辽宁石油化工大学学报

辽宁石油化工大学学报 ›› 2011, Vol. 31 ›› Issue (4): 18-20.

• 石油化工 • 上一篇    下一篇

俄罗斯M100减压渣油生产高等级沥青的研究[

崔 蕊王丽曼赵德智*, 石薇薇李丹东丁 薇   

  1. 辽宁石油化工大学石油化工学院,辽宁抚顺 113001
  • 收稿日期:2011-06-06 出版日期:2011-12-25 发布日期:2017-07-14

Feasibility Study of Bitumen Production From Vacuum Residue of Russian M100

CUI Rui, WANG Li-man, ZHAO De-zhi*, SHI Wei-wei, LI dan-dong, DING Wei   

  1. School of Petrochemical Engineering,Liaoning Shihua Liaoning University, Fushun Liaoning 113001, P.R.China
  • Received:2011-06-06 Published:2011-12-25 Online:2017-07-14

摘要: 对俄罗斯燃料油M100的减压渣油进行研究,利用自制的氧化装置, 控制氧化温度分别为225和250 ℃,通风量为0.2 m3/(h•kg),氧化时间为 10 h。实验结果表明:氧化后样品的沥青3个主要性质数值符合道路沥青技术要求(JTG F40-2004)中130#C等级沥青的标准和110#C等级沥青的标准。添加改性剂SBS质量分数为1%~5%,并加入MAW-1型稳定剂,w(稳定剂)∶w(SBS)为1∶(10~15)。改性后的两种沥青均符合聚合物改性沥青的技术要求(JTG F40-2004)中SBS类I-A的标准。

关键词: 减压渣油, 氧化沥青, 改性沥青, SBS

Abstract: The oxidation of vacuum residue of Russian fuel oil M100 was studied with self-made device for 10 h under the oxidation temperatures 225 and 250 ℃ with the ventilation capacity of 0.2 m3/(h•kg). The results show that three asphalt of oxidized samples can meet well with technical requirements of road asphalt (JTG F40-2004) for 130#C, the standard grade of asphalt and bitumen and 110#C grade standards. A modifier SBS was added with the weight ratio of 1% to 5%, and the MAW-1-type stabilizer was also added with the mass ratio of stabilizers to SBS 1∶(10~15). Two polymer modified bitumen were in line with the standard of the SBS class I-A in the technical requirements (JTG F40-2004).

Key words: Vacuum residue, Oxidized pitch,  Modified bitumen, SBS

引用本文

崔 蕊,王丽曼, 赵德智, 石薇薇, 李丹东, 丁 薇. 俄罗斯M100减压渣油生产高等级沥青的研究[[J]. 辽宁石油化工大学学报, 2011, 31(4): 18-20.

CUI Rui, WANG Li-man, ZHAO De-zhi, SHI Wei-wei, LI dan-dong, DING Wei. Feasibility Study of Bitumen Production From Vacuum Residue of Russian M100[J]. Journal of Liaoning Petrochemical University, 2011, 31(4): 18-20.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://journal.lnpu.edu.cn/CN/

               https://journal.lnpu.edu.cn/CN/Y2011/V31/I4/18