油田作业刹车轮毂的失效分析

辽宁石油化工大学学报 ›› 2007, Vol. 27 ›› Issue (1): 57-59.

油田作业刹车轮毂的失效分析

韦丽娃¹, 田　娜², 郭淑娟²

1. 辽宁石油化工大学顺华学院, 辽宁抚顺113001 ;
2. 辽宁石油化工大学储运与建筑学院, 辽宁抚顺113001

收稿日期:2006-10-18 出版日期:2007-03-20 发布日期:2017-07-05
作者简介:韦丽娃(1962 - ), 女(壮), 广西柳州市, 实验师。

Failure Analysis of the Brake Hub of an Oil Field Working Machine

1. Sunhua College , Liaoning University of Petroleum & Chemical Technology , Fushun Liaoning 113001 , P. R. China;
2. School of Storage - Transport and Architecture Eng ineering , Liaoning Universisty of Petroleum &Chemical Technology , Fushun Liaoning 113001, P. R . China

Received:2006-10-18 Published:2007-03-20 Online:2017-07-05

摘要/Abstract

摘要： 　对辽河油田失效刹车轮毂进行了裂纹形貌、化学成分、机械性能及显微组织的检验、分析及讨论。结果表明, 刹车轮毂的失效主要是由于热处理工艺不当造成的。一方面, 热处理工艺不当无法彻底消除铸态组织的不利影响, 结果使得铸件的塑、韧性指标大幅度降低;另一方面, 热处理工艺不当使得铸造应力及机加工的残余应力无法彻底消除, 这样加剧了裂纹的产生和扩展。建议在最终热处理前增加一道退火工序, 通过细化晶粒, 来消除网状铁素体和不均匀组织, 进一步提高材料的力学性能。

关键词: 作业机刹车轮毂, 　断裂, 　失效分析

Abstract:

　Aiming to the failure phenome a of brake hub of Liaohe oil field, crack figures , chemistry composition , mechanical property , and me tallo graphic structures were tested , analyzed and discussed. The results show that the failure of the brake hub is caused by the improper heat treatment operation. On the one hand, the improper heat treatment operation can not tho roughly remove the bad effects of cast structures and leads to tremendous reduction of the plasticity and toughness index. On the other hand , the improper heat treatment operation can not completely relieve the casting stress and remnant stress, and further enhances generation and expansion of cracks. A working procedure before the last heat treatment operation was suggested to be added. Through refining crystal grain , the reticularferrite and heterogeneous structures are relieved, and further mechanical property of materials can be improved.

Key words: 　Brake hub of a working machine , , Rapture , , Failure analysis

韦丽娃,田　娜,郭淑娟. 油田作业刹车轮毂的失效分析[J]. 辽宁石油化工大学学报, 2007, 27(1): 57-59.

WEI Li - w a, TIA N Na, G UO Shu - juan. Failure Analysis of the Brake Hub of an Oil Field Working Machine[J]. Journal of Liaoning Petrochemical University, 2007, 27(1): 57-59.

[1]	梁　艳，马　超，姜文全. 转化炉管失效分析[J]. 辽宁石油化工大学学报, 2012, 32(4): 60-63.
[2]	王伟,谢禹钧. Ⅰ型类中央双裂纹椭圆形截面管环向裂纹应力强度因子[J]. 辽宁石油化工大学学报, 2010, 30(3): 55-57.
[3]	孙春一,石彬. 考虑裂纹时谐波齿轮传动刚度系数的计算[J]. 辽宁石油化工大学学报, 2009, 29(4): 64-66.
[4]	王　伟, 谢禹钧. 管线断裂失效概率模型及计算[J]. 辽宁石油化工大学学报, 2006, 26(1): 74-75.