Preparation of Anionic Conductive Membrane for Fuel Cells Based on Crown Ether Modified Deacetylated Chitin

doi:10.12422/j.issn.1006-396X.2024.02.009

Abstract

Abstract:

Under alkaline conditions,the aldehyde group is introduced into dibenzo?18?crown?6 (DB18C6) with the help of chloroform (CHCl₃) to prepare dimethyl dibenzo?18?crown?6 (DDB18C6).Then,using DDB18C6 and soluble deacetylated chitin (CTS) as raw materials,Schiff reaction was used to synthesize a grafted crown ether CTS membrane with an increasing mass fraction of small molecule crown ethers,which was named C _a ?CTS membrane (a=m(DDB18C6)/m(C _a ?CTS membrane）).The C _a ?CTS membrane is ion exchanged in alkali solution.The C _a ?CTS membrane absorbs K⁺ through the oxygen hole structure,and then the C _a ?CTSK membrane is prepared.Eeach stage the sample membrane was subjected to structural characterization and performance testing.The results show that with the increase of the crown ether grafting degree,the thermal stability of CTS can be improved;when a=0.20,the grafting degree of C_0.20?CTSK membrane can reach 43.91%,the water absorption rate can reach 168.6%,the IEC value is 1.38 mmol/g. At a temperature of 70 ℃,the conductivity of C_0.20?CTSK membrane can reach 46.8 mS/cm; the introduction of grafting of crown ether improves the alkali resistance stability of this series of membranes. After the C _a ?CTSK series membranes are soaked in 6 mol/L KOH solution for 480 hours, the conductivity decreases only 4.0%.

Key words: Chitosan, Dimethyldibenzo?18?crown?6, Anionic conductive film, Fuel cell, Crown ether

摘要：

在碱性条件下，借助三氯甲烷（CHCl₃）将醛基引入二苯并?18?冠?6（DB18C6）中，制得二甲酰基二苯并?18?冠?6（DDB18C6）；以DDB18C6与可溶性脱乙酰甲壳素（CTS）为原料，利用Schiff反应合成了小分子冠醚质量分数递增的接枝冠醚CTS膜，将其命名为C _a ?CTS膜（a=m（DDB18C6）/m（C _a ?CTS膜））；将C _a ?CTS膜于碱液中进行离子交换，C _a ?CTS膜通过氧空穴结构吸附K⁺，进而制得C _a ?CTSK膜；对各阶段的样品膜进行了结构表征和性能测试。结果表明，随着冠醚接枝度的增加，CTS的热稳定性得到改善；当a=0.20时，C_0.20?CTSK膜的接枝度可达43.91%，吸水率可达168.6%，IEC为1.38 mmol/g；在温度为70 ℃的条件下，C_0.20?CTSK膜的电导率可达46.8 mS/cm；冠醚的接枝引入改善了该系列膜的耐碱稳定性；C _a ?CTSK系列膜在6 mol/L的 KOH溶液中浸泡480 h，电导率降低幅度仅为4.0%。

关键词: 脱乙酰甲壳素, 二甲酰基二苯并?18?冠?6, 阴离子导电膜, 燃料电池, 冠醚

CLC Number:

TQ425.23

Haige NIAN, Xuying ZHENG, Hui GAO, Hai XIN, Jilin WANG. Preparation of Anionic Conductive Membrane for Fuel Cells Based on Crown Ether Modified Deacetylated Chitin[J]. Journal of Petrochemical Universities, 2024, 37(2): 66-72.

年海歌, 郑旭莹, 高慧, 辛海, 王吉林. 基于冠醚改性脱乙酰甲壳素制备燃料电池用阴离子导电膜[J]. 石油化工高等学校学报, 2024, 37(2): 66-72.

