Li⁃Storage of Li2ZnTi3O8@C⁃N Anode Materials with High Specific Capacities

doi:10.3969/j.issn.1006-396X.2022.03.001

Abstract

Abstract:

Li₂ZnTi₃O₈ anodes coated with N?doped carbon from dopamine hydrochloride were synthesized via a high?temperature solid?state method.Some Ti⁴⁺ ions were reduced to Ti³⁺ ions during synthesis,which enabled the co?modification of coating and doping.The modification method can enhance the ion diffusion coefficients and reduce the charge?transfer resistance.In the rate performance tests at 0.5,1.0,1.5,2.0,2.5,3.0 A/g,the specific capacities of N?doped carbon?coated Li₂ZnTi₃O₈(Li₂ZnTi₃O₈@C?N?2) are over 240.0，220.0，210.0，200.0，190.0，180.0 mA $?$ h/g,respectively.In addition,the electrochemical performance of this material at a low temperature was also studied.The results show that the Li₂ZnTi₃O₈@C?N?2 sample has much higher discharge specific capacities than those of unmodified Li₂ZnTi₃O₈ anode material at 0 ℃.The initial discharge specific capacity is 262.5 mA $?$ h/g at 0.2 A/g,and the discharge specific capacity of 241.7 mA $?$ h/g is still obtained after 300 cycles.Even at 1.0 A/g,the discharge specific capacity is kept at 147.4 mA $?$ h/g after 300 cycles.

Key words: Lithium?ion batteries, Li₂ZnTi₃O₈, Anode materials, Carbon coating, Self?doping

摘要：

以盐酸多巴胺为N、C源，高温固相法合成N掺杂C包覆Li₂ZnTi₃O₈@C?N负极材料。在合成过程中发现，部分Ti⁴⁺被还原为Ti³⁺，达到了包覆和掺杂共同改性的目的。该方法有利于提高离子扩散系数和降低电荷转移电阻。在电流密度为0.5、1.0、1.5、2.0、2.5、3.0 A/g时，Li₂ZnTi₃O₈@C?N?2的放电比容量分别超过240.0、220.0、210.0、200.0、190.0、180.0 mA $?$ h/g。还研究了N掺杂C包覆Li₂ZnTi₃O₈复合材料的低温电化学性能。结果表明，0 ℃时该样品的放电比容量远高于未改性的Li₂ZnTi₃O₈负极材料；电流密度为0.2 A/g时的首次放电比容量为262.5 mA $?$ h/g，循环300次后放电比容量为241.7 mA $?$ h/g；在电流密度为1.0 A/g、循环300次后放电比容量依然有147.4 mA $?$ h/g。

关键词: 锂离子电池, 钛酸锌锂, 负极材料, 碳包覆, 自掺杂

CLC Number:

TQ152

Ziye Shen, Lijuan Wang. Li⁃Storage of Li₂ZnTi₃O₈@C⁃N Anode Materials with High Specific Capacities[J]. Journal of Petrochemical Universities, 2022, 35(3): 1-9.

沈紫烨, 王利娟. 高比容量Li₂ZnTi₃O₈@C⁃N负极材料储锂性能研究[J]. 石油化工高等学校学报, 2022, 35(3): 1-9.

Figures/Tables 14

Fig.1 XRD patterns of P?LZTO and LZTO@C?N samples

Table 1 Lattice parameters of P?LZTO and LZTO@C?N samples

样品名称	a/nm	V/nm³	空间群
P⁃LZTO	0.837 13	0.586 66	P4₃32
LZTO@C⁃N⁃1	0.836 89	0.586 15	P4₃32
LZTO@C⁃N⁃2	0.836 61	0.585 56	P4₃32
LZTO@C⁃N⁃3	0.836 35	0.585 01	P4₃32

