ND 钢恒温氧化性能的研究

辽宁石油化工大学学报 ›› 2005, Vol. 25 ›› Issue (3): 48-49.

ND 钢恒温氧化性能的研究

秦　华¹ , 胡传顺^1＊ , 张淑娟¹ , 季　明¹, 韦达刚² , 崔　勇³

1.辽宁石油化工大学机械工程学院, 辽宁抚顺113001;
2.抚顺石油化工设备研究所, 辽宁抚顺113008;3.辽宁抚顺石油三厂, 辽宁抚顺113001

收稿日期:2004-09-03 出版日期:2005-03-25 发布日期:2005-03-25
作者简介:秦华(1978 -), 女, 辽宁抚顺市, 在读硕士。

Oxidation Capability of ND Steel at Isothermal Temperature

1.School of Mechanical Engineering , Liaoning University of Petroleum & Chemical Technology ,Fushun Liaoning 113001 , P .R .China ;
2 .Fushun I nstitute of Petroleum & Chemical Equipment , Fushun Liaoning 113008 , P .R .China ;
3 .No .3 Refinery of Fushun Petroleum Company ,Fushun Liaoning 113001, P .R .China

Received:2004-09-03 Published:2005-03-25 Online:2005-03-25

摘要/Abstract

摘要： 　研究20g 钢和ND 钢在450 ℃下的恒温氧化性能, 得出氧化动力学曲线, 进行氧化动力学曲线公式的拟和, 同时对氧化后的试样表面情况进行宏观观察, 用XRD 分析了氧化物的成分。实验结果表明, 20g 钢和ND 钢表面氧化的程度随着温度升高、保温时间增长, 其氧化速率常数增大, 20g 钢和ND 钢的抗氧化性能不断的降低。ND钢在450 ℃氧化时, 随着氧化时间的增加, 氧化增重加大, 其氧化动力学常数为0.035 。ND 钢与20g 钢相比, 具有较好的抗高温氧化能力, 腐蚀速率低。

关键词: 　20g 钢, 　ND 钢, 　恒温氧化, 　氧化动力学

Abstract:

　 The capability of oxidation of 20g and ND steel at isothermal temperature of 450 ℃ w as studied , and the oxidation kinetic curves were attained.The formula of oxidation kinetic curves was draw n up , at the same time , the oxidization surface of samples was macroscopically observed and the components of oxides w ere analyzed by XRD.The results show as follows :with the increase of the temperature and the time of heat preservation , the constant of oxidation rate increases.The capability of antioxidation of 20g and ND steel decreases continually .While ND steel is oxygenated at 450 ℃, with the increase of oxidation time , oxidation weight increases, and its dynamics constant is 0.035 .Comparing with 20g steel , ND steel has better resist oxidation properties and the velocity of erosion is lower .

Key words: 　20g steel , 　ND steel, 　Isothermal oxidation , 　Dynamics of oxidation