Figures/Tables 8

References 24

1	陈文燕，陈永立，张海兵. 石油产品非加氢脱氮技术对比分析［J］. 新疆石油天然气， 2010， 6（1）： 74⁃77.
	CHEN W Y， CHEN Y L， ZHANG H B. Comparative analysis for petroleum product non⁃hydrogen denitrification techniques［J］. Xinjiang Oil & Gas， 2010， 6（1）： 74⁃77.
2	吴红军，李志达，谷笛，等. 电化学转化二氧化碳制备碳纳米材料及表征［J］. 东北石油大学学报， 2016， 40（2）： 85⁃89.
	WU H J， LI Z D， GU D， et al. Preparation and characterization of carbon nanomaterials by electrochemical conversion of carbon dioxide［J］. Journal of Northeast Petroleum University， 2016， 40（2）： 85⁃89.
3	谢文富，邵明飞，段雪. 电解水制氢之提效降本［J］. 石油炼制与化工， 2021， 52（10）： 18⁃24.
	XIE W F， SHAO M F， DUAN X. Boosting efficiency and reducing cost of hydrogen production from electrochemical water splittinng［J］. Petroleum Processing and Petrochemicals， 2021， 52（10）： 18⁃24.
4	张庆生，黄雪松. 国内外氢能产业政策与技术经济性分析［J］. 低碳化学与化工， 2023， 48（2）： 133⁃139.
	ZHANG Q S， HUANG X S. Analysis of domestic and foreign hydrogen energy industrial policies and technical economy［J］. Low⁃Carbon Chemistry and Chemical Engineering， 2023， 48（2）： 133⁃139.
5	叶典，应迪文，江璇，等. 转盘式光催化燃料电池处理染料废水［J］. 化工环保， 2018， 38（4）： 373⁃378.
	YE D， YING D W， JIANG X， et al. Treatment of dye wastewater in rotating photocatalytic fuel cell［J］. Environmental Protection of Chemical Industry， 2018， 38（4）： 373⁃378.
6	高洁，唐善法，郭海莹，等. 石油污染土壤处理新技术——植物型微生物燃料电池的适用性［J］. 油田化学， 2023， 40（2）： 350⁃355.
	GAO J， TANG S F， GUO H Y， et al. Applicability of new technology for treatment of oil contaminated soil——plant⁃based microbial fuel cell［J］. Oilfield Chemistry， 2023， 40（2）： 350⁃355.
7	刘盈汐，王吉林，王璐璐，等. 基于植酸框架构筑燃料电池用阴离子导电膜［J］. 石油化工高等学校学报， 2023， 36（1）： 74⁃80.
	LIU Y X， WANG J L， WANG L L， et al. Phytic acid framework⁃based alkaline anion exchange membrane construction for fuel cells［J］. Journal of Petrochemical Universities， 2023， 36（1）： 74⁃80.
8	王倩，杨康宁，翟绍雄，等. 基于磺化金属有机骨架的复合质子交换膜的制备及其性能［J］. 石油化工， 2022， 51（3）： 285⁃290.
	WANG Q， YANG K N， ZHAI S X， et al. Preparation and properties of composite proton exchange membrane based on sulfonated metal organic frameworks［J］. Petrochemical Technology， 2022， 51（3）： 285⁃290.
9	张建民，段红星，李红玑，等. PVA/FA/4A复合质子交换膜的制备及性能研究［J］. 当代化工， 2017， 46（11）： 2197⁃2200.
	ZHANG J M， DUAN H X， LI H J， et al. Preparation and properties of PVA/FA/4A composite proton exchange membrane［J］. Contemporary Chemical Industry， 2017， 46（11）： 2197⁃2200.
10	赵卓，吴爱华，栾胜基，等. 燃料电池用阴离子交换膜的研究进展［J］. 高分子通报， 2015（8）： 52⁃62.
	ZHAO Z， WU A H， LUAN S J， et al. Research and development of anion exchange membrane for fuel cell［J］. Chinese Polymer Bulletin， 2015（8）： 52⁃62.
11	LI Y S. A liquid⁃electrolyte⁃free anion⁃exchange membrane direct formate⁃peroxide fuel cell［J］. International Journal of Hydrogen Energy， 2016， 41（5）： 3600⁃3604.
