Effect of Chloride Ion on Corrosion Resistance of 2205 Duplex  Stainless Steel in Hydrofluoric Acid

Pang XuguangHou GuanyuLiang Ping   

  1. (School of Mechanical Engineering,Liaoning Shihua University,Fushun Liaoning 113001,China)
  • Received:2017-03-15 Revised:2017-04-20 Published:2018-04-26 Online:2018-04-25

氯离子对2205双相不锈钢抗氢氟酸腐蚀性能的影响

逄旭光,侯冠宇,梁 平   

  1. (辽宁石油化工大学 机械工程学院,辽宁 抚顺 113001)
  • 通讯作者: 梁平(1974-),男,博士,教授,从事材料的腐蚀与防护方面的研究;E-mail:liangping770101@163.com。
  • 作者简介:逄旭光(1991),男,硕士研究生,从事双相不锈钢材料的腐蚀行为研究;Email:280274780@qq.com。
  • 基金资助:
    辽宁省教育厅科学研究一般项目(L2012127)。

Abstract: The corrosion behavior of 2205 duplex stainless steel (DSS) in hydrofluoric acid (HF) was affected by the chlorine ion. The methods including immersion, potentiodynamic polarization and electrochemical impedance spectra (EIS) were used to understand the effect. The results showed that while the NaCl concentration was added into HF solution from 0.015 mol/L to 0.030 mol/L, the corrosion potential got more positive, and the corrosion current density and average corrosion rate increased with the increasing NaCl content. It was because that NaCl decreased the pH of HF solution.

Key words: 2205 duplex stainless steel, The chloride ion, Hydrofluoric acid, pH

摘要: 采用浸泡失重、动电位极化和电化学阻抗等方法,研究了2205双相不锈钢在含有不同浓度氯化钠(NaCl)的氢氟酸(HF)介质中的腐蚀行为。结果表明,当HF溶液中加入浓度为0.015~0.030 mol/L的NaCl时,随着NaCl浓度的逐渐增加,2205双相不锈钢在该溶液中的腐蚀电位逐渐变负,自腐蚀电流密度逐渐增大,平均腐蚀速率逐渐升高。这主要是因为NaCl降低HF溶液的pH所致。

关键词: 2205双相不锈钢, 氯离子, 氢氟酸, pH

Cite this article

Pang Xuguang, Hou Guanyu, Liang Ping. Effect of Chloride Ion on Corrosion Resistance of 2205 Duplex  Stainless Steel in Hydrofluoric Acid[J]. Journal of Liaoning Petrochemical University, 2018, 38(02): 30-32.

逄旭光,侯冠宇,梁 平. 氯离子对2205双相不锈钢抗氢氟酸腐蚀性能的影响[J]. 辽宁石油化工大学学报, 2018, 38(02): 30-32.