	20.3	3.2
PSF⁃CE_0.2⁃QA_0.8⁃PEG	1.22	12.9	23.9	6.9	10.3	21.1	2.6

Fig.5 The TGA curves of the membrane

Fig.6 Conductivity with temperature curve and Arrhenius plot of PSF?CE X ?QA1-X and PSF?CE X ?QA1-X ?PEG

Fig.7 Changes of conductivity of PSF?CE X ?QA1-X and PSF?CE X ?QA1-X ?PEG with soaking time at 2.0 mol/L KOH

References 19

1	HREN M，BOŽIČ M，FAKIN D，et al.Alkaline membrane fuel cells：Anion exchange membranes and fuels［J］.Sustainable Energy & Fuels，2020，5（3）：604⁃637.
2	STEELE B C，HEINZEL A.Materials for fuel⁃cell technologies［J］.Nature，2001，414（6861）：345⁃352.
3	LUO W J，WANG L L，FENG R J，et al.Preparation of composite anion exchange membranes based on in⁃situ copolymerization of N⁃vinyl formamide and divinylbenzene in porous PTFE［J］.Journal of Applied Polymer Science，2021，138（8）：49872.
4	刘盈汐，王吉林，王璐璐，等.基于植酸框架构筑燃料电池用阴离子导电膜［J］.石油化工高等学校学报，2023，36（1）：74⁃80.
	LIU Y X，WANG J L，WANG L L，et al.Phytic acid framework⁃based alkaline anion exchange membrane construction for fuel cells［J］.Journal of Petrochemical Universities，2023，36（1）：74⁃80.
5	HAGESTEIJN K F L，JIANG S X，LADEWIG B P.A review of the synthesis and characterization of anion exchange membranes［J］.Journal of Materials Science，2018，53（16）：11131⁃11150.
6	HAN J J，LIN B C，PENG H Q，et al.Aggregated and ionic cross⁃linked anion exchange membrane with enhanced hydroxide conductivity and stability［J］.Journal of Power Sources，2020，459：227838.
7	CHA M S，JEONG H Y，SHIN H Y，et al.Crosslinked anion exchange membranes with primary diamine⁃based crosslinkers for vanadium redox flow battery application［J］.Journal of Power Sources，2017，363：78⁃86.
8	ZHENG X Y，SONG S Y，YANG J R，et al.4⁃formyl dibenzo⁃18⁃crown⁃6 grafted polyvinyl alcohol as anion exchange membranes for fuel cell［J］.European Polymer Journal，2019，112：581⁃590.
9	YANG Q，LI L，GAO X L，et al.Crown ether bridged anion exchange membranes with robust alkaline durability［J］.Journal of Membrane Science，2019，578：230⁃238.
10	SHANG C S，LIU Y X，ZENG X R，et al.Preparation and characterization of organic⁃inorganic hybrid anion exchange membrane based on crown ether functionalized mesoporous SBA⁃NH₂［J］.International Journal of Hydrogen Energy，2022，47（30）：14141⁃14157.
11	WAN R Y，XU S C，WANG J，et al.Construction of ion conducting channels by embedding hydrophilic oligomers in piperidine functionalized poly （2，6⁃dimethyl⁃1，4⁃phenylene oxide） membranes［J］.European Polymer Journal，2021，142：110150.
12	ZHANG J J，HE Y B，ZHANG K Y，et al.Cation⁃dipole interaction that creates ordered ion channels in an anion exchange membrane for fast OH^- conduction［J］.AIChE Journal，2021，67（4）：e17133.
13	LI Y Y，LI M S，ZHOU S Y，et al.Enhancement of hydroxide conductivity by incorporating nanofiber⁃like palygorskite into quaternized polysulfone as anion exchange membranes［J］.Applied Clay Science，2020，195：105702.
14	SHANG C S，WANG Z，WANG L L，et al.Preparation and characterization of a polyvinyl alcohol grafted bis⁃crown ether anion exchange membrane with high conductivity and strong alkali stability［J］.International Journal of Hydrogen Energy，2020，45（33）：16738⁃16750.
15	马钰，王璐璐，王吉林.基于金属有机框架构筑的阴离子交换膜溶胀性能研究［J］.石油化工高等学校学报，2021，34（3）：24⁃30.
	MA Y，WANG L L，WANG J L.Research on swelling performance of anion exchange membranes based on metal organic framework［J］.Journal of Petrochemical Universities，2021，34（3）：24⁃30.
16	PÉREZ‐PRIOR M T，VÁREZ A，LEVENFELD B.Synthesis and characterization of benzimidazolium⁃functionalized polysulfones as anion⁃exchange membranes［J］.Journal of Polymer Science Part A Polymer Chemistry，2015，53（20）：2363⁃2373.
17	HUANG X Y，WANG J L，WANG L L.Esterification modification and characterization of polyvinyl alcohol anion exchange membrane for direct methanol fuel cell［J］.Journal of Polymer Research，2022，29（3）：99.
18	YANG K，NI H Z，DU X M，et al.Improvement the hydroxide conductivity and alkaline stability simultaneously of anion exchange membranes by changing quaternary ammonium and imidazole contents［J］.International Journal of Energy Research，2021，45（9）：13668⁃13680.
19	余嘉俊，赵爽，冯霄.膜分离技术在盐湖提锂应用中的研究进展［J］.辽宁石油化工大学学报，2023，43（4）：30⁃35.
	YU J J，ZHAO S，FENG X.Research progress of membrane separation technology in salt lake lithium extraction［J］.Journal of Liaoning Petrochemical University，2023，43（4）：30⁃35.

[1]	Haige NIAN, Xuying ZHENG, Hui GAO, Hai XIN, Jilin WANG. Preparation of Anionic Conductive Membrane for Fuel Cells Based on Crown Ether Modified Deacetylated Chitin [J]. Journal of Petrochemical Universities, 2024, 37(2): 66-72.
[2]	Yingxi Liu, Jilin Wang, Lulu Wang, Zhiqiang Qu. Phytic Acid Framework⁃Based Alkaline Anion Exchange Membrane Construction for Fuel Cells [J]. Journal of Petrochemical Universities, 2023, 36(1): 74-80.
[3]	Wang Xiaohong, Guo Fangrong, Gao Chuanhui, et al. Modification of Poly(Butylene TerephthalatecoButylene Itaconate) Copolyesters [J]. Journal of Petrochemical Universities, 2015, 28(1): 12-15.
[4]	ZHU Wei, YANG Jun, CHEN Wei. Synthesis and Characterization of Methylacrylic Acid Polyethylene Glyco1 Ester [J]. Journal of Petrochemical Universities, 2008, 21(3): 21-23.