12	MEEK K M， ELABD Y A. Alkaline chemical stability and ion transport in polymerized Ionic liquids with various backbones and cations［J］. Macromolecules， 2015， 48（19）： 7071⁃7084.
13	王蕊，封瑞江，王吉林，等. q⁃CS/TEOS复合膜的制备及吸附性能的研究［J］. 辽宁石油化工大学学报， 2011， 31（1）： 13⁃16.
	WANG R， FENG R J， WANG J L， et al. Preparation and adsorption performance of q⁃CS/TEOS hybrid membranes［J］. Journal of Liaoning Shihua University， 2011， 31（1）： 13⁃16.
14	MOHAMMADZADEH K R. Application of crown ethers as stationary phase in the chromatographic methods［J］. Journal of Inclusion Phenomena and Macrocyclic Chemistry， 2013， 75（1）： 11⁃22.
15	REN X T， ZHANG J， CHENG M， et al. Supramolecular systems constructed by crown ether⁃based cryptands［J］. Tetrahedron Letters， 2018， 59（23）： 2197⁃2204.
16	KAKHKI R M. Application of crown ethers as stationary phase in the chromatographic methods［J］. Journal of Inclusion Phenomena and Macrocyclic Chemistry， 2013， 75（1⁃2）： 11⁃22.
17	王世伟，高保娇. 二苯并⁃18⁃冠⁃6在交联聚乙烯醇微球表面的固载化［J］. 功能高分子学报， 2009， 22（4）： 343⁃348.
	WANG S W， GAO B J. Immobilizing dibenzo⁃18⁃crown⁃6 on crosslinked polyvinyl alcohol microspheres［J］. Journal of functional polymers， 2009， 22（4）： 343⁃348.
18	ILES A， FORTT R， DE MELLO A J. Thermal optimisation of the Reimer⁃Tiemann reaction using thermochromic liquid crystals on a microfluidic reactor［J］. Lab on a Chip， 2005， 5（5）： 540⁃544.
19	WANG L L， WANG J L， ZHANG Y， et al. Alkaline hybrid composite membrane for direct methanol fuel cells application［J］. Journal of Electroanalytical Chemistry， 2015， 759， Part 2： 174⁃183.
20	WANG J L， HE R H， CHE Q T. Anion exchange membranes based on semi⁃interpenetrating polymer network of quaternized chitosan and polystyrene［J］. Journal of Colloid and Interface Science， 2011， 361（1）： 219⁃225.
21	WANG J H， LI S H， ZHANG S B.Novel hydroxide⁃conducting polyelectrolyte composed of an poly（arylene ether sulfone） containing pendant quaternary guanidinium groups for alkaline fuel cell applications［J］.Macromolecules， 2010， 43（8）：3890⁃3896.
22	LI Q， LIU L， MIAO Q Q， et al. A novel poly （2，6⁃dimethyl⁃1，4⁃phenylene oxide） with trifunctional ammonium moieties for alkaline anion exchange membranes［J］. Chemical Communications （Cambridge， England）， 2014， 50（21）： 2791⁃2793.
23	郭晓静，褚良银，蔡璐，等. 冠醚的离子识别功能及在分离中的应用［J］. 南京工业大学学报（自科版）， 2013， 35（6）： 120⁃126.
	GUO X J， CHU L Y， CAI L， et al. Ionic recognition properties of crown ethers and their applications in separation［J］. Journal of Nanjing University of Technology（Natural Science Edition）， 2013， 35（6）： 120⁃126.
24	POYNTON S D， KIZEWSKI J P， SLADE R C T， et al. Novel electrolyte membranes and non⁃Pt catalysts for low temperature fuel cells［J］. Solid State Ionics， 2010， 181（3⁃4）： 219⁃222.

