Preparation of HighPurityand White CeO2 by ComplexPrecipitation  Method and Its Photocatalytic Activit

  

  1. (1.College of Chemistry,Chemical Engineering and Environmental Engineering, Liaoning Shihua University,  Fushun Liaoning 113001,China; 2.Project Managment Department, Daqing Petrochemical Company, Daqing Heilongjiang 163714, China)
  • Received:1900-01-01 Revised:1900-01-01 Published:2013-10-25 Online:2013-10-25

络合沉淀法制备高纯白色二氧化铈及其光催化的研究

李秀萍1,董航2,李楚佳1,赵荣祥1,高肖汉1   

  1. (1.辽宁石油化工大学化学化工与环境学部,辽宁抚顺113001;2.大庆石化公司工程管理部,黑龙江大庆163714)
  • 作者简介:李秀萍(1975),辽宁康平县,讲师,在读博士
  • 基金资助:
    国家自然科学青年基金项目(21003069)

Abstract: The cerium oxide was prepared by complexprecipitation method using ethylene diamine tetraacetic acid disodium salt as precipitator and complexing agent. The methylene blue was photocatalyzed to degrate by CeO2 as catalyst. The experiment researched the influence of the amount of complexing agent, reaction time and temperature on the cerium oxide. It was characterized by XRD, SEM, UV, IR. The results show that the optimal condition of preparing CeO2 is the mole ratio of ceric sulfate and complexing agent is 1∶3, reaction time is 1 h, temperature is 60 ℃. The high purity and crystalline cerium oxide was prepared by complexprecipitation method. The experiment researched photocatalytic activity of CeO2 and discussed the effect of catalyst dosage, hydrogen peroxide, pH, time on degrading methylene blue. The results show that the optimal condition of photocatalysis is catalyst dosage is 20 mg,the amount of hydrogen peroxide is 6 mL, pH was 6, the photocatalytic time is 120 min in the 100 mL solution of methylene blue.

Key words: Cerium oxide,    ,  Photocatalysis,   ,  Complexprecipitation method,   ,  Methylene blue

摘要: 以乙二胺四乙酸二钠盐为络合剂和沉淀剂,采用络合沉淀法制备CeO2 并用于光催化降解亚甲基蓝。实验考察络合剂用量、反应时间和反应温度对产物的影响。采用XRD、SEM、IR、UV 对产物进行表征。结果表明,制备CeO2 最佳条件为硫酸铈与络合剂的物质的量比为1暶3,反应时间1h,反应温度60曟,络合沉淀法制备的氧化铈为白色、纯度较高。同时对CeO2 进行了光催化研究,考察了催化剂用量、双氧水用量、pH、催化时间对光催化实验的影响。结果表明,光催化最佳条件为,100mL亚甲基蓝溶液中催化剂用量20mg,双氧水6mL,pH 为6,光照时间120min。

关键词: 二氧化铈,   , 光催化,   , 络合沉淀法,    , 亚甲基蓝

Cite this article

LI Xiuping,DONG Hang,LI Chujia,et al. Preparation of HighPurityand White CeO2 by ComplexPrecipitation  Method and Its Photocatalytic Activit[J]. Journal of Petrochemical Universities, 2013, 26(5): 15-18.

李秀萍,董航,李楚佳. 络合沉淀法制备高纯白色二氧化铈及其光催化的研究[J]. 石油化工高等学校学报, 2013, 26(5): 15-18.