Fig.2 TG curves of the LZTO@C?N samples

Fig.3 XPS spectra of LZTO@C?N samples

Fig.4 SEM and TEM images of P?LZTO and LZTO@C?N samples

Fig.5 Initial discharge?charge curves of P?LZTO and LZTO@C?N samples

Fig.6 Cycling performance of P?LZTO and LZTO@C?N samples

Table 2 Comparison of the specific capacities of carbon?coated LZTO materials

样品	电流密度/(A $⋅$ g^-1)	循环次数	比容量/(mA $⋅$ h $⋅$ g^-1)	来源
LZTO/C	0.5	50	203.2	[7]
LZTO/C⁃2	0.5	100	190.0	[8]
LZTO⁃M	0.5	100	187.2	[9]
LZTO@C⁃N⁃2	1.0	200	172.63	[12]
LZTO/C	1.0	100	165.2	[14]
LZTO@C⁃N⁃700	0.5	200	217.0	[27]
LZTO@C⁃N⁃2	0.5	50	242.89	本实验
LZTO@C⁃N⁃2	0.5	100	256.18	本实验
LZTO@C⁃N⁃2	0.5	200	237.06	本实验
LZTO@C⁃N⁃2	1.0	50	212.07	本实验
LZTO@C⁃N⁃2	1.0	100	209.81	本实验
LZTO@C⁃N⁃2	1.0	200	196.24	本实验

Table 2 Comparison of the specific capacities of carbon?coated LZTO materials

样品	电流密度/(A $⋅$ g^-1)	循环次数	比容量/(mA $⋅$ h $⋅$ g^-1)	来源
LZTO/C	0.5	50	203.2	[7]
LZTO/C⁃2	0.5	100	190.0	[8]
LZTO⁃M	0.5	100	187.2	[9]
LZTO@C⁃N⁃2	1.0	200	172.63	[12]
LZTO/C	1.0	100	165.2	[14]
LZTO@C⁃N⁃700	0.5	200	217.0	[27]
LZTO@C⁃N⁃2	0.5	50	242.89	本实验
LZTO@C⁃N⁃2	0.5	100	256.18	本实验
LZTO@C⁃N⁃2	0.5	200	237.06	本实验
LZTO@C⁃N⁃2	1.0	50	212.07	本实验
LZTO@C⁃N⁃2	1.0	100	209.81	本实验
LZTO@C⁃N⁃2	1.0	200	196.24	本实验

Fig.7 Rate capability of P?LZTO and LZTO@C?N samples

Table 3 Comparison of the rate capability for carbon?coated LZTO materials

样品	电流密度/(A $⋅$ g^-1)	循环次数	比容量/(mA $⋅$ h $⋅$ g^-1)	来源
LZTO/C	2.0	50	145.6	[6]
LZTO/C	0.5	20	229.0	[11]
LZTO/C	1.0	30	197.9	[11]
LZTO/C	2.0	40	169.8	[11]
LZTO/C	1.8	50	121.8	[14]
LZTO/C	1.0	45	206.4	[28]
LZTO/C	2.0	55	178.0	[28]
LZTO@ C⁃N⁃2	0.5	1~20	240	本实验
LZTO@ C⁃N⁃2	1.0	21~40	220	本实验
LZTO@ C⁃N⁃2	2.0	61~80	200	本实验

Table 3 Comparison of the rate capability for carbon?coated LZTO materials

样品	电流密度/(A $⋅$ g^-1)	循环次数	比容量/(mA $⋅$ h $⋅$ g^-1)	来源
LZTO/C	2.0	50	145.6	[6]
LZTO/C	0.5	20	229.0	[11]
LZTO/C	1.0	30	197.9	[11]
LZTO/C	2.0	40	169.8	[11]
LZTO/C	1.8	50	121.8	[14]
LZTO/C	1.0	45	206.4	[28]
LZTO/C	2.0	55	178.0	[28]
LZTO@ C⁃N⁃2	0.5	1~20	240	本实验
LZTO@ C⁃N⁃2	1.0	21~40	220	本实验
LZTO@ C⁃N⁃2	2.0	61~80	200	本实验

Fig.8 CV curves of P?LZTO and LZTO@C?N?2 samples

Fig.9 Electrochemical impedance spectroscopies and relationship between Zre and ω-1/2 for P?LZTO and LZTO@C?N?2 samples

