Photoluminescence of Gd2O2S:Dy3+ Phosphors Synthesized by Homogeneous Precipitation Method

LIAN Jing-bao1, LI Jing1WANG Bing-xin1, SUN Xu-dong2   

  1. 1.School of Mechanical Engineering, Liaoning Shihua University, Fushun Liaoning 113001, P.R.China; 2.Key Lab for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang Liaoning 110004, P.R.China
  • Received:2011-09-21 Published:2012-03-25 Online:2017-07-05

摘要:    采用Gd2O3, Dy2O3, H2SO4 和尿素为实验原料,通过均相沉淀法合成了Gd2O2S:Dy3+ 荧光粉。利用X射线衍射(XRD)、场发射扫描电子显微镜(FE-SEM)和光致发光(PL)光谱对合成的粉体进行了表征。XRD分析表明:前驱体在氢气气氛下900℃煅烧2h能转化成单相的GdS粉体。FE-SEM 观察显示:Gd2O2S粉体形貌为近球形,平均粒度大小为300~500nm。PL光谱分析表明:在270nm紫外光激发下,Gd2O2S:Dy3+ 荧光粉的主次发射峰分别位于579和488nm,分别归属于Dy3+4 F9/26H13/2 4F9/26H15/2  跃迁,这两个跃迁均具有e单指数衰减行为。Dy3+ 的猝灭摩尔分数是1%,(Gd0.99,Dy0.01)2O2S荧光粉的色坐标和色温分别为(0.308,0.379,0.313)和6 464K。

关键词: GdS ,  荧光粉 ,  均相沉淀法 ,  光致发光

Abstract: Gd2O2S:Dy3+  phosphors were synthesized by a homogeneous precipitation method from Gd2O3, Dy2O3, H2SO4 and Urea starting materials. The characterizations of Gd2O2S:Dy3+  phosphors were investigated by means of XRD, FE-SEM and PL spectra. XRD analysis shows that the precursor can be transformed into pure Gd2O2S powder by calcining at 900 ℃ for 1 h in hydrogen. FE-SEM observation shows that the Gd2O2S powder particles are quasi-spherical in shape, with a mean particle size of about 300~500 nm. Photoluminescence (PL) spectroscopy reveals that the main and second emission peaks are located at 579 nm and 488 nm under 270 nm UV light excitation, which corresponds to the 4 F9/26H13/2 and the 4F9/26H15/2 transitions of Dy3+ ions, and both transitions of Dy3+ ions have a single exponential decay behavior. The quenching concentration of Dy3+ ions is 1 %. The CIE coordinate and the color temperature of (Gd0.99,Dy0.01)2 O2S phosphor are (0.308, 0.379, 0.313)and 6 464 K respectively.

Key words: Gadolinium oxysulfide , Phosphor , Homogeneous precipitation , Photoluminescence