辽宁石油化工大学学报

辽宁石油化工大学学报 ›› 2014, Vol. 34 ›› Issue (2): 57-60.DOI: 10.3696/j.issn.1672-6952.2014.02.015

• 化工机械与计算机 • 上一篇    下一篇

省煤器联箱接管座与管排焊接接头泄漏原因分析

季 明1,敖 峰2,胡传顺3,田景涛1   

  1. 1.中国石油抚顺石化公司大项目指挥部质量监督管理部,辽宁抚顺113006;
    2.扬州秋源压力容器制造有限公司,江苏扬州225115;3.辽宁石油化工大学,辽宁抚顺113001
  • 收稿日期:2013-09-02 修回日期:2014-01-10 出版日期:2014-04-25 发布日期:2017-07-14
  • 通讯作者: 胡传顺(1962-),男,博士,教授,从事石油化工装备材料加工与应用技术研究;E-mail:cshu0612@126.com。
  • 作者简介:季明(1963-),男,硕士,高级工程师,从事工程质量管理等方面的研究;E-mail:fsshjm@sohu.com。
  • 基金资助:
    辽宁省教育厅科学技术研究项目(LS2010098)。

Analysis of Leakage Reasons for Joint of Tube of Header and  Weld Joints of Coil Tube on Coal Economizer

Ji Ming1， Ao Feng2， Hu Chuanshun3， Tian Jingtao1   

  1. （1.Fushun Petrochemical Company Project Engineering and Construction Headquarters Quality Assurance Department，Fushun Liaoning 113006，China； 2.Yangzhou Qiuyuan Pressure Vessel Manufacturing Co., Ltd，Yangzhou Jiangsu 225115，China； 3. Liaoning Shihua University，Fushun Liaoning 113001，China）
  • Received:2013-09-02 Revised:2014-01-10 Published:2014-04-25 Online:2017-07-14

PDF

摘要： 通过宏观分析、化学组成分析、金相分析、扫描电镜分析等方法,对省煤器联箱接管座与管排焊接接
头泄漏原因进行了分析。结果表明,焊接管化学成分、换算强度均符合GB5310—2008标准要求。熔合区、过热区晶
粒组织粗大,甚至形成魏氏组织,使这一区域性能弱化。省煤器联箱接管座与管排焊接接头穿孔是因应力作用下在
熔合区、过热区薄弱处首先产生微裂纹,启裂后虽未形成贯穿裂纹,但微裂纹导致缝隙腐蚀,缝隙腐蚀加速裂纹由内
向外深化和扩展直至穿孔,产生泄漏。

关键词: 省煤器 , 联箱 ,  焊接接头 , 泄漏 , 分析

Abstract: Through macroanalysis, chemical composition analysis, metallographic observation, and SEM, the leakage reasons for joint of tube of header and coil tube of coal economizer was analyzed. The results show that the alloy element compositions of welded tubes and conversion strength both met the standard of GB 5310—2008. The grains at fusion zone and overheated zone were coarse and even formed widmanstaten structure which made the performance of the zone weaken. Leakage from the joint of tube of header and coil tube of coal economizer resulted in the micro cracks in the weakened region of fusion and overheated zone under the thermal stress. Though throughwall crack was not formed after micro cracks initiation, micro cracks resulted in crevice corrosion and the crevice corrosion accelerated crack propagation from the inside outwords, and eventually caused the leakage.

Key words: Coal economizer, Tube of header, Welded joint, Leakage, Analysis

引用本文

季 明,敖 峰,胡传顺,田景涛. 省煤器联箱接管座与管排焊接接头泄漏原因分析[J]. 辽宁石油化工大学学报, 2014, 34(2): 57-60.

Ji Ming， Ao Feng， Hu Chuanshun， Tian Jingtao. Analysis of Leakage Reasons for Joint of Tube of Header and  Weld Joints of Coil Tube on Coal Economizer[J]. Journal of Liaoning Petrochemical University, 2014, 34(2): 57-60.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal.lnpu.edu.cn/CN/10.3696/j.issn.1672-6952.2014.02.015

               http://journal.lnpu.edu.cn/CN/Y2014/V34/I2/57



网站版权 © 2021《辽宁石油化工大学学报》编辑部

本系统由北京玛格泰克科技发展有限公司设计开发