Abstract: As the cement slurry hydration speed is slow, the curing time is long and the increase of cement early compressive strength is slow in the low temperature cementing of conductor and surface casing, it is easy to result in oil, gas and water invasion which impairs cementing quality and operation safety. In view of the fact that the accelerator is lack in cementing of low temperature shallow formation currently at home, some accelerators have poor effectiveness and significant negative impact on slurry rheology etc, a new compound accelerator WSA1 was selected by laboratory study. The performance of slurry that mixed WSA1 was systematically evaluated. The result shows that the accelerator WSA1 can enhance the hydration of oil well cement, shorten the thickening time of cement slurry and significantly improve the early compressive strength of cementstones, which all accord with the requirement of the accelerator evaluation criterion. When WSA1 addition amount is 3%, the thickening time of cement slurry can be shortened more than 50%, the 6 h strength of cementstones enhanced from 3.2 MPa to 11.3 MPa and the 24 h strength of cementstones enhanced from 24.3 MPa to 46.1 MPa. Accelerator WSA1 is a kind of highperformance compound accelerator, which can be used in low temperature shallow formation and has no effect on the initial consistency and rheological parameter of cement slurry. 

Key words: Low temperature , Accelerator , Oil well cement

摘要： 在导管或表层段低温固井中,水泥水化速度慢,候凝时间长,油井水泥石早期强度发展缓慢,影响固
井质量和作业安全。针对目前国内油田低温浅层固井可供选择的油井水泥促凝剂种类少、某些油井水泥促凝剂促
凝和早强效果不佳以及对水泥浆流变性影响较大等问题,通过室内实验研制了一种新型复合促凝剂WSA灢1。对加
有促凝剂WSA灢1的水泥浆进行了系统的性能评价。结果表明:促凝剂WSA灢1能加速油井水泥的水化过程,缩短水
泥浆的稠化时间,显著提高水泥石的早期强度,当m(WSA灢1)暶m(水泥干灰)= 3%时,水泥浆稠化时间可缩短
50%以上,水泥石6h强度从3.2MPa增强到11.3MPa,24h抗压强度从24.3MPa增强到46.1MPa,完全满足其
评价标准的相关要求,且对水泥浆的初始稠度和流变参数基本无影响,是一种性能优异的、可用于低温浅层油气井
固井水泥浆体系的复合促凝剂。

关键词: 低温 , 促凝剂 , 油井水泥