Table 4 Electrochemical impedance parameters for P?LZTO and LZTO@C?N?2 electrodes

样品	R_E/Ω	R_ct/Ω	$D L i +$ /(cm² $⋅$ s^-1)
P⁃LZTO	1.834	82.03	4.50×10^-17
LZTO@C⁃N⁃2	2.223	66.83	1.67×10^-15

Table 4 Electrochemical impedance parameters for P?LZTO and LZTO@C?N?2 electrodes

样品	R_E/Ω	R_ct/Ω	$D L i +$ /(cm² $⋅$ s^-1)
P⁃LZTO	1.834	82.03	4.50×10^-17
LZTO@C⁃N⁃2	2.223	66.83	1.67×10^-15

Fig.10 Performance curves of P?LZTO and LZTO@C?N?2 samples at 0 ℃

References 29

1	Li G F，Li Q，Li F，et al.Development of rechargeable lithium⁃ion cell using the LiMn₂O₄ spinel as cathode material in recent 3 years［J］.Journal of Petrochemical Universities，2011，31（2）：72⁃81.
2	Hong Z S，Wei M D，Ding X K，et al.Li₂ZnTi₃O₈ nanorods：A new anode material for lithium⁃ion battery［J］.Electrochemistry Communications，2010，12（6）：720⁃723.
3	Wang L J，Meng Z H，Wang H W，et al.Effects of TiO₂ starting materials on the synthesis of Li₂ZnTi₃O₈ for lithium ion battery anode［J］.Ceramics International，2016，42：16872⁃16881.
4	Chen C，Ai C C，Liu X Y，et al.Advanced electrochemical properties of Ce⁃modified Li₂ZnTi₃O₈ anode material for lithium⁃ion batteries［J］.Electrochimica Acta，2017，227：285⁃293.
5	Yang H，Lun N，Qi Y X，et al.Li₂ZnTi₃O₈ coated with uniform lithium magnesium silicate layer revealing enhanced rate capability as anode material for Li⁃ion battery［J］.Electrochimica Acta，2019，315：24⁃32.
6	Xu Y X，Hong Z S，Xia L C，et al.One step sol⁃gel synthesis of Li₂ZnTi₃O₈/C nanocomposite with enhanced lithium⁃ion storage properties［J］.Electrochimica Acta，2013，88：74⁃78.
7	Tang H Q，Tang Z Y.Effect of different carbon sources on electrochemical properties of Li₂ZnTi₃O₈/C anode material in lithium⁃ion batteries［J］.Journal of Alloys and Compounds，2014，613（7）：267⁃274.
8	Wang L J，Chen B K，Meng Z H，et al.High performance carbon⁃coated lithium zinc titanate as an anode material for lithium⁃ion batteries［J］.Electrochimica Acta，2016，188：135⁃144.
9	Liu T，Tang H Q，Liu J Y，et al.Improved electrochemical performance of Li₂ZnTi₃O₈ using carbon materials as loose and porous agent［J］.Electrochimica Acta，2018，259：28⁃35.
10	刘心仪.锂离子电池负极材料钛酸锌锂的合成、改性及其电化学性能研究［D］.武汉：武汉工程大学，2017.
11	Tang H Q，Chen C，Liu T，et al.Chitosan and chitosan oligosaccharide：Advanced carbon sources are used for preparation of N⁃doped carbon⁃coated Li₂ZnTi₃O₈ anode material［J］.Journal of Electroanalytical Chemistry，2020，858：113789.
12	Meng Z H，Wang S，Wang L J，et al.Synthesis of high performance N⁃doped carbon coated Li₂ZnTi₃O₈ via a NTA⁃assisted solid⁃state route［J］.Dalton Transactions，2018，47：2711⁃2718.
13	Li X，Xiao Q，Liu B，et al.One⁃step solution⁃combustion synthesis of complex spinel titanate flake particles with enhanced lithium⁃storage properties［J］.Journal of Power Sources，2015，273：128⁃135.
14	Tang H Q，Zan L X，Mao W F，et al.Improved rate performance of amorphous carbon coated lithium zinc titanate anode material with alginic acid as carbon precursor and particle size controller［J］.Journal of Electroanalytical Chemistry，2015，751：57⁃64.