序号	膜的名称	G/%
1	C_0.05⁃CTS	14.69
2	C_0.10⁃CTS	27.33
3	C_0.15⁃CTS	34.89
4	C_0.20⁃CTS	43.91
5	C_0.25⁃CTS	37.54

序号	膜的名称	G/%
1	C_0.05⁃CTS	14.69
2	C_0.10⁃CTS	27.33
3	C_0.15⁃CTS	34.89
4	C_0.20⁃CTS	43.91
5	C_0.25⁃CTS	37.54

膜	断裂伸长率/%	厚度/μm	拉伸强度/MPa	离子交换量（IEC）/（mmol·g^-1）
C₀⁃CTSK	15.76	195.13±1.2	26.33	0.48
C_0.05⁃CTSK	13.32	202.31±1.3	22.75	0.75
C_0.10⁃CTSK	14.36	219.12±1.4	25.66	0.89
C_0.15⁃CTSK	15.26	238.14±1.5	28.73	1.15
C_0.20⁃CTSK	17.73	285.17±1.3	18.22	1.38
C_0.25⁃CTSK	15.46	304.16±1.4	13.69	1.13
Polystyrene(ethylene utylenes)^[21]	—	—	—	0.68
QPPO⁃1^[22]	—	—	—	0.87
Nafion 112^[23]	—	—	25.1	0.95
Poly(M⁃c⁃B⁃c⁃V)^[24]	—	—	—	1.25

膜	断裂伸长率/%	厚度/μm	拉伸强度/MPa	离子交换量（IEC）/（mmol·g^-1）
C₀⁃CTSK	15.76	195.13±1.2	26.33	0.48
C_0.05⁃CTSK	13.32	202.31±1.3	22.75	0.75
C_0.10⁃CTSK	14.36	219.12±1.4	25.66	0.89
C_0.15⁃CTSK	15.26	238.14±1.5	28.73	1.15
C_0.20⁃CTSK	17.73	285.17±1.3	18.22	1.38
C_0.25⁃CTSK	15.46	304.16±1.4	13.69	1.13
Polystyrene(ethylene utylenes)^[21]	—	—	—	0.68
QPPO⁃1^[22]	—	—	—	0.87
Nafion 112^[23]	—	—	25.1	0.95
Poly(M⁃c⁃B⁃c⁃V)^[24]	—	—	—	1.25

[1]	Yaning XU, Jianing YAN, Lulu WANG, Jilin WANG. Preparation and Characterization of A Functional Polysulfone Anion Exchange Membrane of Polyethylene Glycol Modified Crown Ether [J]. Journal of Petrochemical Universities, 2024, 37(1): 59-65.
[2]	Xueshi Song, Weili Qu, Lei Zhao, Zhenbo Wang. Research Progress of Pt⁃Based Catalysts for Oxygen Reduction in Proton Exchange Membrane Fuel Cells [J]. Journal of Petrochemical Universities, 2023, 36(4): 25-33.
[3]	Xi Chen, Ying Jin, Ji Ma, Leilei Zhang, Zhaoyuan Song. Study on Cobalt Free Iron Base Like Perovskite as Cathode of SOFC [J]. Journal of Petrochemical Universities, 2023, 36(4): 69-74.
[4]	Haiqun Kou, Zhou Zhu, Yuchang Zhou, Xindian Lan, Meiying Yu, Haonan Chen. COD Reduction in Coking Wastewater by Loading Bentonite with Amphiphilic Chitosan [J]. Journal of Petrochemical Universities, 2023, 36(3): 52-59.
[5]	Quansen Yang, Fangfang Wang. Effect of A⁃Site Defect on Sulfur Poisoning Behaivor of Ferrite⁃Based Cathode Materials [J]. Journal of Petrochemical Universities, 2021, 34(6): 1-6.
[6]	Ma Yu， Wang Lulu， Wang Jilin. Research on Swelling Performance of Anion Exchange Membranes Based on Metal Organic Framework [J]. Journal of Petrochemical Universities, 2021, 34(3): 24-30.
[7]	Liu Lu， Chen Li， Li Yanwu， Huang Liangliang. Research Progress of Metal⁃Oxalate Compounds as Proton Conduction Materials [J]. Journal of Petrochemical Universities, 2020, 33(6): 1-7.
[8]	LI Xiaonan,FENG Ruijiang, WANG Jilin,et al. CrossLinking QCS/PS Anion Exchange Membrane Preparation and Characterization [J]. Journal of Petrochemical Universities, 2013, 26(1): 1-5.
[9]	JIANG Zhen-ju,SUN Zhong,WANG Zhou-yu. Research on the Preparation and Performance of Chitosan Membrane [J]. Journal of Petrochemical Universities, 2010, 23(2): 61-63.