氢氧化钠配方溶液去除铝合金表面油污的研究

时 磊1,任玲玲2,王振飚3   

  1.  
    ( 1. 新泰( 辽宁) 航天精铸有限公司, 辽宁营口1 1 5 0 0 0; 2. 东北大学材料与冶金学院, 辽宁沈阳1 1 0 8 1 9;
    3. 武汉理工大学信息工程学院, 湖北武汉4 3 0 0 7 0)
  • 出版日期:2015-02-15 发布日期:2015-02-28
  • 通讯作者: 任玲玲( 1 9 8 6 - ) , 女, 博士研究生, 从事铝合金材料研究; E - m a i l : 3 1 3 1 0 4 4 9 6@q q. c o m。
  • 作者简介:时磊( 1 9 8 7 - ) , 男, 助理工程师, 从事铸造焊接研究; E - m a i l : 7 7 2 6 3 8 4 4 4@q q. c o m。
  • 基金资助:
    国家先进焊接与连接重点实验室开放课题( AW J - M 1 5 - 1 2) 。

Research of Sodium Hydroxide Solution Formula to Remove Oil from Aluminum Alloy Surface

Shi Lei1, Ren Lingling2, Wang Zhenbiao3   

  1. 1．Suntime(Liaoning)Precision Equipment Co., Ltd., Yingkou Liaoning 115000；

    2.Institute of Materials and Metallurgy，Northeastern University，Shenyang Liaoning 110819,China; 3. School of Information Engineering,Wuhan University of Technology，Wuhan Hubei 430070,China

  • Published:2015-02-15 Online:2015-02-28

PDF

摘要： 研究了在氢氧化钠配方溶液去除铝合金表面油污过程中, 氢氧化钠的质量浓度、 反应温度、 浸泡时
间、 搅拌速度与油污去除率的关系。采用正交实验优化去除油污的工艺条件, 得到各因素的影响由主到次的顺序
为: 反应温度、 浸泡时间、 N a OH的质量浓度、 搅拌速度。优化的工艺条件为: 反应温度为6 0℃, 浸泡时间为2 0m i n,
N a OH的质量浓度为9 0g / L, 搅拌速度为4 0 0r /m i n。按优化工艺条件进行验证, 结果表明, 铝合金表面油污的去除
率达到9 9%以上。

关键词: 氢氧化钠\, 铝合金, 除油, 反应温度, 浸泡时间

Abstract:

The relation of oil removal rate from aluminium alloy surface and NaOH concentration, solution temperature, soak time and stirring intensity was studied. With orthogonal test, the process conditions were optimized. In test conditions, the order from big to small of influence factors is:the reaction temperature,soak time,NaOH concentration,stirring intensity. The optimized process conditions are as follows: solution temperature 60 ℃, soak time 20 min, NaOH concentration 90 g/L and stirring intensity 400 r/min. Under the optimized process conditions, the oil removal rate reaches above 99%.

Key words: Sodium hydroxide, Aluminum alloy, Oil removal, The reaction temperature, Soak time

引用本文

时 磊,任玲玲,王振飚. 氢氧化钠配方溶液去除铝合金表面油污的研究[J]. 辽宁石油化工大学学报, 2015, 35(1): 4-7.

Shi Lei, Ren Lingling, Wang Zhenbiao.

Research of Sodium Hydroxide Solution Formula to Remove Oil from Aluminum Alloy Surface [J]. Journal of Liaoning Petrochemical University, 2015, 35(1): 4-7.

使用本文

0
    /   /   推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal.lnpu.edu.cn/CN/10.3696/j.issn.1672-6952.2015.01.002

               http://journal.lnpu.edu.cn/CN/Y2015/V35/I1/4



网站版权 © 2021《辽宁石油化工大学学报》编辑部

本系统由北京玛格泰克科技发展有限公司设计开发