逆焊接处理对不同材料抗应力腐蚀性能的影响

辽宁石油化工大学学报 ›› 2007, Vol. 27 ›› Issue (3): 32-34.

逆焊接处理对不同材料抗应力腐蚀性能的影响

王岩, 宋天民*, 张国福, 徐东，孙祥广，孟媛媛

辽宁石油化工大学机械工程学院, 辽宁抚顺113001

收稿日期:2006-10-30 出版日期:2007-09-20 发布日期:2017-07-23

Influence and Mechanism of Anti-Welding Procedure on Corrosion Resistance of the Different Materials 

WANG Yan,SONG Tian-min*,ZHANG Guo-fu,XU Dong，SUN Xiang-guang，MENG Yuan-yuan

School of Mechanical Engineering, Liaoning University of Petroleum & Chemical Technology, Fushun Liaoning 113001,P.R.China

Received:2006-10-30 Published:2007-09-20 Online:2017-07-23

摘要/Abstract

摘要： 介绍了采用逆焊接加热处理的方法对Q235、16MnR、20g钢等不同材料在酸性和碱性溶液中抗应力腐蚀性能的影响及机理。将每种材料的试件进行加热处理，再用冷却介质只对焊缝处进行快速冷却，从而获得与焊接温度场相反的负温差，降低焊接过程中产生的残余应力。经过350 ℃处理后的Q235和16MnR钢，在酸性溶液中的腐蚀速率比未处理时分别降低了66.1%和67.9%。实验结果表明，逆焊接加热处理有效的降低了焊接残余应力，并且减缓了应力腐蚀速率,适用于有防止应力腐蚀要求的焊接结构使用。

关键词: 逆焊接加热处理, 压缩残余应力, 应力腐蚀

Abstract: It was introduced that the influence and mechanics of anti-welding procedure on corrosion resistance of the different materials such as Q235 steel,16MnR steel and 20g steel in the acidic and alkali solutions. This method is to carry on the heat treatment for each kind of material sample, and use the cooling medium to cool the welding joint rapidly, in order to obtain the negative temperature departure that is opposite to the welding temperature field，and relieve the residual stresses produced in the welding process. Q235 steel and 16MnR steel which are processed by 350℃ anti-welding procedure, compared with the unprocessed samples, the corrosion rate in the acidic solution reduces 66.1％and 67.9% respectively. The results show that the anti-welding procedure relieves effectively the welding line residual stresses and slows up the stress corrosion rate. This method can be applied to the welding structures which are required to prevent the stress corrosion.

Key words: Anti-welding-procedure, Compressive residual stress, Stress corrosion

王岩, 宋天民, 张国福, 徐东，孙祥广，孟媛媛. 逆焊接处理对不同材料抗应力腐蚀性能的影响[J]. 辽宁石油化工大学学报, 2007, 27(3): 32-34.

WANG Yan,SONG Tian-min,ZHANG Guo-fu,XU Dong，SUN Xiang-guang，MENG Yuan-yuan. Influence and Mechanism of Anti-Welding Procedure on Corrosion Resistance of the Different Materials [J]. Journal of Liaoning Petrochemical University, 2007, 27(3): 32-34.

[1]	李俊池, 谢飞. CO₂增采环境下X70管线钢的应力腐蚀开裂行为研究[J]. 辽宁石油化工大学学报, 2023, 43(1): 38-42.
[2]	赵志伟, 姜文全, 郭俊峰, 安延海, 李志, 张瑶. 石化火炬燃烧器管线裂纹开裂失效分析[J]. 辽宁石油化工大学学报, 2022, 42(5): 80-83.
[3]	付亮,张国福,刘丹. 三催气压机入口过滤器短接开裂失效原因分析[J]. 辽宁石油化工大学学报, 2017, 37(2): 48-53.
[4]	王国庆1,闫萍1,张智超2,朱向哲1. 热焊工艺对2. 2 5 C r 1Mo钢应力腐蚀性能的影响[J]. 辽宁石油化工大学学报, 2015, 35(6): 42-44,48.
[5]	徐东，宋天民，张国福，王岩，孟媛媛. 逆焊接处理对金属材料抗疲劳性能的测试[J]. 辽宁石油化工大学学报, 2007, 27(3): 38-40.
[6]	于　明, 宋天民,等. 重催油浆蒸气发生器管板开裂原因及防治[J]. 辽宁石油化工大学学报, 2005, 25(3): 39-42.
[7]	张玉光. 904L 在甲乙酮生产装置中开裂原因分析[J]. 辽宁石油化工大学学报, 2005, 25(1): 64-66.