高温合金锯齿形切屑绝热剪切带内材料#br# 组织演变及形成机理

邓鹏飞1,赵 杰1,齐 民2   

  1.   
    ( 1. 辽宁石油化工大学, 辽宁抚顺1 1 3 0 0 1; 2. 辽宁工程技术大学, 辽宁阜新1 2 3 0 0 0)
  • 收稿日期:2014-04-20 出版日期:2014-12-25 发布日期:2017-07-14
  • 通讯作者: 赵杰( 1 9 5 7 - ) , 男, 教授, 从事机械CAD / CAM 等方面的研究; E - m a i l : 7 8 0 6 7 2 1 3@q q. c o m。
  • 作者简介:邓鹏飞( 1 9 8 8 - ) , 男, 硕士研究生, 从事机械制造及自动化方面的研究; E - m a i l : 1 9 5 3 2 1 1 9 1@q q. c o m。
  • 基金资助:
    国家自然科学基金项目( 5 1 0 7 5 1 2 8) 。

Processing of SuperAlloy Serrated Chip Organization Evolution  and Formation Mechanism of Adiabatic Shear Band Material

Deng Pengfei1， Zhao Jie1， Qi Min2   

  1. （1.Liaoning Shihua University，Fushun Liaoning 113001，China； 2.Liaoning University of Engineering and Technology，Fuxin Liaoning 123000，China）
  • Received:2014-04-20 Published:2014-12-25 Online:2017-07-14

PDF

摘要： 摘 要:  为了研究不同铣削条件下切屑的宏观形态, 设计了高速铣削单因素试验。通过单因素试验考察了各
个铣削参数对铣削力的影响, 并对改变铣削速度后得到的切屑的宏观形态进行了分析。对铣削加工中得到的切屑
进行镶嵌、 抛光、 腐蚀, 得到其金相显微组织照片, 使用D i g i m i z e r测量软件对切屑形态各参数进行测量, 研究了铣削
速度对锯齿化程度和锯齿齿距的影响。通过得到的金相组织照片, 对不同铣削参数下的切屑基体和绝热剪切带内
材料的组织变化进行分析, 得出了锯齿形切屑的形成机理。

关键词: 高温合金, 高速加工, 切屑形态, 切屑形成机理, 铣削

Abstract: In order to study the macromorphology of the chip under different milling conditions, high speed milling of single factor experiment was designed. The milling parameters were obtained by single factor experiment on the influence of milling force, and the chip macro morphology from the change of milling speed was analyzed. Milling for chip after milling was inlayed, polished and corroded and obtained the metallographic microstructure pictures, and the chip morphology parameters were measured by using Digimizer software. The influence of milling speed was researched on the sawtooth degree and the sawtooth pitch. Through the microstructure pictures ,the chip substrate and the organization change of adiabatic shear band material under different milling parameters were analyzed, and obtained the formation mechanism of serrated chip.

Key words: Superalloy, High speed machining, Chip morphology, Mechanism of chip formation, Milling

引用本文

邓鹏飞,赵 杰,齐 民. 高温合金锯齿形切屑绝热剪切带内材料#br# 组织演变及形成机理[J]. 辽宁石油化工大学学报, 2014, 34(6): 52-56.

Deng Pengfei， Zhao Jie， Qi Min. Processing of SuperAlloy Serrated Chip Organization Evolution  and Formation Mechanism of Adiabatic Shear Band Material[J]. Journal of Liaoning Petrochemical University, 2014, 34(6): 52-56.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://journal.lnpu.edu.cn/CN/10.3696/j.issn.1672-6952.2014.06.011

               https://journal.lnpu.edu.cn/CN/Y2014/V34/I6/52



网站版权 © 2021《辽宁石油化工大学学报》编辑部

地址：辽宁省抚顺市望花区丹东路西段1号 电话：024-56865105 E-mail:lnxuebao@126.com 邮编：113001

本系统由北京玛格泰克科技发展有限公司设计开发