The  H5PMo 1 0V2O4 0 with Keggin structure was prepared by mixing Na2HPO4, NaVO3, and Na2MoO4•2H2O in stoichiometric amount. Then the \[ Bm i m] 5PMo 1 0V2O4 0 hybrid materials was prepared by reacting H5PMo 1 0V2O4 0 with the 1butyl3methyl imidazolium bromide ionic liquid. The IR spectra and XRD data showed that the synthetic \[Bmim\]H5PMo 1 0V2O4 0 hybrid materials display Keggin structure. The SiO2supported \[Bmim\] 5PMo 1 0V2O4 0 hybrid materials were obtained, and the prepared samples were applied to the catalytic degradation of organic dyeRhodamine B. The optimal reaction condition was 30% of \[Bmim\] 5PMo 1 0V2O4 0/SiO2 loading, 1.5 mL of hydrogen peroxide, 0.2 g of the catalyst at 40 ℃. Under the optimal conditions, the highest degradation rate of organic dye Rhodamine B reached up to 97.58%. The catalyst show good regeneration performance, which can be reused at least four times and the degradation rate of Rhodamine B was no significant declined. 