Synthesis of Acetal With Solid Super Acid Catalyst S2O2-8/ZrO2

  1. 1.School of Chemistry and Chemical Engineering, Shanxi Datong University, Datong Shanxi 037009,P.R. China;
    2.Key Laboratory of Coal Science and Technology of Ministry of Education and Shanxi Province, Taiyuan University of Technology, Taiyuan Shanxi030024,P.R.China
  • Received:2008-08-30 Revised:2009-03-12 Published:2009-09-25 Online:2009-09-25

PDF

摘要： 通过沉淀、老化、过滤、洗涤、干燥、浸渍和焙烧等过程，由 ZrOCl2 和(NH4)2S2O8制备了S2O2-8 /ZrO2催化剂。用XRD，FT-IR，NH3-TPD对其进行了表征，研究了焙烧温度对其酸性、结构和催化性能的影响。XRD 结果表明具有较高T型晶相峰。FT-IR分析表明S2O2-8 /ZrO2 表面以双桥鳌合状配位化合物形式结合。研究了醛醇物质的量比、催化剂用量、反应时间等因素对产品收率的影响。结果表明，在 n(丁醛) / n(乙二醇) =1:1 .4，催化剂质量分数为0 .25%,反应时间为 50 min的最佳条件下，丁醛乙二醇缩醛的收率可达95.8%；在n(苯甲醛)/ n(乙二醇)=1∶1 .25，催化剂质量分数为0 .5%，反应时间为50 min的最佳条件下，苯甲醛乙二醇缩醛的收率可达 88 .8%。

关键词: 丁醛乙二醇缩醛 , 苯甲醛乙二醇缩醛 , 固体超强酸 , 催化 , 缩醛反应

Abstract:

The S2O2-8/ZrO2  solid acid catalyst was prepared from ZrOCl2 and (NH4)2S2O8 by precipitation, aging, filtering, washing, drying, impregnation and calcination processes. The characterization of the catalyst was performed using XRD, FT-IR and NH3-TPD. The effect of calcination temperature on the acidic property, textural property and catalytic perfomance of S2O2-8/ZrO2 solid acid catalysts was studied. XRD patterns show that the catalyst present is higher tetragonal phase. FT-IR spectra shows that S2O2-8 is strongly bind with the ZrO2 surface bidentately. With S2O2-8/ZrO2 as catalyst,the effects of molar ratio of glycol to aldehyde, quantity of catalyst, reaction time on the yield of acetalation was more systematically studied and the best reaction conditions were confirmed.  The results show that the molar ratio of butyraldehyde to glycol is 1∶1.4, the quantity of catalyst is equal to 0.25% of feed stocks, the reaction time is 50 min, and the yield of butyraldehyde glycol acetal can reach 75.8%; the yield of benzaldehyde glycol acetal is 68.8% under the following conditions：molar ratio of benzaldehyde to glycol 1∶1.25, the quantity of catalyst 0.5% of feed stocks, the reaction time 50 min.

Key words: Butyraldehyde glycol acetal , Benzaldehyde glycol acetal , Solid superacid , Catalysis , Acetalization

引用本文

王俊丽,孟双明,李 忠. 固体超强酸S2O2-8/ZrO2催化合成缩醛[J]. 石油化工高等学校学报, 2009, 22(3): 5-8.

WANG Jun-li,MENG Shuang-ming,LI Zhong,et al. Synthesis of Acetal With Solid Super Acid Catalyst S2O2-8/ZrO2[J]. Journal of Petrochemical Universities, 2009, 22(3): 5-8.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal.lnpu.edu.cn/syhg/CN/10.3696/j.issn.1006-396X.2009.03.002

               http://journal.lnpu.edu.cn/syhg/CN/Y2009/V22/I3/5



网站版权 © 2021《石油化工高等学校学报》编辑部

本系统由北京玛格泰克科技发展有限公司设计开发