汽轮机叶片阻尼涂层减振研究

doi:10.3969/j.issn.1672-6952.2020.03.011

辽宁石油化工大学学报 ›› 2020, Vol. 40 ›› Issue (3): 57-62.DOI: 10.3969/j.issn.1672-6952.2020.03.011

汽轮机叶片阻尼涂层减振研究

张修铭¹，陈盛军²，邓子龙¹，姜文全¹，杨帆¹，杜广煜³

1.辽宁石油化工大学机械工程学院，辽宁抚顺 113001； 2.中国石油抚顺石化设备技术开发有限公司； 3.东北大学机械工程及自动化学院，辽宁沈阳 110819

收稿日期:2020-01-20 修回日期:2020-03-04 出版日期:2020-06-29 发布日期:2020-07-06
通讯作者: 邓子龙（1967⁃），男，硕士，教授，从事机电液一体化、机械现代设计与理论方面的研究；E⁃mail：dzl56801@sina.com。
作者简介:张修铭（1994?），男，硕士研究生，从事表面工程技术方面的研究；E?mail：531746247@qq.com。
基金资助:
国家自然科学基金项目（51005043）；辽宁省自然科学基金项目（20170540587）。

Research on Damping Coating of Steam Turbine Blade Damping Coating

Zhang Xiuming¹， Chen Shengjun² Deng Zilong¹， Jiang Wenquan¹， Yang Fan¹， Du Guangyu³

1.School of Mechanical Engineering，Liaoning Shihua University，Fushun Liaoning 113001，China； 2.Fushun Petrochemical Company Equipment Technology Development Co., Ltd，China Petroleum，Fushun Liaoning 113008，China； 3.School of Mechanical Engineering and Automation，Northeastern University，Shenyang Liaoning 110819，China

Received:2020-01-20 Revised:2020-03-04 Published:2020-06-29 Online:2020-07-06

摘要/Abstract

摘要： 研究了汽轮机叶片镀金属薄膜后叶片的阻尼减振性能，将汽轮机叶轮合理简化后通过ug软件建模，运用ANSYS软件，对相同厚度的铝、钛、铝钛薄膜叶片试件及不镀膜的叶片试件等4种模型的整体叶盘进行模态分析，得到振型图和固有振动频率，从整体上观察叶轮的易损部位；对单个叶片进行谐响应分析，进一步分析4种叶片在外加同一载荷情况下的形变量，讨论其阻尼减振效果。结合实验结果，利用动态机械热分析仪（DMA），对镀铝、镀钛、先镀铝后镀钛处理的试件及不镀膜试件进行分析，检测涂层的阻尼性能。结果表明，镀膜后的叶片各阶模态的形变量均小于未镀膜叶片，对叶片镀膜具有一定的减震阻尼效果。

关键词: 金属薄膜, 　阻尼, 　模态, 　镀膜

Abstract: 　The damping vibration performance of the blade after metallization of steam turbine blades is studied. The turbine impeller was simplified and then modeled by ug software, and the modal analysis is carried out on the integral blade disk of the same thickness of the aluminum, titanium, aluminum titanium film blade and the uncoated blade by ANSYS software. The vibration pattern and natural vibration frequency are obtained, and the vulnerable parts of the impeller are observed as a whole；Harmonic response analysis of a single blade,The deformation of the four blades under the same load was further analyzed, and their damping effects were discussed.Combined with the experimental results, the test specimens were subjected to aluminum plating, titanium plating, aluminum plating first and then titanium plating treatment, and uncoated specimens formed a control group.Testing the damping performance of coatings with a Dynamic Mechanical Thermal Analyzer (DMA).The results show that the deformation of each step mode of the blade after coating is smaller than that of the blade without coating，it can play a certain damping effect on the blade coating.

Key words: Metal film, Damping, Modal, Coating

张修铭, 陈盛军, 邓子龙, 姜文全, 杨帆, 杜广煜. 汽轮机叶片阻尼涂层减振研究[J]. 辽宁石油化工大学学报, 2020, 40(3): 57-62.

Zhang Xiuming, Chen Shengjun, Deng Zilong, Jiang Wenquan, Yang Fan, Du Guangyu. Research on Damping Coating of Steam Turbine Blade Damping Coating[J]. Journal of Liaoning Petrochemical University, 2020, 40(3): 57-62.

[1]	林学洋，高兴军，王月，邓子龙. 双悬臂式压电振动给料器设计与性能分析[J]. 辽宁石油化工大学学报, 2021, 41(3): 77-81.
[2]	王国良，孙媛媛. 控制器模态不匹配的半马尔可夫系统的可达集分析[J]. 辽宁石油化工大学学报, 2021, 41(3): 82-90.
[3]	徐晶晶，石成江，高鹏. 基于ANSYS的井下齿轮传动系统振动分析[J]. 辽宁石油化工大学学报, 2019, 39(1): 61-64.
[4]	王强,高思,王庆国,杨春明,尹权,郭志英. 方形塔的有限元分析[J]. 辽宁石油化工大学学报, 2016, 36(1): 46-51.
[5]	钮科,邓子龙,王月,许龙. 小型液压挖掘机动臂的性能分析[J]. 辽宁石油化工大学学报, 2013, 33(3): 64-66.
[6]	黄磊,张巨伟,李英魁. 基于ANSYS的ZDY2000L型煤矿钻机给进模块的有限元分析[J]. 辽宁石油化工大学学报, 2013, 33(1): 78-81.
[7]	赵　斌. PACKER 内拉杆的有限元模态分析[J]. 辽宁石油化工大学学报, 2007, 27(1): 50-52.

汽轮机叶片阻尼涂层减振研究

Research on Damping Coating of Steam Turbine Blade Damping Coating