Abstract: Borate esters were prepared as anti-wear lubricants additives from stearic acid, diethanolamine and boric acid and characterized by infrared spectroscopy. Their optimum preparation conditions were determined by examining molecular ratio of reactants, amount of sodium hydroxide[KG*3]and[KG*3]so[KG*3]on.[KG*3]The[KG*3]experimental[KG*3]results[KG*3]show[KG*2]that[KG*2]the[KG*2]yield[KG*2]of[KG*2]borate[KG*2]esters[KG*2]can[KG*2]reach 43.33% under the optimum conditions: mole ratio of stearic acid, diethanolamine to boric acid 1.0∶1.1∶1.0, reaction temperature 105~110 ℃, reaction time 11 h. At the meanwhile, the effect of adding amount of lubricant additives on anti-wear performance of the lubricant base oil agents was also studied and find that when the mass fraction of nitrogen-containing borate ester 0.25% was adding in the liquid paraffin, PB value can reach 697.9 N, minimum wear scar diameter is 0.49 mm, the friction coefficient reduces by 0.017 as compared with that of liquid paraffin oil.

Key words: Extreme-pressure anti-wear performance , Borate ester , Nitrogen-containing