辽宁石油化工大学学报

辽宁石油化工大学学报 ›› 2014, Vol. 34 ›› Issue (6): 16-20.DOI: 10.3696/j.issn.1672-6952.2014.06.004

• 石油化工 • 上一篇    下一篇

渣油型船用燃料油降黏剂的合成工艺及降黏效果的研究

郭志文1,王洪国1,郝春来2,廖克俭1   

  1. ( 1. 辽宁石油化工大学, 辽宁抚顺1 1 3 0 0 1; 2. 辽阳石化分公司研究院, 辽宁辽阳1 1 3 0 0 3)
  • 收稿日期:2014-09-09 出版日期:2014-12-25 发布日期:2017-07-14
  • 通讯作者: 王洪国( 1 9 7 1 - ) , 男, 博士, 副教授, 从事石油化学品研制与化工生产工艺研究; E - m a i l : w h g t o m@1 6 3. c o m。
  • 作者简介:郭志文( 1 9 8 7 - ) , 男, 硕士研究生, 从事石油化学品的研制与开发研究; E - m a i l : 4 6 0 1 7 6 5 4 5@q q. c o m。
  • 基金资助:
    中国石油天然气股份有限公司辽阳石油化工研究院项目( 2 0 1 3 0 1 0 3 0 3) 。

Synthesis and Property Evaluation of Viscosity Depressant for Residual Marine Fuel Oil

Guo Zhiwen1， Wang Hongguo1， Hao Chunlai2， Liao Kejian1   

  1. (1.Liaoning Shihua University，Fushun Liaoning 113001，China； 2.Research Institute of Liaoyang Petrochemical Company，Liaoyang Liaoning 113003，China)
  • Received:2014-09-09 Published:2014-12-25 Online:2017-07-14

PDF

摘要：  以马来酸酐( M) 、 苯乙烯( S) 与自制的丙烯酸十八醇醚酯单体( A) 共聚合成了三元共聚物( MS A) 型油
溶性降黏剂, 考察了降黏剂对RMG 3 8 0船舶燃料油的降黏效果。实验结果表明, MS A的最佳合成条件为: 丙烯酸十
八醇醚酯、 苯乙烯、 马来酸酐物质的量比为5∶1∶3, 反应温度为9 0℃, 引发剂过氧化苯甲酰( B P O) 的质量分数为
0 . 6%, 反应时间为6h。在降黏剂质量浓度为3 0 0m g / L、 剪切速率为20 0 0r /m i n时, RMG船舶燃料油的降黏率达
到6 6. 1 1%以上, 满足了I S O 8 2 1 7—2 0 0 5标准中RMG 3 8 0船舶燃料油的黏度要求, 降黏剂对不同的船舶燃料油均具
有较好的降黏效果, 但随着时间的增加降黏效果逐渐减弱。

关键词: 船舶燃料; , 三元共聚物; , 降黏剂; , 合成; , 降黏效果

Abstract: he RMG380 marine fuel oil was prepared by vacuum residue, coking wax oil and ethylene tar, the oil-soluble viscosity depressant was synthesized by maleic anhydride, styrene and octadecyl acrylate(MSA). The optimized synthesis conditions are as follows: octadecyl acrylate, styrene and maleic anhydride monomer ratio 5∶1∶3, dosage of initiator 0.6%, synthetic temperature 90 ℃, reaction time 6 h. This synthesized viscosity depressant was evaluated under the concentration of 300 mg/L and shear rate of 2 000 r/min at 50 ℃, the ratio of viscosity reduction of marine fuel oil can reach 66.11%, and meet the ISO8217—2005 RMG380 viscosity requirements of marine fuel oil. Meanwhile, this viscosity depressant was suitable for different marine fuel oil, while viscosity reducing effect gradually weakened with the increase of time.

Key words: Marine fuel oil, Terpolymer, Viscosity depressant, Synthesis, Effect of viscosity reduction

引用本文

郭志文,王洪国,郝春来,廖克俭. 渣油型船用燃料油降黏剂的合成工艺及降黏效果的研究[J]. 辽宁石油化工大学学报, 2014, 34(6): 16-20.

Guo Zhiwen， Wang Hongguo， Hao Chunlai， Liao Kejian. Synthesis and Property Evaluation of Viscosity Depressant for Residual Marine Fuel Oil[J]. Journal of Liaoning Petrochemical University, 2014, 34(6): 16-20.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal.lnpu.edu.cn/CN/10.3696/j.issn.1672-6952.2014.06.004

               http://journal.lnpu.edu.cn/CN/Y2014/V34/I6/16



网站版权 © 2021《辽宁石油化工大学学报》编辑部

本系统由北京玛格泰克科技发展有限公司设计开发