15	Chen C，Ai C C，Liu X Y.Ti（Ⅲ） self⁃doped Li₂ZnTi₃O₈ as a superior anode material for Li⁃ion batteries［J］.Electrochimica Acta，2018，265：448⁃454.
16	周雄.氧缺位型钛酸锂的制备及其电化学性能研究［D］.昆明：昆明理工大学，2019.
17	李珠叶.Li₂ZnTi₃O₈的结构修饰及电化学性能研究［D］.武汉：湖北工业大学，2020.
18	Zhou X，Pu T，Yang G L，et al.Origin and effect of oxygen defect in Li₄Ti₅O₁₂ prepared with carbon source［J］.Journal of The Electrochemical Society，2019，166（4）：A448⁃A454.
19	Park H，Jae W，Kim J.One⁃pot synthesis of Li₃VO₄ particles with thin nitrogen⁃doped carbon coating layers as an anode material for lithium⁃ion batteries［J］.Journal of Alloys and Compounds，2018，767：657⁃665.
20	Fang R，Xiao W，Miao C，et al.Enhanced lithium storage performance of core⁃shell structural Si@TiO₂/NC composite anode via facile sol⁃gel and in situ N⁃doped carbon coating processes［J］.Electrochimica Acta，2019，317：575⁃582.
21	Liu H C，Shi L D，Li D Z，et al.Rational design of hierarchical ZnO@Carbon nanoflower for high performance lithium ion battery anodes［J］.Journal of Power Sources，2018，387：64⁃71.
22	Ming H，Ming J，Li X W，et al.Hierarchical Li₄Ti₅O₁₂ particles co⁃modified with C & N towards enhanced performance in lithium⁃ion battery applications［J］.Electrochimica Acta，2014，116：224⁃229.
23	Bai X，Li T，Qi Y X，et al.One⁃step fabricating nitrogen⁃doped TiO₂ nanoparticles coated with carbon to achieve excellent high⁃rate lithium storage performance［J］.Electrochimica Acta，2016，187：389⁃396.
24	Yang H，Hu Y，Huang D，et al.Efficient hydrogen and oxygen evolution electrocatalysis by cobalt and phosphorus dual⁃doped vanadium nitride nanowires［J］.Materials Today Chemistry，2019，11：1⁃7.
25	Liu X M，Zang W J，Guan C，et al.Ni⁃doped cobalt–cobalt nitride heterostructure arrays for high⁃power supercapacitors［J］.ACS Energy Letters，2018，3：2462⁃2469.
26	Chen C，Li Z Y，Xu B M.Surface modification of Li₂ZnTi₃O₈ with the C & N layer for lithium⁃ion batteries［J］.Materials Chemistry and Physics，2020，245：122718.
27	Wang X J，Wang L J，Chen B K，et al.MOFs as reactant：In situ synthesis of Li₂ZnTi₃O₈@C⁃N nanocomposites as high performance anodes for lithium⁃ion batteries［J］.Journal of Electroanalytical Chemistry，2016，775：311⁃319.
28	Lan T B，Lin C，Liu Y B，et al.Nanocomposite Li₂ZnTi₃O₈/C with enhanced electrochemical performances for lithium⁃ion batteries［J］.Journal of Electroanalytical Chemistry，2017，794：120⁃125.
29	Zhang Z X，Xun R，Shen Z Y，et al.Synthesis of Nb⁃doped Li₂ZnTi₃O₈ anode with long cycle life and applications in LiMn₂O₄/Li₂ZnTi₃O₈ full cell［J］.ACS Sustainable Chemistry & Engineering，2020，8：2763⁃2771.

Li⁃Storage of Li₂ZnTi₃O₈@C⁃N Anode Materials with High Specific Capacities

高比容量Li₂ZnTi₃O₈@C⁃N负极材料储锂性能研究

HTML

PDF

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 14

References 29

Related Articles 1

Recommended Articles

Metrics