PAM-SA新型水系灭火剂的制备及性能研究

辽宁石油化工大学学报 ›› 2009, Vol. 29 ›› Issue (1): 15-17.

PAM-SA新型水系灭火剂的制备及性能研究

张丹,罗根祥

(辽宁石油化工大学化学与材料科学学院,辽宁抚顺113001

收稿日期:2008-10-28 出版日期:2009-03-25 发布日期:2017-07-05
作者简介:张丹(1980- ),女,辽宁抚顺市,硕士

Preparation and Performance Evaluation on PAM-SA New Water-Series Extinguisher 

ZHANG Dan, LUO Gen-xiang

School of Chemistry and Materials Science，Liaoning University of Petroleum & Chemical Technology，Fushun Liaoning 113001， P．R．China

Received:2008-10-28 Published:2009-03-25 Online:2017-07-05

摘要/Abstract

摘要： 以聚丙烯酰胺(PAM)和高分子吸水树脂(SA)为原料,采用混配法制备了PAM-SA 新型水系灭火
剂,并考察了此种实验样品的保水率、吸水倍率、运动粘度、pH 值等的适用范围。实验结果表明,m (PAM)∶m
(SA)为1∶1时,此种实验样品的保水率为100%,吸水倍率为135,运动粘度为2103.6mm2/s,pH 值为5.0~9.0
时,制备的灭火剂实验样品效果最佳。

关键词: 灭火剂 , 运动粘度 , 高分子吸水树脂

Abstract: The PAM-SA new water-series extinguisher was prepared by mixed method with polyacrylamide（PAM） and super absorbent materia（SA）as raw materials. The scope of application of test sample including water-retention ratio, water absorption, viscosity and pH was studied. The results show that when PAM/SA mass ratio is 1∶1, water-retention ratio is 100%，water absorption is 135，viscosity is 2 103.6 mm2/s and pH value is 5.0~9.0，the extinguisher prepared has best Fire-extinguishing capability. 

Key words: Fire-extinguishing chemicals , Viscosity , Water absorbent materia

张丹,罗根祥. PAM-SA新型水系灭火剂的制备及性能研究[J]. 辽宁石油化工大学学报, 2009, 29(1): 15-17.

ZHANG Dan, LUO Gen-xiang. Preparation and Performance Evaluation on PAM-SA New Water-Series Extinguisher [J]. Journal of Liaoning Petrochemical University, 2009, 29(1): 15-17.