Pt负载Li2Co2O4的合成及其析氧性能研究

关扬1,2闫飞3黄亮亮1林逍2王建强2   

  1. (1.辽宁石油化工大学 化学化工与环境学部,辽宁 抚顺 113001;2.中国科学院 上海应用物理研究所,上海 201800;3.辽宁省产品质量监督检验院,辽宁 沈阳 110032)
  • 收稿日期:2017-03-24 修回日期:2017-04-06 出版日期:2018-10-26 发布日期:2018-11-02
  • 通讯作者: 黄亮亮(1983-),女,博士,副教授,从事功能材料的研究;E-mail:lianglianghuang1@163.com
  • 作者简介:关扬(1992-),女,硕士研究生,从事CO2/H2O高温共电解制备合成气的研究;E-mail:guanyang0430@163.com
  • 基金资助:
    国家自然科学基金青年科学基金项目(21406257)

Synthesis of Pt Loaded Li2Co2O4 and Its Oxygen Evolution Performance

Guan Yang 1,2Yan Fei3Huang Liangliang1Lin Xiao2Wang Jianqiang2   

  1. (1.College of Chemistry, Chemical Engineering and Environmental Engineering, Liaoning Shihua University, Fushun Liaoning 113001, China; 2.Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800, China;3.Liaoning Institute of Products Quality Supervision and Inspection, Shenyang Liaoning 110032, China)
  • Received:2017-03-24 Revised:2017-04-06 Published:2018-10-26 Online:2018-11-02

摘要: 氢气作为清洁燃料在未来的能源版图中将发挥重要作用。电解水制氢反应只生成氢气和氧气,具有成本低、效率高、环境友好、安全性好等优点,而析氧反应是电解水制氢中的一个关键控速反应步骤。介绍了一种简单的Pt负载Li2Co2O4合成方法,并对其析氧性能进行了表征。调控不同的Pt负载量(质量分数),比较对电催化性能的影响,最后得到Pt负载量5%为最优负载量。通过X射线衍射(XRD)、透射电子显微镜(TEM)对材料的结构进行表征,结果表明,得到了一种在保持催化剂的活性与耐久性的同时能够减少Pt消耗的高效催化剂。

关键词: 电解水制氢, Pt负载Li2Co2O4, 高效催化剂

Abstract: Hydrogen as a clean fuel will play a critical role in the future energy landscape. The hydrogen production reaction of electrolytic water only produces hydrogen and oxygen, which has the advantages of low cost, high efficiency, environmental friendliness and good safety. The oxygen evolution reaction is a key ratecontrolled reaction step in hydrogen production from electrolytic water. A simple Pt loaded Li2Co2O4 synthesis method was introduced and its oxygen evolution performance was characterized. The effects of different Pt loading (mass fraction) on the electrocatalytic performance were compared, and the optimum Pt loading was obtained when the Pt loading was 5%. The structure of the material was characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that a highly efficient catalyst capable of reducing the Pt consumption while maintaining the activity and durability of the catalyst is obtained.

Key words: Electrolytic water hydrogen production, Pt loaded Li2Co2O4, Highly efficient catalyst

引用本文

关扬,闫飞,黄亮亮,林逍,王建强. Pt负载Li2Co2O4的合成及其析氧性能研究[J]. 辽宁石油化工大学学报, 2018, 38(05): 30-34.

Guan Yang,Yan Fei,Huang Liangliang,Lin Xiao,Wang Jianqiang. Synthesis of Pt Loaded Li2Co2O4 and Its Oxygen Evolution Performance[J]. Journal of Liaoning Petrochemical University, 2018, 38(05): 30-34.