Magnetostriction Coefficient of Amorphous Fe78Si9B13 Under Two Distinctive Treatment

 

GUO Hong, CHEN Ming-ming
  

  1. School of Sciences,Liaoning Shihua University, Fushun Liaoning 113001, P.R.China
  • Received:2012-03-19 Published:2012-12-20 Online:2017-07-06

两种处理工艺下Ｆｅ７８Ｓｉ９Ｂ１３非晶薄带的磁致伸缩系数

郭　红，陈明明   

  1. 辽宁石油化工大学理学院，辽宁抚顺１１３００１
  • 作者简介:郭红（１９５７－），女（满），辽宁抚顺市，教授，博士。

PDF

Abstract:  

Amorphous alloy sample Fe78Si9B13 is disposed by low frequency pulsating magnetic field and isothermic annealing, measuring magnetostriction coefficient by self-made magnetostriction coefficient measuring system. Results showed that both treatment process decreased the saturation magnetostriction coefficient λs of sample, λs is related with annealing time t and it reached minimal value 4.952×10-5 when annealing under 300℃ for 40min. Saturation magnetostriction coefficient λs and low-frequency pulsed magnetic field strength Hp is nonlinear relationship, λs has a choice on the disposing parameters of pulsed magnetic field, λs reach minimal value 2.70×10-5 when Hp equals to 19 900 A/m, pulsing frequency equals to 30Hz and processing time t equals to 240s. The impact of saturation magnetostriction coefficient by low frequency pulsed magnetic field is significantly greater than annealing.

Key words: Magnetostriction coefficient ,  Amorphous alloys , Low-frequency pulsed magnetic field ,  Isothermic annealing.

摘要：         采用低频脉冲磁场和等温退火工艺分别对非晶合金Ｆｅ７８Ｓｉ９Ｂ１３样品进行处理，用自制磁致伸缩测量系统对处理前后样品的磁致伸缩系数进行测量。实验结果表明，两种处理工艺都使样品的饱和磁致伸缩系数λｓ 减小，饱和磁致伸缩系数与退火时间ｔ有关，在３００℃温度下等温退火４０ｍｉｎ，样品的饱和磁致伸缩系数最小，其值为４９．５２×１０－５。饱和磁致伸缩系数λｓ 与低频脉冲磁场强度Ｈｐ 为非线性关系，饱和磁致伸系数λｓ 对脉冲磁场处理参数有所选择，当Ｈｐ 为１９　９００Ａ／ｍ、脉冲频率ｆ 为３０Ｈｚ、ｔ为２４０ｓ时，饱和磁致伸缩系数最小，其值为２．７０×１０－５。低频脉冲磁场处理对样品的饱和磁致伸缩系数的影响明显大于等温退火。

关键词: 磁致伸缩系数, 　非晶合金, 　低频脉冲磁场, 　等温退火

Cite this article

GUO Hong, CHEN Ming-ming.  

Magnetostriction Coefficient of Amorphous Fe78Si9B13 Under Two Distinctive Treatment
[J]. Journal of Liaoning Petrochemical University, 2012, 32(4): 92-94.

郭　红，陈明明. 两种处理工艺下Ｆｅ７８Ｓｉ９Ｂ１３非晶薄带的磁致伸缩系数[J]. 辽宁石油化工大学学报, 2012, 32(4): 92-94.

share this article

0
    /   /   Recommend

Add to citation manager EndNote|Ris|BibTeX

URL: https://journal.lnpu.edu.cn/EN/10.3696/j.issn.1672-6952.2012.04.024

         https://journal.lnpu.edu.cn/EN/Y2012/V32/I4/92

Website Copyright © Editorial Department of Journal of Liaoning Petrochemical University

Address: No. 1, west section of Dandong Road, Wanghua District, Fushun City, Liaoning Province Tel:024-56865105 E-mail:lnxuebao@126.com Zip Code:113001

The system is designed and developed by Beijing magtec Technology Development Co., Ltd.